Poly(ether-sulfone)s having an identical backbone were prepared by four different methods. First, silylated bisphenol A (BSBA) was polycondensed with 4,4'-difluorodiphenyl sulfone (DFDPS) and K2CO3 in N-methylpyrrolidone with variation of the temperature. Second, analogous polycondensation were conducted using CsF as catalyst (and no K2CO3). Third, CsF-catalyzed polycondensations BSBA and DFDPS were conducted in bulk up to 290 C. Fourth, free bisphenol was polycondensed with DFDPS or 4,4'-dichlorodiphenyl sulfone and K2CO3 in DMSO with azeotropic removal of water. MALDI-TOF mass spectroscopy revealed that the first method mainly yielded cyclic poly(ether-sulfone)s which were detected up to masses around 13 000 Da. These and other results suggest that these polycondensations take a kinetically kontrolled course at tempeatures 145 C. This interpretation is also valid for the fourth method where high yields of cycles were obtained with DFDPS. With the less reactive 4,4'-dichlorodiphenyl sulfone lower conversions, lower molecular weights and lower fractions of cycles were found. In contrast to KF (resulting from K2CO3) CsF cleaves the poly(ether sulfone) backbone at temperatures > 145 C. Smaller amounts of smaller cycles were found in these CsF-catalyzed polycondensations which were in this case the result of thermodynamically controlled "back-biting degradation".
Various dibutyltin derivatives were polycondensed with aliphatic ,-dicarboxylic acids having chain lengths from 4 (succinic acid) to 22 carbon atoms. White crystalline products were obtained from all experiments, and the structure of the products was independent of the synthetic method. Viscosity measurements revealed low molecular weights (n 1 500 Da) in all cases. Vapor pressure osmometry (VPO) measurements and matrix-assisted laser desorption time-of-flight (MALDI-TOF) mass spectrometry proved that cyclic dimers and trimer were formed from dicarboxylic acids having 6 to 16 carbons, but mainly the monomeric cycle from docosane dioic acid. Heating to 250°C did not change the structure. Therefore, the results indicate that the macrocycles are the result of a thermodynamically controlled ring-closing polycondensation. This means that linear high-molecular weight poly(dibutyltin dicarboxylate)s cannot exist above room temperature.
Various dibutyltin derivatives were polycondensed with aliphatic ,-dicarboxylic acids having chain lengths from 4 (succinic acid) to 22 carbon atoms. White crystalline products were obtained from all experiments, and the structure of the products was independent of the synthetic method. Viscosity measurements revealed low molecular weights (n 1 500 Da) in all cases. Vapor pressure osmometry (VPO) measurements and matrix-assisted laser desorption time-of-flight (MALDI-TOF) mass spectrometry proved that cyclic dimers and trimer were formed from dicarboxylic acids having 6 to 16 carbons, but mainly the monomeric cycle from docosane dioic acid. Heating to 250°C did not change the structure. Therefore, the results indicate that the macrocycles are the result of a thermodynamically controlled ring-closing polycondensation. This means that linear high-molecular weight poly(dibutyltin dicarboxylate)s cannot exist above room temperature.