Three polyethylene (PE) types with different branching structures were subjected to air, water and ethanol aerosol-assisted dielectric barrier discharges (DBD) for surface modification. Using the air DBD the incorporated oxygen concentration was found to be independent on the branching of PE in contrast to the introduction of OH groups, which was PE-2 > PE-1 > PE-3. For water-aerosol DBD the succession of OH concentration was in the order of PE-1 > PE-2 > PE-3. Ethanol aerosol-assisted DBD produced the lowest concentration of OH groups also independent on the branching of PE. The chemical nature of introduced oxygen functional groups was inspected by X-ray photoelectron spectroscopy (XPS) and assigned as C–O, >C=O/CHO/O–C–O and O=C–O.
A convenient way to overcome the chemical inertness of polyolefin surfaces is to expose them to the atmospheric air plasma of a dielectric barrier discharge (DBD). To improve the efficiency in formation of polar groups at the polyolefin surface, different liquids such as water and ethanol were sprayed as aerosol into the plasma zone between the powered electrode and the polyolefin surface. Both sprayed liquids as well as the polyolefin surface were simultaneously activated; thus, the formation of different functional groups at the polyolefin surface was realized. The type of aerosol-sprayed additive, exposure time, power etc. have been found to determine the efficiency with respect to introduction of polar groups.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Aerosol-based DBD - A simple way to provide polymers with functional groups for adhesion promotion
(2013)
Polypropylene (PP) foils were exposed to the plasma of an atmospheric dielectric barrier discharge (DBD) in presence of different aerosols. Pure liquids such as water, ethanol, and 1/1 mixtures ethanol/water (v/v) or aqueous Solutions of acetic acid, poly(acrylic acid), poly(vinyl alcohol), and ethylene glycolpoly(vinyl alcohol) copolymer were introduced into the DBD. Surface composition, the number of functional groups per 100 C atoms, and water contact angles were correlated with the energy density of DBD plasma exposure.
The wettability of the treated surfaces was investigated for different storage times. Peel strength of the thermally deposited aluminum layer to modified polymer surfaces revealed that the aerosol introduction strongly improves the adhesion between aluminum and polypropylene.
Polypropylene supports were functionalized by plasma-deposition of polymeric allylamine layers. The surface amino groups generated were wet-chemically reacted with xanthene dyes resulting in fluorescent polymer films. The effect of polymer-attachment of the dyes on their emission features was studied fluorometrically and different methods were tested to improve the fluorescence properties of the films. Modification with cucurbit[6]uril (CB6) yields a moderately enhanced fluorescence as well as an improved photostability. The observed effect is most likely due to CB6-induced rigidization of the linker molecules which seems to reduce fluorescence quenching dyedye and fluorophoresurface interactions.