The friction and wear behaviour of SiC, Si3N4 and SiC/Si3N4 composite ceramics were investigated with oscillating sliding (gross slip fretting) at room temperature. The influence of counter body material and the humidity of the surrounding air was studied with a ball-on-disc configuration with different ball materials (1000Cr6, Al2O3 SiC and Si3N4). The effect of RH on friction is marginal with exception of SiC (low friction) as counter body material. The wear behaviour, however, is strongly affected by humidity, showing inverse trends for different counter body materials. Consequently, the wear behaviour of a tribo couple can be improved by selecting an adequate mating material. The results reveal the necessity to control RH in tribological tests. For estimation of the performance of tribo couples under varying environmental conditions, a variation of RH is required. In tribo couples with single phase SiC, either as ball or disc, the tribological behaviour of the system is dominated by SiC. The friction behaviour of the composite material is in between the behaviour of the two single phase materials, Si3N4 and SiC, whereas the wear behaviour is very similar to that of single phase Si3N4.
The high temperature tribological performance of tetrahedral amorphous carbon coatings has been analyzed at elevated temperatures up to 250 °C in air against three different counterbody materials-steel 100Cr6, a-alumina and silicon nitride. The results show that the counterbody material influences the friction and wear behavior and therefore coating life time strongly. This effect is well known for these coatings at room temperature under dry environmental conditions, equivalent to conditions above 100 °C when water molecules desorb from the surface. However, the sharp difference in tribological performance between silicon nitride on the one hand and alumina and steel on the other hand cannot be understood in this context. Analyzing the friction behavior during the running-in phase, it is evident that only alumina and steel form a stable interface with constant low friction and relatively low wear rates. Silicon nitride forms an unstable interface with fluctuating COF and relatively high wear rates due to its own inherent tendency to tribo-oxidation.