Ceramics are of increasing interest for application in many branches of technique. In order to improve the tribological performance of ceramic materials, composites on the basis of silicon carbide with different amounts of titanium carbide, boron carbide, titanium diboride and free carbon in the form of graphite were manufactured by a reaction sintering process.
The friction and wear behaviour of these composites was investigated with oscillating sliding motion in unlubricated tests at room temperature on different levels of relative humidity. Additional tests were performed under water lubrication, revealing the superior behaviour of composites for special test conditions. A major influence of the free carbon on friction or wear behaviour was not observed. The tribological behaviour in air as well as under water is mainly dependant on the amount of titanium phases.
The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the semiconductor SiC and the composite compound SiCTiCTiB2 was investigated. Surface analytical techniques, such as XPS, depth profile (DP), and micro-Raman spectroscopy (?-RS) were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. Crystal structure changes were observed as a consequence of laser-induced melting and resolidification. In air contact all components underwent oxidation reactions according to thermodynamic expectations. Exceptions were observed under exclusion of oxygen, SiC was reduced to elemental Si.
Influence of Slip Viscosity on the Mechanical Properties of High Purity Alumina made by Gelcasting
(1997)
The isoelectric point is a material property for the characterization of acid-base behavior of the powder surface. The IEP of two alumina powders (AKP-30, Grade A) with different particle size characteristics in aqueous suspension has been determined by colloid vibration current (CVI) and particle charge detection (PCD) methods in moderately concentrated suspensions in order to qualify these methods for a future standardization. The solid loading of the suspensions were 1 and 5 vol%. The comparison of the IEP determined by PCD and CVI was in good agreement. However, the solid loading dependence of IEP and a large IEP hysteresis (at 1 vol%) were observed, which do not allow a proper determination of the IEP. The recording of the potential curve and therfore the determination of the IEP with CVI was difficult for the suspension of Grade A powder due to formation of agglomerates at pH values near the pHIEP.
Ceramic particulate composites in the system SiC-TiC-TiB2 sliding against SiC and Al2O3 under water
(1999)
The tribological behaviour of SiC, SiC-TiC and SiC-TiC-TiB2 was determined in oscillating sliding against SiC and -Al2O3 in water at room temperature. The tribo-systems with the composite materials containing TiC and TiB2 differ significantly from the systems with the single phase SiC: The wear is reduced and the friction is increased. The wear reduction up to a factor of 10 is mainly due to the formation of an oxide film containing titanium oxides which is soft, stable in water and well adhering to the bulk material. This oxide film is transferred to the alumina ball but not to the silicon carbide ball.
The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.
With respect to their excellent material properties ceramics are of interest as candidate materials for tribological applications. The friction and wear behaviour of ceramics is often superior to that of metallic materials. Furthermore, an essential improvement of tribological performance will be possible by tailoring of ceramics in the process of powder preparation and sintering technique. Silicon Carbide (SiC) shows interesting friction and wear behaviour at room temperature, even under unlubricated running conditions but is very sensitive against effects of environmental humidity and shows high friction and high wear in the absence of water vapour. The tribological performance of SiC can be improved considerably by adding substantial amounts of TiC and TiB2 to the microstructure thus creating ceramic particulate composite materials.
Various composites in the quasi ternary system SiC-TiC-TiB2 were prepared by a ceramic manufacturing process including sintering temperatures up to 2180 °C. Comparative tribo tests were performed under unlubricated oscillating sliding motion in dry, normal, and moist air and under water lubrication with SiC balls and Al2O3 balls as counter bodies. The friction is affected by the relative humidity (RH) but barely at all by the composition of the composites. The wear resistance of the composites was found to be improved considerably by addition of TiB2 in the range from 20 to 60 %. The highest wear resistance of the system wear was found when Al2O3 was used as counter body material.