Molecular engineering of polymer surfaces that includes the attachment of functional molecules to existing or previously generated reactive chemical groups like e.g., - OH, - NH2, or - CHO requires simple strategies and tools for the controlled generation of surface functionalities and their derivatization as well as for their identification and eventually quantification. Here, we systematically investigate the plasma-chemical surface modification of polypropylene films in combination with dansyl labeling chemistry and conventional, yet costly, XPS and highly sensitive fluorescence spectroscopy for the detection of surface groups. Based on these results, the potential of and requirements on the fluorometric characterization and quantification of surfaces functionalities are discussed.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.
Three polyethylene (PE) types with different branching structures were subjected to air, water and ethanol aerosol-assisted dielectric barrier discharges (DBD) for surface modification. Using the air DBD the incorporated oxygen concentration was found to be independent on the branching of PE in contrast to the introduction of OH groups, which was PE-2 > PE-1 > PE-3. For water-aerosol DBD the succession of OH concentration was in the order of PE-1 > PE-2 > PE-3. Ethanol aerosol-assisted DBD produced the lowest concentration of OH groups also independent on the branching of PE. The chemical nature of introduced oxygen functional groups was inspected by X-ray photoelectron spectroscopy (XPS) and assigned as C–O, >C=O/CHO/O–C–O and O=C–O.
The applicability of polymer-metal composites is mainly determined by the durability of the adhesive strength between both components. Aluminium (Al) deposited on polypropylene (PP) exemplifies different options of interface design. By deposition of plasma polymers on PP the effect of the type of the functionality was investigated. Spacer insertion was accomplished to position the functional group away from the topmost surface. A further kind of interface design involved a partial condensation of functional groups. Hydroxyl and carboxyl groups were most effective to improve adhesion in Al-PP systems. Approximately 7-10 carboxyl or 25-27 hydroxyl groups per 100 C atoms were necessary to increase the peel strength up to ~700 N/m. In this range, the failure of the composite propagated along the interface Al-tape (no peeling of the metal). Spacer molecules between surface and functional groups provoked the effect that the number of needed functional groups for maximum adhesion was strongly reduced. Linking of the functional groups resulted in non-peelable Al-PP laminates. Two adhesion tests were applied - the peel test and the centrifuge technology. For PP foils modified with chemically bonded and additionally linked silanol groups (no peeling) an adhesive strength of (2.5 ± 0.2) N/mm² was determined by centrifuge technology. XPS inspection of both fracture surfaces indicated a sub-surface failure in the polymer.
Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored
by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields information
about the change in structure and dynamics of the system. The fluctuations of the polar groups which
are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic
relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters
like the activation energy and dielectric strength are strongly dependent upon changes induced
by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil
reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission
and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline
regions are not affected. After this induction period, an increase in the degree of crystallization was
observed by employing differential calorimetry. The increasing crystallinity is considered as one of the
reasons for embrittlement which finally leads to the complete loss of the structural integrity.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
Plasmapolymerisierte Allylaminschichten (50 nm) wurden auf Polypropylenfolien abgeschieden. Die auf diese Weise generierte NH2-funktionalisierte Polymeroberfläche wurde mit Xanthen-Fluorophoren chemisch umgesetzt. Da die Farbstoff-gekoppelten Folien nur geringe Fluoreszenz aufwiesen, wurden zwei Wege zur möglichen Entkopplung der Farbstoffe von der Oberfläche und damit zur Erhöhung der Fluoreszenzintensität getestet. Als erstes wurde ein Spacer durch die Umsetzung der primären Aminogruppen mit Glutaraldehyd und der nachfolgenden Kettenverlängerung mit Diaminohexan eingeführt. Diese nachfolgende Reaktion ergab eine spacergebundene NH2-Oberfläche, die analog der Allylaminschicht mit den Farbstoffen umgesetzt wurde. Als weiterer Weg wurde der Zusatz einer geeigneten Käfigverbindung, des Cucurbit[6]urils, getestet. Die spacergebundenen und zusätzlich mit Cucurbituril modifizierten aminofunktionellen Oberflächen zeigten nach der Farbstoffankopplung eine verbesserte Fluoreszenzintensität.
A new concept for molecular interface design in metal-polymer systems is presented. The main features of this concept are the replacement of weak physical interactions by strong covalent bonds, the flexibilization of the interface for compensating different thermal expansions of materials by using long-chain flexible and covalently bonded spacers between the metal and the polymer as well as its design as a moisture-repellent structure for hindering diffusion of water molecules into the interface and hydrolysis of chemical bonds.
For this purpose, the main task was to develop plasmachemical and chemical techniques for equipping polymer surfaces with monotype functional groups of adjustable concentration. The establishing of monotype functional groups allows grafting the functional groups by spacer molecules by applying usual wet-chemical reactions. Four processes were favoured for production of monotype functional groups by highly selective reactions: the plasma bromination, the plasma deposition of plasma polymers, the post-plasma chemical reduction of O-functionalities to OH-groups, and the chemical replacement of bromine groups by NH2-groups. The grafting of flexible organic molecules as spacers between the metal layer and polymer improved the peel strength of the metal. To obtain maximal peel strength of aluminium coatings to polypropylene films and occurrence of cohesive failure in the polypropylene substrate, about 27 OH groups per 100 C-atoms or 6 COOH groups per 100 C-atoms were needed. Introducing C6-11-aliphatic spacers 1 OH or COOH group per 100 C-atoms contributed about 60% of the maximal peel strength of the Al-PP system, i.e. 2 or 3 spacer molecules per 100 C-atoms were sufficient for maximal peel strength.