Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (62)
- Vortrag (48)
- Beitrag zu einem Tagungsband (33)
- Beitrag zu einem Sammelband (20)
- Posterpräsentation (2)
- Forschungsbericht (2)
- Buchkapitel (1)
- Sonstiges (1)
Schlagworte
- Wear (21)
- Friction (16)
- Temperature (12)
- Fretting (9)
- Silicon carbide (7)
- Ceramics (6)
- Reibung (6)
- Alumina (4)
- Ceramic (4)
- Humidity (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (48)
An extended study on tribological properties of carbon nitride coatings under oscillating sliding conditions has been carried out. The coatings were prepared by reactive magnetron sputtering with graphite target using nitrogen as reactive gas in an argon/nitrogen atmosphere during the deposition process to deposit carbon nitride, CNx. Coating thickness was about 2 µm. A 200300 nm thick Ti interlayer was used to enhance adhesion. The nitrogen flow during the deposition was varied to control the amount of nitrogen in the coating. Maximum amount of N-content was about 28 at%, achieved at a maximum N2 flow rate. Other deposition parameters were target to substrate distance, substrate temperature during deposition and bias voltage. The results show a large variation of hardness depending mainly on the nitrogen content and bias voltage. Higher bias voltage produced harder coatings as did lower nitrogen content. The tribological properties were tested unlubricated and lubricated by paraffin oil under gross slip fretting conditions at room temperature against alumina as counter material. Most coatings, but not all, showed a more or less pronounced dependence of wear on relative humidity with wear rates from 10-5 to 10-6 mm3/Nm. The best coatings with regard to a low wear rate and the least dependence upon relative humidity were carbon nitride coatings deposited at elevated substrate temperatures up to 350 °C. The wear resistance of these coatings was increased under the most severe conditions by about one order of magnitude. The results are discussed on the basis of a transfer layer formation. The results show clearly that wear is not significantly correlated to the coating hardness which itself is strongly dependant on the nitrogen content. However, under lubricated conditions with paraffin oil, wear rates were generally very low with wear coefficients at about 10-8 mm3/Nm.
The friction and wear properties of polyetherimide composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C) was investigated. The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. In case of carbon fiber composite abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated.
Performance and efficiency of piezo-electric stick-slip actuators are dependent on the waveform of the electrical actuation of the piezo-stack. This paper compares between a conventional saw-tooth actuation with two waveforms that feature softer acceleration in order to minimize the duration of the slip-phase. It is shown that the proposed waveforms increase both maximum mechanical output power (by 43%) and overall efficiency (by 25%) of the examined actuator.
Tribological properties of neat polyetherimide (PEI), glass, carbon fiber, and solid lubricants filled PEI composites are presented in this article. The aim of this study was to investigate the friction and wear properties of these composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C). The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. Incorporation of carbon fiber in the PEI matrix has increased the wear rate at RT, while at elevated temperature this trend was opposite. Abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated. Tribological performance of neat PEI and glass fiber composite was similar with each other at RT. Scanning electron micrographs and optical micrographs of the worn polymer specimens and the steel cylinders was used to study the possible wear mechanisms. The present test results were also compared with data available on the reciprocating wear of PEI and composites in the literature and trends have been reported.
Untersucht wurden Verschleißpartikel als elektronentransparente Proben auf dünnen Trägerfolien mit einem hochauflösendem Rasterelektronenmikroskop und energiedispersiver Röntgenspektrometrie im Transmissionsmodus.
Die hohe laterale Auflösung dieser modernen Methoden ermöglicht eine morphologische Charakterisierung der Verschleißpartikel bis in den nm-Bereich. Die hochauflösende Elementanalyse erlaubt eine Interpretation der Zusammensetzung und damit Rückschlüsse auf die Verschleißpartikelbildung. Die tribologischen Untersuchungen sind an einem Modell-Verschleißtribometer nach DIN 51834-2 geschmiert, aber ohne Ölkreislauf, durchgeführt worden. Die Präparation der Verschleißpartikel über eine Entnahme und Übertragung einer geringen Schmierstoffmenge mit einer Mikropipette auf eine TEM-Trägerfolie ist mit einem geringen Aufwand möglich. Der präparative Aufwand ist relativ gering. Das benötigte Schmierstoffvolumen beträgt wenige Mikroliter (0,001 ml).
