Sintering, crystallization, and foaming of 44.8SiO2–2.5P2O3–36.5CaO–6.6Na2O–6.6K2O–3.0CaF2 (F3) and 54.6SiO2–1.7P2O3–22.1CaO–6.0Na2O–7.9K2O–7.7MgO (13–93) bioactive glass powders milled in isopropanol and CO2 were studied via heating microscopy, differential thermal analysis, vacuum hot extraction (VHE), Infrared spectroscopy, and time-of-flight secondary ion mass spectrometry. Full densification was reached in any case and followed by significant foaming.
VHE studies show that foaming is driven by carbon gases and carbonates were detected by Infrared spectroscopy to provide the major foaming source. Carbonates could be detected even after heating to 750◦C, which hints on a thermally very stable species or mechanical trapping. Otherwise, dark gray compact colors for milling in isopropanol indicate the presence of residual carbon as well. Its significant contribution to foaming, however, could not be proved and might be
limited by the diffusivity of oxygen needed for carbon oxidation to carbon gas.
The lecture focuses on the mechanisms of non-desired gas bubble formation and foaming during the sintering of glass powder compacts. It is shown that foaming is driven by carbon gases and that carbonates, encapsulated in micropores or mechaniacally dissolved beneath the glass surface, provide the major foaming source.
Barium silicate glass powders 4 h milled in CO2 and Ar and sintered in air are studied with microscopy, total carbon analysis, differential thermal Analysis (DTA), vacuum hot extraction mass spectroscopy (VHE-MS), Fourier-transformed infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and time-of-flight secondary-ion mass spectrometry (TOF-SIMS). Intensive foaming of powder compacts is evident, and VHE studies prove that foaming is predominantly caused by carbonaceous species for both milling gases. DTA Shows that the decomposition of BaCO3 particles mix-milled with glass powders occurs at similar temperatures as foaming of compacts. However, no carbonate at the glass surface could be detected by FTIR spectroscopy, XPS, and TOF-SIMS after heating to the temperature of sintering. Instead, CO2 molecules unable to rotate identified by FTIR spectroscopy after milling, probably trapped by mechanical dissolution into the glass bulk. Such a mechanism or microencapsulation in cracks and particle aggregates can explain the contribution of Ar to foaming after intense milling in Ar atmosphere. The amount of CO2 molecules and Ar, however, cannot fully explain the extent of foaming. Carbonates mechanically dissolved beneath the surface or encapsulated in cracks and micropores of particle aggregates are therefore probably the major foaming source.
Glasses in the systems Me2O-ZnO-B2O3 with Me = Li, Na, K, Rb (MeZB), Na2O-ZnO-CuO-B2O3 (NZCuB), CaO-ZnO-B2O3 (CaZB), and Li2O-PbO-B2O3 (LPbB) as a reference, were studied by differential thermal analysis, dilatometry, rotational viscometry, and heating microscopy. A decrease of viscosity and sintering range was found with decreasing number of fourfold coordinated boron. The viscosity of the alkali zinc borate glasses varies only slightly. LPbB and CaZB stand out by their reduced and increased viscosities, respectively. Sodium, potassium, and calcium zinc borate glasses possess a fragility above 76. All glasses were sintered to full density before crystallization. Mostly binary zinc borate phases govern crystallization. A ternary crystalline phase was detected only in the potassium containing sample. The Weinberg glass stability parameter ranges between 0.07 and 0.12. This is caused by the presence of several crystalline phases and varying melting points of even the same crystalline phase in different glass matrices.
Sintering of LTCC
(2008)
Low Temperature Co-fired Ceramic materials (LTCC) have attracted growing interest in recent years since they are promising candidates for highly integrated ceramic packaging. This paper surveys materials concepts of related glass ceramic composites (GCC) and discusses unsolved problems and challenges. The densification of GCC based on "viscous sintering" may be affected by steric effects and partial dissolution of dispersed crystal particles, crystallization and phase boundary reactions.
