Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (39)
- Beitrag zu einem Tagungsband (20)
- Beitrag zu einem Sammelband (16)
- Vortrag (15)
- Posterpräsentation (13)
- Buchkapitel (2)
- Sonstiges (1)
Schlagworte
- Plasma modification (8)
- Plasma polymerization (7)
- Surface functionalization (7)
- Surface modification (5)
- Adhesion (4)
- Aerosol-assisted DBD (4)
- Aluminium (4)
- Fluorescence spectroscopy (4)
- Allyl alcohol (3)
- Functional groups (3)
Eingeladener Vortrag
- nein (15)
Polyolefins are chemically inert and do not adhere well to metals, polymers or inorganics. To overcome this problem, polyolefin surfaces were modified thermally, plasmachemically, or by flame treatment with different oxygen-containing groups, however, unfortunately, such treatments were accompanied by undesired, adhesion lowering polymer degradation. To solve this dilemma, solutions of synthetic polymers and copolymers were prepared, sprayed into the barrier discharge or electrosprayed without discharge and deposited as thin adhesion-promoting layers. The deposited polymer layers from poly(vinylamine), poly(ethylene glycol)-poly(vinyl alcohol) copolymers and poly(acrylic acid) were endowed with monotype functional groups. Using the aerosol - dielectric barrier discharge only a fraction of functional groups survived the deposition process in contrast to the electrospray in which all functional groups were retained.
Polymer surfaces were modified in low-pressure glow discharge plasmas for introduction of monotype functional groups of different type and density. For this purpose three ways are selected, (i) oxygen plasma treatment followed by wet-chemical reduction of O functional groups to OH groups, (ii) plasma bromination for introducing C - Br groups and (iii) coating by deposition of thin plasma (co-) polymerized layers of functional groups-bearing monomers with OH, NH2, COOH, epoxy etc. functionalities. Subsequently, these groups were used as anchoring points for chemical grafting of spacer molecules, oligomers, prepolymers, fluorescent labels, ionic and nucleic acid residues, employing different chemical routes. The yield in monosort functional groups at polymer surfaces ranged from 1014 (process i), 2040 (process ii) and 1831 groups per 100 C atoms (process iii) as measured by XPS after derivatization. The consumption of functional groups amounted to 4090% of all functionalities present at the surface and depended on the dimensions of grafted molecules. For infinitely variably tuning the number of functional groups process iii was performed as copolymerization of a functional group-carrying comonomer with a non-functionalized (chain-extending) comonomer.
Bulk samples and thin films of polyamides (PA6 and PA12) were exposed to fluorine (1 - 10 vol.-% F2 in N2) and analysed with photoelectron (XPS) and infrared spectroscopy. Fluorination affects both, the amide and the hydrocarbon parts of the polymers. However, only the carbon atom next to the carbonyl is readily fluorinated. Chemical modification of the amide group is apparent in a large binding energy shift (+5 eV) of the N1s level and the appearance of a CO band at 1734 cm-1. It is concluded that the amide C-N bond is cleaved in the fluorination process and that COOH and NF2 end groups are formed. This conclusion is corroborated by the appearance of ester oxygen in the XPS and by the 19F NMR spectra of the volatile products that show fluorine signals chemically shifted about 200 ppm towards lower field as compared with the CHF environment.
Communication: Fire retardant coatings are deposited on polyamide-66 using plasma polymerisation. Chemical composition and thickness of deposits are adjusted varying the plasma treatment based on hexamethydisiloxane mixed with oxygen. The fire retardancy performances are evaluated using a cone calorimeter. The correlation between fire retardancy and thickness as well as chemical composition is discussed.