Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
For simulation and acceleration of artificial polymer ageing, polyolefin foils were exposed to low-pressure Ar plasma. Plasma particle bombardment and irradiation induce C–C and C–H bond scissions by σ→σ* excitations on the surface and in near-surface layers. Consequently, radicals are generated. They react by recombination, cross-linking, metastable trapping of the radical site or formation of olefinic double bonds. The long-living and metastable trapped C-radicals as well as double bonds in polyolefins were immediately exposed to bromine vapour without breaking the vacuum after switching-off the plasma. These reactive sites rapidly react with the molecular bromine under formation of C–Br bonds. For 5 min of argon plasma exposure, the elemental concentration of bromine was 13% for polyethylene and 22% Br/C for polypropylene as analysed by X-ray photoelectron spectroscopy. Nevertheless, not all C radical sites have reacted with bromine. Later on, when the polyolefins brought in contact with ambient air, an additional post-plasma reaction of the remaining trapped radicals with oxygen was observed. The oxygen concentrations were lower after bromine gassing, thus repressing partially the post-plasma oxidation in the analysed layer (ca. 6 nm) by radical quenching. Such bromination took place either at the surface or in near-surface layers because the Attenuated Total Reflectance (ATR)-FTIR spectra (sampling depth ca. 2500 nm) did not show significant changes for argon plasma-treated PE foils with and without bromine vapour exposure. Further addition of bromine may also occur on C=C double bonds.