Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (12)
- Posterpräsentation (8)
- Beitrag zu einem Tagungsband (5)
- Vortrag (4)
- Buchkapitel (1)
- Beitrag zu einem Sammelband (1)
Schlagworte
- Corrosion (4)
- Alumina (3)
- Coating (3)
- Sol-gel (3)
- TEM (3)
- Al2O3 (2)
- Alumosol (2)
- Beschichtung (2)
- Corundum (2)
- Geothermal (2)
- High-temperature corrosion (2)
- Martensitic steel (2)
- Oxidationsschutz (2)
- Sol-Gel-Verfahren (2)
- Sol-gel coating (2)
- Abwasser (1)
- Advanced oxidation (1)
- AlPO4 (1)
- Alpha-cordierite (1)
- Alumina coating (1)
- Alumina coatings (1)
- Aluminium oxide (1)
- Aufbaugranulation (1)
- Back-filling specimen mount technique (1)
- Behmite (1)
- Boehmite (1)
- Cement (1)
- Ceramics (1)
- Chromium (1)
- Coatings (1)
- Concrete (1)
- Corrosion protection (1)
- Flow Coefficient (1)
- Heterogeneous photocatalysis (1)
- High temperature corrosion (1)
- High-temperature oxidation (1)
- Hochtemperaturanwendungen (1)
- Hybrid coatings (1)
- Hydrophobization (1)
- IR-spectroscopy (1)
- Inconel 625 (1)
- Indialite (1)
- Limestone Filler (1)
- Martensitic steels (1)
- Methylene blue (1)
- Nanozirconia (1)
- Oxidation protection (1)
- Oxide coatings (1)
- Oxyfuel (1)
- Particle Size Distribution (1)
- Photokatalyse (1)
- Powder processing (1)
- Protection (1)
- Protective coating (1)
- Redispersion (1)
- Reference Material (1)
- Rheology (1)
- SEM (1)
- Schichtherstellung (1)
- Schichttestung (1)
- Standard material (1)
- Steel (1)
- Steel P92 (1)
- Steel protection (1)
- Tape casting (1)
- Transmission electron microscopy (1)
- Volume Fraction (1)
- Water treatment (1)
- Wetting (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.