Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (62)
- Vortrag (48)
- Beitrag zu einem Tagungsband (33)
- Beitrag zu einem Sammelband (20)
- Posterpräsentation (2)
- Forschungsbericht (2)
- Buchkapitel (1)
- Sonstiges (1)
Schlagworte
- Wear (21)
- Friction (16)
- Temperature (12)
- Fretting (9)
- Silicon carbide (7)
- Ceramics (6)
- Reibung (6)
- Alumina (4)
- Ceramic (4)
- Humidity (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (48)
Niobium-titanium carbide cermets with nickel binder have been prepared by colloidal processing in water without a milling step by using Poly-diallyl-dimethyl-ammonium chloride (Poly-DADMAC) as a dispersant. Homogeneous microstructures with relative densities larger than 99% of the theoretical density have been achieved by gas pressure sintering in argon atmosphere. However, mechanical properties like hardness and strength were slightly decreased due to precipitation of free carbon.
Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
The tribological behaviour under dry sliding conditions of Magneli phase Ti4O7 and e-phase Ti2Cr2O7 with α-alumina as a sliding partner has been characterised at room temperature by oscillating sliding. The mechanical properties as well as Vickers hardness measurements do not reveal big differences between the materials, and 4-point bending strengths are around 200 MPa for both materials. Although the friction coefficients are in the medium range of 0.6 and do not differ much between the materials, the wear behaviour is very different. At room temperature, the wear coefficient of Ti2O7 is strongly dependent on relative humidity, and wear is highest under dry conditions when relative humidity is low as it is typically found for many ceramic materials. Ti2Cr2O7 shows remarkably different wear behaviour with the lowest wear in dry conditions. The measured coefficients of wear at low relative humidity of 4% are more than 2 orders of magnitude lower than those for Ti2O7.
Tribological properties of ultrahigh-molecular weight polyethylene (UHMWPE) and cross-linked polyethylene (XLPE) were studied in two different wear modes. Firstly, reciprocating sliding wear studies under non-conformal contact investigated the effects of counterface surface roughness (polished, lapped and ground) of Ti6Al4V on the friction and wear of the polyethylenes. Secondly, two-body abrasive wear studies in conformal contact against different abrasive grit size papers were also carried out to ascertain the wear sensitivity of the polyethylenes under these adverse conditions. Wear mechanisms were studied using optical and scanning electron micrographs. The results of the reciprocating sliding wear studies showed that surface roughness of the counterface influenced friction and wear characteristics although no correlation was found between the coefficient of friction and specific wear rate. XLPE demonstrated wear sensitivity, particularly under severe abrasive wear condition. The results indicated that the performance of the polyethylenes greatly depends upon the tribological system under which it is operating.