Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (38)
- Beitrag zu einem Tagungsband (18)
- Beitrag zu einem Sammelband (15)
- Posterpräsentation (5)
- Buchkapitel (2)
- Vortrag (2)
- Sonstiges (1)
Sprache
- Englisch (81) (entfernen)
Schlagworte
- Plasma modification (8)
- Plasma polymerization (7)
- Surface functionalization (7)
- Surface modification (5)
- Adhesion (4)
- Aerosol-assisted DBD (4)
- Aluminium (4)
- Fluorescence spectroscopy (4)
- Allyl alcohol (3)
- Functional groups (3)
Eingeladener Vortrag
- nein (2)
Functional groups bearing monomers were pulsed plasma polymerised with a degree of retained functional groups of 5591%. The following functional groups could be produced at a maximum of: 30 OH, 18 NH2, and 24 COOH per 100 C atoms. A plasma-initiated radical copolymerisation could also be realised using the functional group bearing monomers as a source of functionalities, olefins as chain-extenders and dienes as chemical cross-linkers. The peel strengths of Al layers on such plasma polymers were correlated to the type and density of functional groups.
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
This new functionalization method consists of the deposition of very thin plasma polymer layers (20 to 100 nm) of functional group bearing monomers in pulsed plasma. With allylalcohol, a maximum of 30 OH groups per 100 C atoms was measured with a selectivity of about 90% and a significant stability at long-time exposure to air. Allylamine was used to produce primary amino groups, with a maximum of 18 NH2 groups per 100 C atoms. Side reactions were observed during the storage in air, such as oxidation of the amino groups. Carboxylic groups could be produced using acrylic acid with a maximum concentration of 24 COOH groups per 100 C atoms. The most prominent side reaction was the decarbonylation/ decarboxylation of the acid group during plasma deposition.___TAGSTART___BR___TAGEND___ The variation of the density of functional groups using the pulsed-plasma polymerization of functional-group-bearing monomers was possible by the chemically-initiated radical copolymerization with either a chain-extending monomer, such as ethylene, or a cross linker, such as butadiene, in plasma. The density of functional groups could be adjusted continuously (0 to 30 OH, 0 to 18 NH2 and 0 to 24 COOH groups per 100 C atoms).___TAGSTART___BR___TAGEND___ The successful application of these densely functionalized polymer surfaces for producing biocompatible surfaces and for use in metalpolymer composites is proposed.
Polymers synthesized with plasma techniques are very interesting materials for electronic, optic, and bio compatible applications. Thin films of plasma polymers shows a good adhesion to metals, glass, or other polymers. But the supramolecular structure, the durability, and the chemical and mechanical behavior of these polymers is poorly understood. Therefore dielectric investigations are carried out to study the dynamic behavior of the plasma polymers. As polymer system allyl alcohol/alkene is chosen to get polymers with a defined concentration of hydroxyl groups. The dielectric investigations shows several relaxation processes and a dependency of the dielectric parameters from the ratio of allyl alcohol in the polymer is observed. This results indicated that the alkene monomers were assembled continuous into the polymer matrix.