Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (39)
- Beitrag zu einem Tagungsband (20)
- Beitrag zu einem Sammelband (16)
- Vortrag (15)
- Posterpräsentation (13)
- Buchkapitel (2)
- Sonstiges (1)
Schlagworte
- Plasma modification (8)
- Plasma polymerization (7)
- Surface functionalization (7)
- Surface modification (5)
- Adhesion (4)
- Aerosol-assisted DBD (4)
- Aluminium (4)
- Fluorescence spectroscopy (4)
- Allyl alcohol (3)
- Functional groups (3)
Eingeladener Vortrag
- nein (15)
Polypropylen (PP) ist als Niedrigenergie-Polymer ohne nass- und plasmachemische Vorbehandlung weder haftfest zu beschichten noch verbundfest zu kleben. Typische Haft- bzw. Klebfestigkeiten liegen für die unbehandelte Polymeroberfläche bei maximal 0,5 MPa. Hinzu kommt, dass bei der Bestimmung von Haft- und Klebfestigkeiten der unmodifizierten Oberfläche mit großen Streuungen zu rechnen ist, die bezogen auf die Spannweite durchaus einem Faktor 5 entsprechen können. Generell besteht bei Prüfung der Haftfestigkeit mittels Stirnabzugsversuch und bei der Prüfung der Klebfestigkeit die Notwendigkeit eines statistisch validierten Herangehens. Hierzu sind zeitaufwändige Ein-Proben-Klebungen und -Prüfungen nur eingeschränkt geeignet. Zudem ist, insbesondere für geringe Haft- bzw. Klebfestigkeiten, ein querkraftfreies Prüfen Grundvoraussetzung. Im vorliegenden Beitrag werden verschiedenartige plasmagestützte Oberflächenfunktionalisierungen von PP sowie das Mehr-Proben-Konzept zur Klebung/Prüfung von bis zu acht Proben vorgestellt. Dazu werden ein BAM-Funktionsmuster einer Mehr-Proben-Kleb-Vorrichtung und eine kommerzielle analytische Zentrifuge zum Prüfen verwendet.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches were compared for various application examples: ranking of different classes of adhesives, validated statistics of adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives, metallic and dielectric coatings on polymers.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in
single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the
corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By
applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous
tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to
introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which
enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches
were compared for various application examples: ranking of different classes of adhesives, validated statistics of
adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive
strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives,
metallic and dielectric coatings on polymers.
Standardised conventional adhesion tests are time-consuming single-sample tests. Moreover, except for the pull-off test, all these tests provide only qualitative or semi-quantitative (ranking, respectively measurement of an adhesion-correlated quantity) information on adhesion. Sometimes, adhesion is evaluated even under compressive stress conditions (e.g. cross-cut and scratch test), which itself is a contradiction to adhesive strength as defined in terms of tensile force per area.
For optical coatings it has been shown that the pull-off test in a centrifuge is definitely a promising alternative with respect to the reliable, fast and quantitative determination of adhesive strength in N/mm2. The force-controlled centrifuge test is the only multiple-sample test which provides reliable quantitative information on the adhesive strength in agreement with DIN EN 15870 and DIN EN ISO 4624 on a statistical basis for up to eight samples simultaneously tested under identical testing conditions.
Poly(allyl alcohol) films with a thickness of about 150 nm were deposited by pulse plasma polymerization onto different substrates (inorganic and organic). The structure/property relationships of these samples were studied in dependence on the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time volume sensitive methods (FTIR and dielectric spectroscopy) are combined with surface analytics by employing XPS for that system. FTIR spectroscopy gives qualitatively the same dependence of the concentration of the OH groups on DC like XPS.
The observed differences are discussed considering the different analytical depths of both the methods. The dielectric measurements show that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating. The results obtained by dielectric spectroscopy are discussed in detail with the data from FTIR and XPS measurements.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
Poly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating, where the reaction kinetics depends on DC.