Die Untersuchung zeigt die geringe geometrische Größe der Verschleißpartikel und bestätigt indirekt die These der Reaktionsschichtbildung mit einer geringen Schichtdicke, die ständig verschleißt und sich stetig neu bildet. Die beschriebenen Verschleißprozesse sind in der Modell-Verschleiß-Prüfung mit sehr hohen Pressungen am Versuchsbeginn nachweisbar.
The influence of temperature and counterbody material on the tribological properties of a-C:H coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk contact situation. The results show, that the wear volumes of the system increase exponentially with increasing temperature. Two different wear mechanisms seem to have a major influence: First, the abrasive action due to materials hardness and second, the tribooxidation when silicon nitride is counter material.
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
The accurate EDS microanalysis of light elements such as boron and carbon by spectrum imaging will be demonstrated using a sintered hard ceramic material composed of the three major phases titanium boride (TiB2), titanium carbide (TiC), silicon carbide (SiC) and minor phases, sub-μm in size.
The combination of these three materials leads to improved mechanical and tribological properties. Silicon carbide is a material used for mechanical seals. It has the disadvantage of reduced failsafe running functions, causing increased wear when running dry. The added titanium components (TiC and TiB2) improve the failsafe running functions. This technology has already been transferred to industrial applications.
Pristine, reduced, and alkylated graphene oxides are applied as lubricating additives in paraffin grease. It has revealed that their crystalline structure governs the tribological properties of grease for steel tribo-pair. The microstructural analyses of grease samples showed that a loose fiber network of soap in the presence of graphene-based additive allows their facile release for efficient lubrication. The surface analyses based on the microscopic and elemental mapping show the development of a graphene-derived protective film on the worn scars, which protected the tribo-surfaces and subsided the wear. The reduced graphene oxide (rGO) with the interlamellar distance of 0.35 nm in the (002) plane provided minimum resistance to shear and exhibited maximum reduction in coefficient of friction (COF) for the paraffin grease. The presence of oxygen functionalities in the basal of pristine and alkylated graphene oxide (GO) compromised the interlamellar shearing under tribo-stress; consequently, higher COF than that of rGO.
The sintering behaviour of one microcrystalline and several nanocrystalline TiN powders was investigated by means of a gas pressure furnace with an integrated dilatometer. The investigated nanocrystalline powders strongly differ in the sintering activity. It can be concluded from the experiments, that small grain size, narrow grain size distribution and a low oxygen content are the most important prerequisites for high sintering activity of the nanocrystalline TiN powders.
The extraordinary sintering activity of the best TiN powder makes it possible to produce a dense (< 2 % porosity), pure (no sintering aids) and nanostructured (mean diameter of crystals about 100 nm) TiN bodies.
The tribological behaviour of different monolithic and composite ceramics was evaluated in the temperature range between room temperature and 750°C. The test method was oscillating sliding with a ball-on-disk arrangement in an SRV machine. Alumina balls were used as counter body. The friction behaviour was determined on-line, and the wear behaviour was determined from calculations on the basis of wear scar dimensions and profilometric measurements. The friction depends on temperature and shows an increase for most materials for increasing temperature; the smallest friction at all temperatures is found for monolithic TiC. The wear behaviour shows different trends for the different materials. In tests against SiC a maximum of wear is found at 500°C, for TiC at 200°C and for TiB2 at 750°C. The composite ceramics suffer the smallest wear of all materials in the range from 200°C to 500°C.
Main focus was on the deposition of carbon nanofibers (CNFs) onto the hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) (nACo®) coating surface and the investigation of the structure and tribological properties of CNFs. The alcohol chemical vapor deposition (ACCVD) method was employed to prepare CNFs and the deposition temperatures were 600 and 700 °C, respectively. Prior to the CNF deposition, Ni catalyst was deposited onto the nACo® surface using the magnetron sputtering. The influence of the deposition temperature on the carbon nanofibers structure was investigated by Raman spectroscopy and scanning electron microscopy (SEM). The higher order degree of CNF structure is observed with increasing deposition temperature. Tribological tests were carried out under fretting contact conditions against Al2O3 ball. It is shown that the coefficient of friction (COF) decreases from 1.0 to 1.2 for the clean nACo® surface to 0.2–0.4 for the CNF layers deposited on the nACo® surface. The roughness of the nACo® surface was varied and a higher durability of the CNF layers deposited on the rougher nACo® surface is found.