Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (39)
- Beitrag zu einem Tagungsband (20)
- Beitrag zu einem Sammelband (16)
- Vortrag (15)
- Posterpräsentation (13)
- Buchkapitel (2)
- Sonstiges (1)
Schlagworte
- Plasma modification (8)
- Plasma polymerization (7)
- Surface functionalization (7)
- Surface modification (5)
- Adhesion (4)
- Aerosol-assisted DBD (4)
- Aluminium (4)
- Fluorescence spectroscopy (4)
- Allyl alcohol (3)
- Functional groups (3)
Eingeladener Vortrag
- nein (15)
The dynamic glass transition (α relaxation, structural relaxation) of ultrathin polysulfone films prepared between aluminum electrodes is investigated by dielectric relaxation spectroscopy. As a main result, it is found that the glass transition temperature Tg does not depend on the thickness of the polymeric layer down to a thickness of 10 nm. For thicknesses lower than 10 nm, an increase of Tg is observed. A more detailed analysis of the temperature dependence of the relaxation rates reveals that the Vogel temperature increases and the fragility decreases systematically with decreasing film thickness d. Further, the dielectric strength Δε decreases with decreasing d. This is discussed by the formation of a surface layer of adsorbed polysulfone segments having a reduced molecular mobility with regard to the time scale characteristic of the glassy dynamics of bulk polysulfone. Plotted versus inverse film thickness Δε decreases linearly with 1/d and becomes zero for an extrapolated length scale of 10 nm. From that it is concluded that the thickness of the adsorbed boundary layer is about 5 nm. Contact-angle measurements were carried out to confirm the strong interaction between aluminum and polysulfone. It is also shown that preparation details like annealing conditions strongly influence the glass transition of supported ultrathin films.
Polypropylene supports were functionalized by plasma-deposition of polymeric allylamine layers. The surface amino groups generated were wet-chemically reacted with xanthene dyes resulting in fluorescent polymer films. The effect of polymer-attachment of the dyes on their emission features was studied fluorometrically and different methods were tested to improve the fluorescence properties of the films. Modification with cucurbit[6]uril (CB6) yields a moderately enhanced fluorescence as well as an improved photostability. The observed effect is most likely due to CB6-induced rigidization of the linker molecules which seems to reduce fluorescence quenching dyedye and fluorophoresurface interactions.
A new concept for molecular interface design in metal-polymer systems is presented. The main features of this concept are the replacement of weak physical interactions by strong covalent bonds, the flexibilization of the interface for compensating different thermal expansions of materials by using long-chain flexible and covalently bonded spacers between the metal and the polymer as well as its design as a moisture-repellent structure for hindering diffusion of water molecules into the interface and hydrolysis of chemical bonds.
For this purpose, the main task was to develop plasmachemical and chemical techniques for equipping polymer surfaces with monotype functional groups of adjustable concentration. The establishing of monotype functional groups allows grafting the functional groups by spacer molecules by applying usual wet-chemical reactions. Four processes were favoured for production of monotype functional groups by highly selective reactions: the plasma bromination, the plasma deposition of plasma polymers, the post-plasma chemical reduction of O-functionalities to OH-groups, and the chemical replacement of bromine groups by NH2-groups. The grafting of flexible organic molecules as spacers between the metal layer and polymer improved the peel strength of the metal. To obtain maximal peel strength of aluminium coatings to polypropylene films and occurrence of cohesive failure in the polypropylene substrate, about 27 OH groups per 100 C-atoms or 6 COOH groups per 100 C-atoms were needed. Introducing C6-11-aliphatic spacers 1 OH or COOH group per 100 C-atoms contributed about 60% of the maximal peel strength of the Al-PP system, i.e. 2 or 3 spacer molecules per 100 C-atoms were sufficient for maximal peel strength.
The production of chemically-defined plasma polymers and the introduction of monotype functional groups onto polymer surfaces are described. One method is to lower the energetic level of low-pressure plasmas. Pressure- and plasma-pulsed plasmas were successfully tested for the production of chemically-defined plasma polymers by increasing the monomer supply during the plasma-off period. Well-defined ultra-thin polymer films with regular structure were deposited from atmospheric plasmas by electrospray techniques. Post-plasma wet-chemical processing was also applied, as were gas/liquid-based aerosols and underwater plasmas.
Plasmapolymerisierte Allylaminschichten (50 nm) wurden auf Polypropylenfolien abgeschieden. Die auf diese Weise generierte NH2-funktionalisierte Polymeroberfläche wurde mit Xanthen-Fluorophoren chemisch umgesetzt. Da die Farbstoff-gekoppelten Folien nur geringe Fluoreszenz aufwiesen, wurden zwei Wege zur möglichen Entkopplung der Farbstoffe von der Oberfläche und damit zur Erhöhung der Fluoreszenzintensität getestet. Als erstes wurde ein Spacer durch die Umsetzung der primären Aminogruppen mit Glutaraldehyd und der nachfolgenden Kettenverlängerung mit Diaminohexan eingeführt. Diese nachfolgende Reaktion ergab eine spacergebundene NH2-Oberfläche, die analog der Allylaminschicht mit den Farbstoffen umgesetzt wurde. Als weiterer Weg wurde der Zusatz einer geeigneten Käfigverbindung, des Cucurbit[6]urils, getestet. Die spacergebundenen und zusätzlich mit Cucurbituril modifizierten aminofunktionellen Oberflächen zeigten nach der Farbstoffankopplung eine verbesserte Fluoreszenzintensität.
