- Zeitschriftenartikel (15) (entfernen)
Schlagworte
- Friction (5)
- Wear (5)
- Silicon carbide (4)
- Oscillating sliding (2)
- Relative humidity (2)
- Titanium carbide (2)
- Titanium diboride (2)
- Alumina (1)
- Bearbeitbarkeit (1)
- Ca-Ba fluoride (1)
Ceramic particulate composites in the system SiC-TiC-TiB2 sliding against SiC and Al2O3 under water
(1999)
The tribological behaviour of SiC, SiC-TiC and SiC-TiC-TiB2 was determined in oscillating sliding against SiC and -Al2O3 in water at room temperature. The tribo-systems with the composite materials containing TiC and TiB2 differ significantly from the systems with the single phase SiC: The wear is reduced and the friction is increased. The wear reduction up to a factor of 10 is mainly due to the formation of an oxide film containing titanium oxides which is soft, stable in water and well adhering to the bulk material. This oxide film is transferred to the alumina ball but not to the silicon carbide ball.
The tribological behaviour of different monolithic and composite ceramics was evaluated in the temperature range between room temperature and 750°C. The test method was oscillating sliding with a ball-on-disk arrangement in an SRV machine. Alumina balls were used as counter body. The friction behaviour was determined on-line, and the wear behaviour was determined from calculations on the basis of wear scar dimensions and profilometric measurements. The friction depends on temperature and shows an increase for most materials for increasing temperature; the smallest friction at all temperatures is found for monolithic TiC. The wear behaviour shows different trends for the different materials. In tests against SiC a maximum of wear is found at 500°C, for TiC at 200°C and for TiB2 at 750°C. The composite ceramics suffer the smallest wear of all materials in the range from 200°C to 500°C.
The friction and wear behaviour of SiC, Si3N4 and SiC/Si3N4 composite ceramics were investigated with oscillating sliding (gross slip fretting) at room temperature. The influence of counter body material and the humidity of the surrounding air was studied with a ball-on-disc configuration with different ball materials (1000Cr6, Al2O3 SiC and Si3N4). The effect of RH on friction is marginal with exception of SiC (low friction) as counter body material. The wear behaviour, however, is strongly affected by humidity, showing inverse trends for different counter body materials. Consequently, the wear behaviour of a tribo couple can be improved by selecting an adequate mating material. The results reveal the necessity to control RH in tribological tests. For estimation of the performance of tribo couples under varying environmental conditions, a variation of RH is required. In tribo couples with single phase SiC, either as ball or disc, the tribological behaviour of the system is dominated by SiC. The friction behaviour of the composite material is in between the behaviour of the two single phase materials, Si3N4 and SiC, whereas the wear behaviour is very similar to that of single phase Si3N4.
Tribological characterisation of siliconcarbonitride ceramics derived from preceramic polymers
(2006)
Amorphous SiCN ceramics were prepared in a laboratory scale as disk shaped specimens with 10 mm diameter and 0.3 mm thickness. The friction and wear behaviour was characterised in gross slip fretting tests under unlubricated conditions at room temperature against steel (100Cr6) and ceramic (Al2O3). Tests with a ball-on-disk contact were performed in laboratory air with different content of water vapour. The results show clearly that the relative humidity has a significant effect on friction and wear behaviour. All tests in dry air lead to higher friction and higher wear rate than in normal air. Improved friction and wear behaviour was observed with increasing pyrolysis temperature up to 1100 °C of the SiCN specimens. This is attributed to increasingly better mechanical properties and higher stiffness of the amorphous network due to the evaporation of gaseous organic species and the formation of free graphite like carbon.
The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.
With respect to their excellent material properties ceramics are of interest as candidate materials for tribological applications. The friction and wear behaviour of ceramics is often superior to that of metallic materials. Furthermore, an essential improvement of tribological performance will be possible by tailoring of ceramics in the process of powder preparation and sintering technique. Silicon Carbide (SiC) shows interesting friction and wear behaviour at room temperature, even under unlubricated running conditions but is very sensitive against effects of environmental humidity and shows high friction and high wear in the absence of water vapour. The tribological performance of SiC can be improved considerably by adding substantial amounts of TiC and TiB2 to the microstructure thus creating ceramic particulate composite materials.
Various composites in the quasi ternary system SiC-TiC-TiB2 were prepared by a ceramic manufacturing process including sintering temperatures up to 2180 °C. Comparative tribo tests were performed under unlubricated oscillating sliding motion in dry, normal, and moist air and under water lubrication with SiC balls and Al2O3 balls as counter bodies. The friction is affected by the relative humidity (RH) but barely at all by the composition of the composites. The wear resistance of the composites was found to be improved considerably by addition of TiB2 in the range from 20 to 60 %. The highest wear resistance of the system wear was found when Al2O3 was used as counter body material.
Ceramics are of increasing interest for application in many branches of technique. In order to improve the tribological performance of ceramic materials, composites on the basis of silicon carbide with different amounts of titanium carbide, boron carbide, titanium diboride and free carbon in the form of graphite were manufactured by a reaction sintering process.
The friction and wear behaviour of these composites was investigated with oscillating sliding motion in unlubricated tests at room temperature on different levels of relative humidity. Additional tests were performed under water lubrication, revealing the superior behaviour of composites for special test conditions. A major influence of the free carbon on friction or wear behaviour was not observed. The tribological behaviour in air as well as under water is mainly dependant on the amount of titanium phases.