Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (80)
- Vortrag (52)
- Beitrag zu einem Tagungsband (23)
- Beitrag zu einem Sammelband (13)
- Posterpräsentation (12)
- Buchkapitel (2)
- Forschungsbericht (1)
Sprache
- Englisch (116)
- Deutsch (64)
- Mongolisch (3)
Schlagworte
- Glass (26)
- Sintering (20)
- Crystallization (10)
- LTCC (9)
- Viscosity (8)
- Foaming (7)
- Glas (7)
- Sintern (7)
- Water content (5)
- Crystal growth (4)
Organisationseinheit der BAM
- 5 Werkstofftechnik (51)
- 5.6 Glas (51)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.3 Sicherheit von Transportbehältern (1)
- 5.0 Abteilungsleitung und andere (1)
- 5.3 Polymere Verbundwerkstoffe (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 6 Materialchemie (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 7 Bauwerkssicherheit (1)
- 7.2 Ingenieurbau (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
Glass bricks are important transparent building materials. They are produced by joining two halves of glass pressings at 600700 °C. During this production process alkali oxides evaporate and are redeposited at the cooler inner front surfaces of the bricks. This surface layer reacts with H2O and CO2 from the residual brick atmosphere, leading to the formation of an alkali-rich silicate-hydrate layer of ≥50 nm thickness, which could be evidenced leading to a reduced nano-hardness of similar thickness, and from which NaHCO3 crystals can finally grow. Climate chamber experiments (repeated cooling between at -8 and -14 °C and reheating to 0 to 15 °C) resulted in reversible NaHCO3 crystallization and redissolution, presumably influenced by water evaporation or condensation and driven by the NaHCO3 supersaturation of the silicate-hydrate layer. Depending on the timetemperature schedule, different crystal morphologies became visible in this closed system, e.g. isolated spherical crystals, crystals arranged in chains and in double-chains, respectively, which can limit already the transmittance of the glass bricks. When a crack occurs or the brick is opened, the hygroscopic NaHCO3 crystals take up more H2O from the ambient, react irreversibly with the glass surface, finally leading to a total loss of transmittance.
Surface crystallization
(2004)
The effect of elastic stress and relaxation on crystal nucleation in lithium disilicate glass
(2004)
In the framework of a general theoretical approach recently developed, the effect of elastic stresses on the rate of nucleation of crystallites of critical sizes in the process of crystallization of lithium disilicate glasses is studied. Hereby both the evolution of elastic stresses due to changes in the specific volume of the crystallizing system (i.e., differences in the densities of the melt and the crystal) and their relaxation connected with viscous flow are taken into consideration. If the classical theory of nucleation is employed for the determination of the nucleation rates (modified by taking into account elastic stresses), elastic stresses may lead, for the system under consideration, to a decrease of the nucleation rate by up to two orders of magnitude. As shown, the theory allows an at least qualitatively correct incorporation of the effect of elastic stresses and stress relaxation into the description of nucleation phenomena in glass-forming melts.
Zuordnung von Hydroxylgruppen- und Wasserbanden in den Schwingungsspektren wasserarmer Silicatgläser
(2001)
Two fluorescent dyes were incorporated into sol-gel derived SiO2 matrices. The dye was added to SiO2 precursors of different degrees of pre-condensation and the spectroscopic properties of the immobilized dye were measured at various aging and drying stages of the resulting gels. The significant influence of the processing parameters on the spectroscopic properties is manifested in the relative intensity of a second red shifted emission band (550560 nm), which was observed besides the typical coumarin emission band (495 nm). The appearance of this long wavelength emission might be attributed to dye aggregation or to other reactions with the ambient matrix forced by micro porosity phenomena.