Chemical variability is a main strength of glass. Glass powders are therefore promising candidates for manufacturing a broad diversity of sintered materials like sintered ¬glass-ceramics, glass matrix composites or glass bonded ceramics with tailored mechanical, thermal, electrical and optical properties and complex shape. Its wide and precise adjustability makes this class of materials, even if it may not be obvious at first sight, a key component of advanced technologies. Manufacture and processing of initial glass powders often allow even more flexibility in materials design. At the same time, however, they can cause additional problems. The lecture illustrates possible consequences of glass powder processing upon glass crystallization and sintering as well as chances for targeted utilization. Simple kinetic models describing the effect of particle size distribution, surface crystallization and rigid inclusions on sintering as well effects of different milling and seeding on sinter crystallization are presented.
The manufacture of sintered glasses and glass-ceramics, glass matrix composites, and glass-bounded ceramics or pastes is often affected by gas bubble formation. Against this background, we studied sintering and foaming of barium silicate glass powders used as SOFC sealants using different powder milling procedures. Sintering was measured by means of heating microscopy backed up by XPD, differential thermal analysis, vacuum hot extraction (VHE), and optical and electron microscopy. Foaming increased significantly as milling progressed. For moderately milled glass powders, subsequent storage in air could also promote foaming. Although the powder compacts were uniaxially pressed and sintered in air, the milling atmosphere significantly affected foaming. The strength of this effect increased in the order Ar ≈ N2 < air < CO2. Conformingly, VHE studies revealed that the pores of foamed samples predominantly encapsulated CO2, even for powders milled in Ar and N2. Results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface. Foaming could be substantially reduced by milling in water and 10 wt% HCl.
Advanced methods for 3D green density characterization like computed tomography and 3D FE sinter modeling can be utilized for increasing the reliability of sintered components. The experimental in situ observation of sintering, however, is currently restricted to silhouette methods, i.e. heating microscopy. For complex shaped samples, in situ shape screening during shrinkage would allow much better validation of 3D sinter simulation models. Further, by revealing temporary sinter warpage, 3D high-temperature shape screening allows to locate potential defects of complex sintered components. Against this background, BAM developed a testing device for in situ 3D high-temperature shape screening for ceramic and glass-ceramic tapes up to 1000°C [1-3]. Current work is focused on dropping this restriction in sample shape and temperature. The poster illustrates the current state of this work and possible applications of the method e.g. in detecting sinter warpage of metallized glass-ceramic LTCC tapes.
The manufacture of sintered glasses and glass-ceramics, glass Matrix composites and glass-bounded ceramics or pastes is often affected by gas bubble formation. Against this background, we studied sintering and foaming of barium silicate glass powders used as SOFC sealants using different powder milling scenarios. Sintering was measured by means of heating microscopy backed up by XPD, DTA, Vacuum Hot Extraction (VHE) and optical and electron microscopy. Foaming increased significantly as milling progressed. For moderately milled glass powders, subsequent storage in air could also promote foaming. Although the powder compacts were uniaxially pressed and sintered in air, the milling environment significantly affected foaming. The strength of this effect increased in the order Ar >> N2 < air < CO2. Conformingly, VHE studies revealed that the pores of aerated samples predominantly encapsulated CO2, even for powders milled in Ar and N2. Results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface. Foaming could be substantially reduced by milling in water and 10 wt% HCl.
