Refinement of the weld metal grain structure can improve the mechanical properties of the weld and decrease the susceptibility to solidification cracking of the weld metal. In this study, commercial Al Ti5B1 grain refiner was used to refine the microstructure of LB (laser beam) and GTA (gas tungsten arc) aluminum welds by inoculation. The grain refiner additions led to a significant decrease in the weld metal mean grain size whereby a transition from columnar to equiaxed grain structure (Columnar to Equiaxed Transition, CET) was observed. The development of both grain size and shape depended upon the base metal (Al alloys 1050A, 5083 and 6082) and upon the welding process. The GTA welding process allowed a more pronounced and a more efficient refinement than in LB welds. Furthermore, the influence of the solidification conditions on the CET was investigated through temperature measurements in the weld metal. The temperature profiles revealed a faster solidification of LB welds than in GTA welds. The results from the temperature measurements were also used to estimate (according to an existing model) the critical thermal gradient at which the CET occurs.
The present investigations cover different relevant influences on the numerical calculation of welding-induced distortion. Therefore, a single-layer pulsed gas metal arc (GMA) weld of structural Steel S355J2+N with a thickness Öf5 mm is experimentally and numerically investigated. The influences of mesh density, tack-welds, and continuous cooling transformation (CCT) diagrams on welding-induced distortion are studied. The quality and quantity of These effects are clarified based on the used experimental and numerical set up. The occurring differences between the investigated cases achieve significant values. Consequently, prediction of welding-induced distortion can be improved considering the present investigations.
Experimental investigation of the laser-plume interaction during high power fiber laser welding
(2011)
The effect of the well-known plasma absorption and refraction in CO2-laser metal welding plumes is in case of high power solid state laser welding negligibly small. By contrast, the diffraction effects of shorter wavelength laser radiation are considerable. According
to the results of preliminary studies, the fine condensed metal particles in the welding plume can lead to essential worsening of the laser beam quality.
This work is devoted to the investigation of the lasermatter interaction during up to 20 kW ytterbium fiber laser welding of thick mild steel plates. The plume attenuation of a probe 1.3 µm wavelength diode laser beam as well as of continuous radiation in 250-600 nm
wavelength range was measured during welding with and without Ar shielding gas supply. The measured results allow it to calculate average size and concentration of fine condensed metal particles in
different plume areas using the multi-wavelength method and the Mie scattering theory. The plume temperature, which determines the condensation conditions, was measured by means of Fe I atom
spectral line emission registration.
The obtained results can be also of interest for remote metal treatment with high-power fiber or disc lasers.
A three-dimensional laminar steady
state numerical model was used to investigate
the influence of an alternating current (ac)
magnetic field during high power laser beam
keyhole welding of 20 mm thick nonferromagnetic
aluminum. COMSOL
Multiphysics was used to calculate the threedimensional
heat transfer, fluid dynamics and
electromagnetic field equations. Most
important physical effects of the process were
taken into account: Thermo-capillary
(Marangoni) convection at the upper and lower
weld pool boundaries, natural convection due
to gravity and latent heat of solid-liquid phase
transition. It is shown that the gravity drop-out
associated with welding of thick plates due to
the hydrostatic pressure can be prevented by
the application of an ac magnetic field. The
application of an oscillating magnetic field of
70 mT was investigated to allow for singlepass
laser beam welding of thick aluminum
plates. The flow pattern in the molten zone and
the temperature distributions are significantly
changed.
Die lokalen Festigkeiten im Bereich einer Schweißverbindung sind maßgebend für deren Widerstandsfähigkeit gegenüber mechanischen Beanspruchungen. Im Gegensatz zu anderen präparationsaufwendigen Methoden, z. B. die Untersuchung von Mikro-Zugproben, liefert die instrumentierte Eindringprüfung mit deutlich geringerem Aufwand Verläufe von Festigkeiten mit sehr guter Ortsauflösung. Es werden wahre Spannungs-Dehnungs-Kurven aus zyklischen Eindringversuchen mittels Auswertungen auf der Basis repräsentativer Spannungen und Dehnungen und auf der Basis neuronaler Netze an Punktschweißverbindungen zweier hochfester Stähle, eines TRIP-Stahls und eines martensitischen Stahls, sowie eines weichen niedrig legierten Stahls bestimmt, jeweils im Bereich des Grundwerkstoffs und der Schweißlinse.