Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (33) (entfernen)
Sprache
- Englisch (33)
Referierte Publikation
- ja (33) (entfernen)
Schlagworte
- Plasma polymerization (5)
- Surface functionalization (4)
- Fluorescence spectroscopy (3)
- Surface modification (3)
- Allyl alcohol (2)
- Aluminium (2)
- Dielectric properties (2)
- Dielectric relaxation (2)
- Peel strength (2)
- Plasma modification (2)
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
Poly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating, where the reaction kinetics depends on DC.
Poly(allyl alcohol) films with a thickness of about 150 nm were deposited by pulse plasma polymerization onto different substrates (inorganic and organic). The structure/property relationships of these samples were studied in dependence on the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time volume sensitive methods (FTIR and dielectric spectroscopy) are combined with surface analytics by employing XPS for that system. FTIR spectroscopy gives qualitatively the same dependence of the concentration of the OH groups on DC like XPS.
The observed differences are discussed considering the different analytical depths of both the methods. The dielectric measurements show that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating. The results obtained by dielectric spectroscopy are discussed in detail with the data from FTIR and XPS measurements.
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
Functional groups bearing monomers were pulsed plasma polymerised with a degree of retained functional groups of 5591%. The following functional groups could be produced at a maximum of: 30 OH, 18 NH2, and 24 COOH per 100 C atoms. A plasma-initiated radical copolymerisation could also be realised using the functional group bearing monomers as a source of functionalities, olefins as chain-extenders and dienes as chemical cross-linkers. The peel strengths of Al layers on such plasma polymers were correlated to the type and density of functional groups.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
The production of chemically-defined plasma polymers and the introduction of monotype functional groups onto polymer surfaces are described. One method is to lower the energetic level of low-pressure plasmas. Pressure- and plasma-pulsed plasmas were successfully tested for the production of chemically-defined plasma polymers by increasing the monomer supply during the plasma-off period. Well-defined ultra-thin polymer films with regular structure were deposited from atmospheric plasmas by electrospray techniques. Post-plasma wet-chemical processing was also applied, as were gas/liquid-based aerosols and underwater plasmas.