Electric contacts based on silver-glass dispersions are key components in optoelectronic microsystems and control modules for medical, information & communication and energy technology in our networked society. Driven by the complexity of modern production processes and ever shorter time-to-market requirements, the fast and specific development of tailored silver-glass dispersions has become a bottleneck of technology development. Nevertheless, the underlying mechanisms of silver dissolution, transport, and reprecipitation, and the resulting micro structure evolution during firing are poorly understood. The broad literature on the precipitation of colloidal silver particles and the related processes of silver dissolution and diffusion mostly refer to very small volume fractions of silver. Transferring these results to the sintering of glass-containing silver dispersions, is therefore highly questionable. In this case, silver dissolution, electrical contact between silver particles, transport and reprecipitation take place under special conditions. This includes short diffusion lengths (particle size < 10 μm), the presence of three-phase contacts silver - glass - sintering atmosphere, as well as silver reprecipitation at the sintering contacts as the driving force of silver transport. Here, a dynamic balance of the silver concentration can be expected to result from the ratio between silver dissolution and reprecipitation. The aim of the project is to gain basic insight into the mechanisms of dissolution, transport and reprecipitation of silver in sintering silver glass dispersions. In this context, the main focus is on gaining basic knowledge about the dissolution of metallic silver in low melting oxide glasses as the limiting factor of the sintering of silver-glass composites. In particular, we will strive to gain insight into the effect of the oxygen content of the sintering atmosphere, of the oxygen dissolved in the silver particles, of silver oxide on the surface of the silver powder, of the electric contact between the silver particles, as well as the basicity of the glass. Furthermore, we strive for insights into the silver mobility and the silver concentration that can be attained (silver solubility) in oxide glasses with a low melting point. Summing up all these aspects, a closed explanatory model for silver dissolution, transport and reprecipitation during the sintering of glass silver dispersions will be introduced.
Electric contacts based on silver-glass dispersions are key components in optoelectronic microsystems and control modules for medical, information & communication and energy technology in our networked society. Driven by the complexity of modern production processes and ever shorter time-to-market requirements, the fast and specific development of tailored silver-glass dispersions has become a bottleneck of technology development. Nevertheless, the underlying mechanisms of silver dissolution, transport, and reprecipitation, and the resulting micro structure evolution during firing are poorly understood. The broad literature on the precipitation of colloidal silver particles and the related processes of silver dissolution and diffusion mostly refer to very small volume fractions of silver. Transferring these results to the sintering of glass-containing silver dispersions, is therefore highly questionable. In this case, silver dissolution, electrical contact between silver particles, transport and reprecipitation take place under special conditions. This includes short diffusion lengths (particle size < 10 μm), the presence of three-phase contacts silver - glass - sintering atmosphere, as well as silver reprecipitation at the sintering contacts as the driving force of silver transport. Here, a dynamic balance of the silver concentration can be expected to result from the ratio between silver dissolution and reprecipitation. The aim of the project is to gain basic insight into the mechanisms of dissolution, transport and reprecipitation of silver in sintering silver glass dispersions. In this context, the main focus is on gaining basic knowledge about the dissolution of metallic silver in low melting oxide glasses as the limiting factor of the sintering of silver-glass composites. In particular, we will strive to gain insight into the effect of the oxygen content of the sintering atmosphere, of the oxygen dissolved in the silver particles, of silver oxide on the surface of the silver powder, of the electric contact between the silver particles, as well as the basicity of the glass. Furthermore, we strive for insights into the silver mobility and the silver concentration that can be attained (silver solubility) in oxide glasses with a low melting point. Summing up all these aspects, a closed explanatory model for silver dissolution, transport and reprecipitation during the sintering of glass silver dispersions will be introduced.
Sintering and foaming of barium and calcium silicate glass powder compacts have been studied for different powder milling. Sintering was measured by means of heating microscopy backed up by XRD, DTA, Vacuum Hot Extraction (VHE) and electron microscopy. Foaming intensity strongly increased with decreasing glass partiefe size. Although powder compacts were uniaxially pressed and sintered in ambient air, foaming was affected by the milling atmosphere and most intensive for milfing in C02. Conformingly, VHE studies revealed that foaming of fully sintered samples was mainly driven by C02, even for powders milled in technical air, Ar and N2. Prolonged storage of air milled barium silicate glass powders in ambient air before pressing and sintering caused further increase of foaming intensity. These findings indicate that carbonaceous species are preferentially trapped to or close beneath the powder surface during milling and later storage. The temperature range of C02 degassing from fully sintered barium and calcium silicate g/ass powder compacts fits the temperature ranges of decomposition of BaC03 and CaC03 mix-milled with the respective barium and calcium silicate glass powders.