A straightforward strategy toward the sensitive fluorometric detection of primary amino groups on plasma-chemically modified polypropylene supports is presented, exploiting the transformation of the sterically nonhindered pyrylium dye Py-1 into its pyridinium counterpart. The reaction-induced blue-shifted absorption and emission bands and an increased fluorescence quantum yield provide the basis for the spectroscopic distinction between covalently bound and free, that is, nonspecifically adsorbed label molecules. With this label, for the first time, plasma-chemically introduced amino functionalities could be monitored on the surface of a polymer film employing fluorescence spectroscopy and confocal laser scanning microscopy.
Polymer surfaces were modified in low-pressure glow discharge plasmas for introduction of monotype functional groups of different type and density. For this purpose three ways are selected, (i) oxygen plasma treatment followed by wet-chemical reduction of O functional groups to OH groups, (ii) plasma bromination for introducing C - Br groups and (iii) coating by deposition of thin plasma (co-) polymerized layers of functional groups-bearing monomers with OH, NH2, COOH, epoxy etc. functionalities. Subsequently, these groups were used as anchoring points for chemical grafting of spacer molecules, oligomers, prepolymers, fluorescent labels, ionic and nucleic acid residues, employing different chemical routes. The yield in monosort functional groups at polymer surfaces ranged from 1014 (process i), 2040 (process ii) and 1831 groups per 100 C atoms (process iii) as measured by XPS after derivatization. The consumption of functional groups amounted to 4090% of all functionalities present at the surface and depended on the dimensions of grafted molecules. For infinitely variably tuning the number of functional groups process iii was performed as copolymerization of a functional group-carrying comonomer with a non-functionalized (chain-extending) comonomer.
Molecular engineering of polymer surfaces that includes the attachment of functional molecules to existing or previously generated reactive chemical groups like e.g., - OH, - NH2, or - CHO requires simple strategies and tools for the controlled generation of surface functionalities and their derivatization as well as for their identification and eventually quantification. Here, we systematically investigate the plasma-chemical surface modification of polypropylene films in combination with dansyl labeling chemistry and conventional, yet costly, XPS and highly sensitive fluorescence spectroscopy for the detection of surface groups. Based on these results, the potential of and requirements on the fluorometric characterization and quantification of surfaces functionalities are discussed.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
Bulk samples and thin films of polyamides (PA6 and PA12) were exposed to fluorine (1 - 10 vol.-% F2 in N2) and analysed with photoelectron (XPS) and infrared spectroscopy. Fluorination affects both, the amide and the hydrocarbon parts of the polymers. However, only the carbon atom next to the carbonyl is readily fluorinated. Chemical modification of the amide group is apparent in a large binding energy shift (+5 eV) of the N1s level and the appearance of a CO band at 1734 cm-1. It is concluded that the amide C-N bond is cleaved in the fluorination process and that COOH and NF2 end groups are formed. This conclusion is corroborated by the appearance of ester oxygen in the XPS and by the 19F NMR spectra of the volatile products that show fluorine signals chemically shifted about 200 ppm towards lower field as compared with the CHF environment.
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
Functional groups bearing monomers were pulsed plasma polymerised with a degree of retained functional groups of 5591%. The following functional groups could be produced at a maximum of: 30 OH, 18 NH2, and 24 COOH per 100 C atoms. A plasma-initiated radical copolymerisation could also be realised using the functional group bearing monomers as a source of functionalities, olefins as chain-extenders and dienes as chemical cross-linkers. The peel strengths of Al layers on such plasma polymers were correlated to the type and density of functional groups.
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
This new functionalization method consists of the deposition of very thin plasma polymer layers (20 to 100 nm) of functional group bearing monomers in pulsed plasma. With allylalcohol, a maximum of 30 OH groups per 100 C atoms was measured with a selectivity of about 90% and a significant stability at long-time exposure to air. Allylamine was used to produce primary amino groups, with a maximum of 18 NH2 groups per 100 C atoms. Side reactions were observed during the storage in air, such as oxidation of the amino groups. Carboxylic groups could be produced using acrylic acid with a maximum concentration of 24 COOH groups per 100 C atoms. The most prominent side reaction was the decarbonylation/ decarboxylation of the acid group during plasma deposition.___TAGSTART___BR___TAGEND___ The variation of the density of functional groups using the pulsed-plasma polymerization of functional-group-bearing monomers was possible by the chemically-initiated radical copolymerization with either a chain-extending monomer, such as ethylene, or a cross linker, such as butadiene, in plasma. The density of functional groups could be adjusted continuously (0 to 30 OH, 0 to 18 NH2 and 0 to 24 COOH groups per 100 C atoms).___TAGSTART___BR___TAGEND___ The successful application of these densely functionalized polymer surfaces for producing biocompatible surfaces and for use in metalpolymer composites is proposed.