Tribological behaviour of polyurethane under oscillating sliding conditions against cast iron
(2012)
Zero wear (Null Verschleiß)
(2012)
Recent developments in contact mechanics and microfribology have shown that it is very important to study surface modification effects for quantification of „Zero wear“ (plastic deformation of upper parts of asperities) during sliding friction. The present work considers experimental and Simulation data on the Formation of elastic and plastic contact areas during sliding friction on rough surfaces. The Simulation of discrete contact was carried out using as a source the AFMimages of real surface topography at micro/nanoscale.
The approach for quantification of „zero wear“, proposed here, is not using common Statistical Parameters of roughness, but it considers contact areas on asperities.
In these areas some regions are undergoing plastic deformation which influences surface Transformation during sliding friction. Also, the workhardening effect was taken into account in the Simulation
of sliding friction. This enabled a rnore successful fit of experimental data. The results obtained of the Computer simulations will provide a way of studying friction force at the initial stage of the running-in process.
The tribological behaviour of unfilled thermoplastic polyurethane (TPU) and a polymer sphere filled (TPUG) thermoplastic polyurethane have been studied under oscillating sliding condition against cast iron as a counterpart. In the case of unfilled TPU, the wear mechanisms are dominated by particle detachment and roll formation. In principle, TPUG also showed a similar wear mechanism as that of unfilled TPU; in addition, particle pull-out and delamination are also observed. Wear volume of TPUG was significantly higher than that for the unfilled TPU and this is attributed to the different material removal processes taking place in the material during sliding. The polymer spheres as a filler material deteriorated the wear resistance of TPU because of improper adhesion and bonding of filler in the TPU matrix and therefore it contributed to more wear. In case of TPU the friction behaviour was strongly dependant on the temperature and surface roughness of the counter body. The results showed that below the glass transition temperature higher friction values are observed with higher counter body surface roughness. However, above the glass transition temperature, higher friction values are observed with a smoother surface roughness of the counter body. In case of TPUG, the friction behaviour was not significantly dependent on surface roughness of the counter body.