The sintering of bioactive glasses allows for the preparation of complex structures, such as three‐dimensional porous scaffolds. Such 3D constructs are particularly interesting for clinical applications of bioactive glasses in bone regeneration, as the scaffolds can act as a guide for in‐growing bone cells, allowing for good Integration with existing and newly formed tissue while the scaffold slowly degrades. Owing to the pronounced tendency of many bioactive glasses to crystallize upon heat treatment, 3D scaffolds have not been much exploited commercially. Here, we investigate the influence of crystallization on the sintering behavior of several bioactive glasses. In a series of mixed‐alkali glasses an increased CaO/alkali metal oxide Ratio improved sintering compared to Bioglass 45S5, where dense sintering was inhibited.
Addition of small amounts of calcium fluoride helped to keep melting and sintering temperatures low. Unlike glass 13‐93, these new glasses crystallized during sintering but this did not prevent densification. Variation in bioactive glass particle size allowed for fine‐tuning the microporosity resulting from the sintering process.
Glass powders are promising candidates for manufacturing a broad diversity of sintered materials like sintered glass-ceramics, glass matrix composites or glass bonded ceramics with tailored mechanical, thermal, electrical and optical properties and complex shape. Its wide and precise adjustability makes this class of materials a key component for advanced technologies. Processing of glass or composite powders often allow even more flexibility in materials design. At the same time, however, processing can have substantial effects on the glass powder surface and sinterability. Thus, mechanical damage and surface contamination can strongly enhance surface crystallization, which may retard or even fully prevent densification. Whereas sintering and concurrent crystallization have been widely studied, partially as cooperative effort of the TC7 of the ICG, and although glass powder sintering is predominantly applied for glasses of low crystallization tendency, sintering is also limited by gas bubble formation or foaming. The latter phenomenon is much less understood and can occur even for slow crystallizing glass powders. The lecture illustrates possible consequences of glass powder processing on glass sintering, crystallization and foaming.
Glass powders are promising candidates for manufacturing a broad diversity of sintered materials like sintered glass-ceramics, glass matrix composites or glass bonded ceramics with properties and complex shape. Powder processing, however, can substantially affect sinterability, e.g. by promoting surface crystallization. On the other hand, densification can be hindered by gas bubble formation for slow crystallizing glass powders. Against this background, we studied sintering and foaming of silicate glass powders with different crystallization tendency for wet milling and dry milling in air, Ar, N2, and CO2 by means of heating microscopy, DTA, Vacuum Hot Extraction (VHE), SEM, IR spectroscopy, XPS, and ToF-SIMS. In any case, foaming activity increased significantly with progressive milling. For moderately milled glass powders, subsequent storage in air could also promote foaming. Contrarily, foaming could be substantially reduced by milling in water and 10 wt% HCl. Although all powder compacts were uniaxially pressed and sintered in air, foaming was significantly affected by different milling atmosphere and was found most pronounced for milling in CO2 atmosphere. Conformingly, VHE studies revealed that foaming is mainly driven by carbonaceous species, even for powders milled in other gases. Current results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface.
This study investigates the sintering and crystallization behavior and kinetic of the bioactive glass (BG) 13–93 with nominal composition (in mol%): 54.6 SiO2 - 1.7 P2O3 - 22.1 CaO - 6.0 Na2O - 7.9 K2O - 7.7 MgO. Sintering and crystallization were investigated non-isothermally for various particle size fractions smaller than 315 μm as well as for bulk samples. Densification was not hindered by the presence of crystalline phases across all particle size fractions. Afterwards, wollastonite was found as the dominant crystal phase at higher temperature which resorb primary surface precipitation-like quartz crystallites. The growth direction shifts into volume when the sample surface is nearly covered. The crystal growth rate of wollastonite was calculated from the crystalline surface layer thickness measured during heating. The findings of this study are relevant for the high temperature processing of BG 13–93.