Zero wear (Null Verschleiß)
(2013)
Main focus was on the deposition of carbon nanofibers (CNFs) onto the hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) (nACo®) coating surface and the investigation of the structure and tribological properties of CNFs. The alcohol chemical vapor deposition (ACCVD) method was employed to prepare CNFs and the deposition temperatures were 600 and 700 °C, respectively. Prior to the CNF deposition, Ni catalyst was deposited onto the nACo® surface using the magnetron sputtering. The influence of the deposition temperature on the carbon nanofibers structure was investigated by Raman spectroscopy and scanning electron microscopy (SEM). The higher order degree of CNF structure is observed with increasing deposition temperature. Tribological tests were carried out under fretting contact conditions against Al2O3 ball. It is shown that the coefficient of friction (COF) decreases from 1.0 to 1.2 for the clean nACo® surface to 0.2–0.4 for the CNF layers deposited on the nACo® surface. The roughness of the nACo® surface was varied and a higher durability of the CNF layers deposited on the rougher nACo® surface is found.
In this article we demonstrate the use of atomic force microscopy (AFM) measurements for the study of macroscopic wear scars. By stitching AFM images acquired over the wear scar, the detailed structure of the scar can be characterized even when the scar is much wider than the typical maximum scan range of the AFM (50–100 µm). The results obtained by AFM are compared with those yielded by white light interferometry (WLI). The comparison validates the WLI measurements; at the same time, it shows decisive differences in the resolutions of these two methods. As a consequence, AFM measurements are necessary whenever a precise characterization of the structure of the scar is required. However, since stitching of AFM images is rather time-consuming, white light interferometry is recommended as a faster method whenever experiments are aimed at just a gross characterization of the scar and the measurement of mean quantities (e.g. the wear volume).