Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (53)
- Beitrag zu einem Tagungsband (25)
- Vortrag (23)
- Beitrag zu einem Sammelband (14)
- Sonstiges (1)
- Posterpräsentation (1)
Sprache
- Englisch (117) (entfernen)
Schlagworte
- Wear (20)
- Friction (14)
- Temperature (11)
- Fretting (8)
- Ceramics (6)
- Silicon carbide (6)
- Alumina (4)
- Ceramic (4)
- Humidity (4)
- Oscillating sliding (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (23)
Ceramics are of increasing interest for application in many branches of technique. In order to improve the tribological performance of ceramic materials, composites on the basis of silicon carbide with different amounts of titanium carbide, boron carbide, titanium diboride and free carbon in the form of graphite were manufactured by a reaction sintering process.
The friction and wear behaviour of these composites was investigated with oscillating sliding motion in unlubricated tests at room temperature on different levels of relative humidity. Additional tests were performed under water lubrication, revealing the superior behaviour of composites for special test conditions. A major influence of the free carbon on friction or wear behaviour was not observed. The tribological behaviour in air as well as under water is mainly dependant on the amount of titanium phases.
The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the direct semiconductor SiC and the composite compound SiC-TiC-TiB2 was investigated in respect to resulting physicochemical processes. Surface analytical techniques, such as XPS, µ-Raman, and EDX were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material
modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. In the nanosecond case, melting of the surface and redeposited material (debris) were observed. With femtosecond pulses instead, only negligible melting and few debris could be detected. Additionally, periodic structures (ripples) appeared, with parallel orientation and in most cases two different periodicities for a particular material. Laser ablation of all the studied compound materials exhibited preferential ablation of the lighter component elements. Crystal structure changes of the irradiated surface were observed as a consequence of laser-induced melting and resolidification. An oxidation process interfered with all this processes so that unstoichiometric oxides were formed.
The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the semiconductor SiC and the composite compound SiCTiCTiB2 was investigated. Surface analytical techniques, such as XPS, depth profile (DP), and micro-Raman spectroscopy (?-RS) were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. Crystal structure changes were observed as a consequence of laser-induced melting and resolidification. In air contact all components underwent oxidation reactions according to thermodynamic expectations. Exceptions were observed under exclusion of oxygen, SiC was reduced to elemental Si.
COMPOSITE MATERIALS OF A 99.7 % ALPHA-ALUMINA MATRIX WITH PLATELETS OF SILICON CARBIDE (SICP) HAVE BEEN PREPARED BY GELCASTING. DENSIFICATION WAS CARRIED OUT BY GAS-PRESSURE SINTERING WITHOUT FURTHER SINTERING AIDS. FIVE DIFFERENT COMPOSITIONS WITH 0, 5, 10, 15, AND 20 VOL.% SICP RESP. HAVE BEEN INVESTIGATED AND TRIBOLOGICAL PROPERTIES WERE CHARACTERIZED. INCREASING AMOUNT OF SICP AS RIGID PARTICLES IN THE FINE GRAINED MATRIX COMPLICATE THE DENSIFICATION PROCESS. WITH THE APPLICATION OF 50 BAR AR PRESSURE DURING THE FINAL SINTERING STEP AT A TEMPERATURE OF 1700 DEGREE C THE DENSITY OF THE SAMPLES COULD BE INCREASED BY 3-5%. INVESTIGATION OF THE TRIBOLOGICAL PROPERTIES AGAINST STEEL AS A COUNTERBODY UNDER UNLUBRICATED OSCILLATING SLIDING CONDITIONS SHOWED A HIGH COEFFICIENT OF FRICTION AND AN INCREASING WEAR RATE UP TO A SICP CONTENT OF 10 VOL. % . AT 15 AND 20 VOL. % SICP RESP. BOTH THE COEFFICIENT OF FRICTION AND THE COEFFICIENT OF WEAR DROP DOWN.
Influence of Slip Viscosity on the Mechanical Properties of High Purity Alumina made by Gelcasting
(1997)
The isoelectric point is a material property for the characterization of acid-base behavior of the powder surface. The IEP of two alumina powders (AKP-30, Grade A) with different particle size characteristics in aqueous suspension has been determined by colloid vibration current (CVI) and particle charge detection (PCD) methods in moderately concentrated suspensions in order to qualify these methods for a future standardization. The solid loading of the suspensions were 1 and 5 vol%. The comparison of the IEP determined by PCD and CVI was in good agreement. However, the solid loading dependence of IEP and a large IEP hysteresis (at 1 vol%) were observed, which do not allow a proper determination of the IEP. The recording of the potential curve and therfore the determination of the IEP with CVI was difficult for the suspension of Grade A powder due to formation of agglomerates at pH values near the pHIEP.