Schlagworte
- Atomic force microscopy (1)
- Ceramic wear (1)
- Gross slip fretting (1)
- Imaging (1)
- Low IR-emission ceramics (1)
- Roughness (1)
- Wear scar (1)
- Wear volume (1)
- White light interferometry (1)
- Yttrium titanate (1)
The tribological behavior of different low infrared (IR) emission ceramic materials from the titanate group has been investigated at room temperature under gross slip fretting conditions against 100Cr6 ball bearing steel and α-alumina as the counterface materials. For all material pairs, friction and wear depended largely on the relative humidity of the environment. When paired with steel the low IR-emission ceramic disks showed higher wear resistance. Under dry conditions, almost no wear was found on the low IR-emission ceramic specimen. The high wear on the steel counter body is caused not only by tribo-oxidation, which is the main wear mechanism, but also by abrasion. In dry conditions a COF of 0.6 and in humid conditions a COF of 0.2 have been measured. When paired with α-alumina the results on wear are just opposite to those with steel counterbody and the low IR-emission ceramic materials show much lower wear resistance under all conditions. This is explained by the predominance of abrasion and the relatively large difference in hardness between the low IR-emission ceramic and α-alumina. In high humidity environments the results point to the formation of stable reaction layers causing lower friction and wear.
In this article we demonstrate the use of atomic force microscopy (AFM) measurements for the study of macroscopic wear scars. By stitching AFM images acquired over the wear scar, the detailed structure of the scar can be characterized even when the scar is much wider than the typical maximum scan range of the AFM (50–100 µm). The results obtained by AFM are compared with those yielded by white light interferometry (WLI). The comparison validates the WLI measurements; at the same time, it shows decisive differences in the resolutions of these two methods. As a consequence, AFM measurements are necessary whenever a precise characterization of the structure of the scar is required. However, since stitching of AFM images is rather time-consuming, white light interferometry is recommended as a faster method whenever experiments are aimed at just a gross characterization of the scar and the measurement of mean quantities (e.g. the wear volume).