Integration of magnetic functional components in LTCC Circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of p=900 were developed which can be fully densified at the Standard LTCC sintering temperature of 900 °C. Successful co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal expansion during the cooling period - especially in the temperature range below the transformation point of the glassy phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found by EDX measurements. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, i.e. a decrease of more than 50 %.
To investigate the origin of this permeability reduction, Ni-Cu-Zn ferrite laminates were sintered separately, and in combination with alumina release tapes or dielectric tapes, respectively. SEM and EDX analysis of co-fired laminates reveal differences in the ferrite grain growth behavior. Ferrite laminates with homogeneous microstructure and grain size up to 50 pm exhibit large permeability. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between high permeability and volume fraction of large ferrite grains. Regions of fine and coarse grains inside the ferrite layers show different bismuth concentration; the Bi-content is larger in regions of fine ferrite grains.
New applications of low-temperature co-fired ceramics (LTCC), such as pressure sensors or integrated functional layers, require materials that possess higher coefficients of thermal expansion (CTE). To fabricate LTCC with elevated CTE, two methods of material design are examined: firstly, glass ceramic composites (GCC), which consist of >50 vol% glass in the starting powder, and, secondly, glass-bonded ceramics (GBC), where glass is added as a sintering aid only. The CTE of GBC is mainly determined by the crystalline component. For GCC, the CTE can be well predicted, if CTE and elastic data of each phase in the microstructure are known. A nonlinear characteristic of the CTE versus phase composition was found with increasing Ecrystals/Eglass ratio and absolute CTE difference between the components. The glass composition and glass amount can be used to compensate the fixed properties of a crystalline material in a desired way. However, because the CTE and permittivity of a glass cannot be chosen independently, an optimum glass composition has to be found. For a given LTCC, it is possible to control the devitrification by shifting the glass composition. In this way, the resulting CTE values can be predicted more exactly and tailoring becomes possible. Different LTCC materials, based on the crystalline compounds Ba(La,Nd)2Ti4O12, ZrO2 (Y-TZP), SiO2 (quartz), and specially developed glasses, possessing an elevated CTE of around 10 × 10-6 K-1 while showing permittivity εr between 6 and 63, are introduced.
Novel approaches of tunable devices for millimeter wave applications based on liquid crystal (LC) are presented. In the first part of the paper, a novel concept of a tunable LC phase shifter realized in Low Temperature Cofired Ceramics technology is shown while the second part of the paper deals with a tunable high-gain antenna based on an LC tunable reflectarray. The reflectarray features continuously beam scanning in between ±25°. Also first investigations on radiation hardness of LCs are carried out, indicating that LCs might be suitable for space applications.
This paper presents, the investigation of tunable components based on LTCC technology, implementing ferroelectric tunable thick-film dielectric. The tunable loaded line phase shifters are fabricated with metal-insulator-metal (MIM) varactors to demonstrate the capabilities of this method for packaging of the tunable components. The MIM varactors consist of one tunable dielectric paste layer that is printed between two silver layers. The tunable ferroelectric paste is optimized for LTCC sintering temperature around 850°C. The phase shifters are fabricated in two different process. They were achieved a figure of merit of 24°/dB (phase shift 192°) at 3 GHz and 18°/dB (phase shift 98°) at 4.4 GHz by using seven unit cells that each unit cell consisting of two MIM varactors.
The wireless high-frequency technology requires a robust, cost-effective, and highly integrated substrate technology offering the capability for areas of tailored permittivity. The wet-chemical porosification of low temperature co-fired ceramics (LTCC) substrates offers such an approach by locally embedding air. Porosification of LTCC in both extremely acidic and alkaline media has been investigated in previous works. However, for improving the available knowledge on the porosification of LTCC with H3PO4 as a standard and a widely used etching solution, the impact of solution concentration was systematically investigated and a substantial improvement in the etching performance was achieved. Moreover, in the present study, for the first time, the intermediate pH values, and the impact of pH as a key parameter on the etching process have been investigated. For this purpose, the applicability of phosphate buffer solution (PBS) as a prospective novel etchant mixture for the porosification of a commercially available LTCC tape (Ceramtape GC) was explored. Valuable information about surface morphology, crystalline composition, and the pore structure of the etched LTCCs was gathered employing scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, and mercury porosimetry measurements. Based on these findings, the performance of PBS-based etchant systems towards the generation of porous LTCCs combining high depths of porosification with acceptable surface characteristics for subsequent metallization is demonstrated. Based on the obtained results, by application of a 0.2 mol L−1 solution of PBS, the effective relative permittivity of test samples with a thickness of approximately 600 µm and a porosification depth of 186 µm from each side, could be reduced up to 10% of its initial “as fired” value. Also, based on the measurement results and by measuring the depth of porosification, the permittivity of the etched layer was estimated to show a reduction of up to 22% compared to the initial “as fired” value.