Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in
single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the
corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By
applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous
tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to
introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which
enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches
were compared for various application examples: ranking of different classes of adhesives, validated statistics of
adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive
strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives,
metallic and dielectric coatings on polymers.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches were compared for various application examples: ranking of different classes of adhesives, validated statistics of adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives, metallic and dielectric coatings on polymers.
Response of linear, branched or crosslinked polyethylene structures on the attack of oxygen plasma
(2014)
Linear, branched and crosslinked polyethylenes (PE) were exposed to the low-pressure oxygen plasma for 2–120 s. In the following the samples were washed with solvents to remove low-molecular weight oxidized material and to excavate the subjacent polymer structure for microscopic characterization. X-ray photoelectron spectroscopy (XPS) measurements provided information about changes in elemental composition and chemical structure of PE after plasma exposure and washing. The calculation of the concentration of tertiary C atoms using XPS data was a measure of branches and crosslinking in the polymer before and after exposure to oxygen plasma. Linear PE was most sensitive towards oxygen plasma and showed the highest concentration in tertiary C atoms after plasma exposure. On the other hand branched PE types, which possess originally more tertiary carbon atoms, have lost two-third of them after 2 s oxygen plasma exposure. Branched PE show also topological changes at their surface as detected by atomic force microscopy. Differential scanning calorimetry measurements confirmed strong changes in crystallinity and molecular orientation of linear PE already after 120 s exposure to the oxygen plasma interpreted as amorphization. These effects should be interpreted as result of crosslinking caused by the recombination of dangling bond sites.
Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates
(2014)
Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition.