Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.
The suitability of an Al2O3 coating for corrosion protection on X20Cr13 was evaluated in various artificial geothermal brines, focusing on the influence of different pH (4, 6 and 8) and their chemical compositions on the coating properties. All experiments were performed in the laboratory using autoclaves at 150 ◦C and 1 MPa in deaerated condition for 1 and 7 days. Results showed that the pH of geothermal waters is the most detrimental factor in the transformation of ɣ-Al2O3 and its protective abilities. Delaminations were found in the Coating exposed to geothermal brines with pH 4. FTIR spectra indicated a transformation of ɣ-Al2O3 to boehmite AlOOH after exposure to pH 4 and 6, and bayerite Al(OH)3 was formed after exposure to pH 8. Different Crystal structures of the hydrated Al2O3 also contribute to the stability of the coatings, observed by the SEM- EDX of the surface and cross-section of coatings. This study indicated that ɣ-Al2O3 sol-gel coating presents a promising aspect of corrosion protection in geothermal environment with a neutral pH.
Improved wetting of bare and pre-coated steels by aqueous alumina sols for optimum coating success
(2010)
Alumina coatings are a promising candidate for
the protection of metals prone to high temperature corrosion.
If applied via sol–gel process, especially by using so
called aqueous modified Yoldas-sols, the deposition is
hardened by differences in surface free energy of substrate
and sol. In this paper the apparent surface properties of
samples to be coated and sols were examined by contact
angle measurements, IR-spectroscopy and tensiometry.
The results imply, after consideration of possible uncertainties,
the use of surface tension reducing 2-butanol
already present during hydrolysis of the sols to obtain an
easy and successful coating process.
Sol-Gel-Aluminiumoxidschichten für den Oxidationsschutz von Hochtemperaturlegierungen, Teil 2
(2009)
Sol-Gel-Aluminiumoxidschichten für den Oxidationsschutz von Hochtemperaturlegierungen, Teil 1
(2009)
Microstructure, smoothening effect, and local defects of alumina sol-gel coatings on ground steel
(2017)
Porous alumina films with thicknesses of a few microns were prepared via a dip-coating technique on steel P92. The coating is shown to protect the steel against massive corrosion, which is typical in the hot reactive environment of coal fired power plants. To mimic real conditions ground steel plates were coated with a boehmite-sol. This leads to an overall smoothing of the formerly rough surface. In the following short annealing step the inner porous construction with worm-like particles consisting of nano-crystallites and amorphous alumina is formed. Due to the simultaneous diffusion of chromium and iron ions out of the bulk steel material into the porous alumina coating, a dense interface with satisfactory adhesion is formed. However, the film exhibits few local defects like cracks or dense alumina nodules caused by steep edges in the ground surface or agglomeration of boehmite-sol components, respectively. Cracks especially have to be avoided. This problem can be overcome so far by slight modifications in the sol preparation process and surface treatment of the substrates. Nevertheless the results demonstrate the potential of sol-gel based alumina coatings as a time- and cost-saving protection type for commercial steel P92.
Nano-TiO2 powder is known to show high photocatalytic reactivity in the degradation of several organic pollutants.
In thiswork, the powderwas fixed on the surface of SiO2 granuleswith the size of several micrometers using a high shear granulation process. Nanozirconia sol was applied as an inorganic binder. When the samples were tempered at 300 °C, they showed high stability in an aqueous solution for several hours. An energy dispersive x-ray spectroscopy (EDX) analysis confirmed that the cores and shells of the granules consisted solely of SiO2 and TiO2 respectively, and that ZrO2 was found throughout the whole granules. Methylene blue (MB) was employed as amodel systemto evaluate the photocatalytic activity of the TiO2 nanopowder and coated granules.
Itwas shown that the TiO2-coated granules lead to the degradation ofMB under UV irradiation,whereas no effect was observed in the dark. After the Degradation experiments the granules could be recovered and they remained active for further applications.
Al2O3 has been widely used as a coating in industrial applications due to its excellent chemical and thermal resistance. Considering high temperatures and aggressive mediums exist in geothermal systems, Al2O3 can be a potential coating candidate to protect steels in geothermal applications. In this study, γ-Al2O3 was used as a coating on martensitic steels by applying AlOOH sol followed by a heat treatment at 600 °C. To evaluate the coating application process, one-, two-, and three-layer coatings were tested in the artificial North German Basin (NGB), containing 166 g/L Cl−, at 150 °C and 1 MPa for 168 h. To reveal the stability of the Al2O3 coating in NGB solution, three-layer coatings were used in exposure tests for 24, 168, 672, and 1296 h, followed by surface and cross-section characterization. SEM images show that the Al2O3 coating was stable up to 1296 h of exposure, where the outer layer mostly transformed into boehmite AlOOH with needle-like crystals dominating the surface. Closer analysis of cross-sections showed that the interface between each layer was affected in long-term exposure tests, which caused local delamination after 168 h of exposure. In separate experiments, electrochemical impedance spectroscopy (EIS) was performed at 150 °C to evaluate the changes of coatings within the first 24 h. Results showed that the most significant decrease in the impedance is within 6 h, which can be associated with the electrolyte penetration through the coating, followed by the formation of AlOOH. Here, results of both short-term EIS measurements (up to 24 h) and long-term exposure tests (up to 1296 h) are discussed.
Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C
(2018)
Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far.