Monodisperse, citrate-stabilized gold nanoparticles of sizes ranging from 15 to 40 nm were synthesized and characterized by small angle X-ray scattering and UV-vis experiments. Identical surface properties of nanoparticles of different sizes to avoid variation in the chemical surface-enhanced Raman scattering (SERS) enhancement, as well as selection of experimental conditions so that no aggregation took place, enabled the investigation of enhancement of individual nanospheres. Enhancement factors (EFs) for SERS were determined using the dye crystal violet (CV). EFs for individual gold nanospheres ranged from 102 to 103, in agreement with theoretical predictions. An increase of the EFs of individual spheres with size can be correlated to changes in the extinction spectra of nanoparticle solutions. This confirms that the increase in enhancement with increasing size results from an increase in electromagnetic enhancement. Beyond this dependence of EFs of isolated gold spheres on their size, EFs were shown to vary with analyte concentration as a result of analyte-induced aggregation. This has implications for the application of nanoparticle solutions as SERS substrates in quantitative analytical tasks.
In any given matrix control over the final particle size distribution requires a constitutive understanding of the mechanisms and kinetics of the particle evolution. In this contribution we report on the formation mechanism of silver nanoparticles embedded in a soda-lime silicate glass matrix. For the silver ion-exchanged glass it is shown that at temperatures below 410 °C only molecular clusters (diameter <1 nm) are forming which are most likely silver dimers. These clusters grow to nanoparticles (diameter >1 nm) by annealing above this threshold temperature of 410 °C. It is evidenced that the growth and thus the final silver nanoparticle size are determined by matrix-assisted reduction mechanisms. As a consequence, particle growth proceeds after the initial formation of stable clusters by addition of silver monomers which diffuse from the glass matrix. This is in contrast to the widely accepted concept of particle growth in metal–glass systems, in which it is assumed that the nanoparticle formation is predominantly governed by Ostwald ripening processes.
The synthesis and properties of a series of new structure-directing triblock copolymers with PEO-PB-PEO structure (PEO = poly(ethylene oxide) and PB = polybutadiene) and their application as superior pore-templates for the preparation of mesoporous titania coatings are reported. Starting from either TiCl4 or from preformed TiO2 nanocrystalline building blocks, mesoporous crystalline titanium oxide films with a significant degree of mesoscopic ordered pores are derived, and the pore size can be controlled by the molecular mass of the template polymer. Moreover, the triblock copolymers form stable micelles already at very low concentration, i.e., prior to solvent evaporation during the evaporation-induced self-assembly process (EISA). Consequently, the thickness of pore walls can be controlled independently of pore size by changing the polymer-to-precursor ratio. Thus, unprecedented control of wall thickness in the structure of mesoporous oxide coatings is achieved. In addition, the micelle formation of the new template polymers is sufficiently distinct from that of typical commercial PPO-PEO-PPO polymers (Pluronics; PPO = poly(propylene oxide)), so that a combination of both polymers facilitates bimodal porosity via dual micelle templating.
We report on the online coupling of asymmetrical flow field-flow fractionation (A4F) with small-angle X-ray scattering (SAXS) for the detection of nanoparticles. The A4F was used to fractionate superparamagnetic maghemite nanoparticles, which were prepared continuously with a micromixer. The outlet of the A4F was directly coupled to a flow capillary of a SAXSess instrument (Kratky type of camera). SAXS curves were recorded in a 1 s time interval. This was possible by using intense synchrotron radiation. The radii of gyration of the nanoparticles, as determined from Guinier plots, increased from 2 to 6 nm with increasing fractionation time of the A4F. A more detailed analysis of the scattering curves revealed that the particles were cylindrical in shape (nanorods), which we attributed to the micromixing preparation technique. The radii of the nanorods increased only slightly from 1.2 to 1.7 nm with increasing fractionation time, while the lengths increased strongly from 7.0 to 30.0 nm. The volume distribution of the nanorods was determined and described by Schultz-Zimm and log-normal distributions. Nanorod volumes increased from 45 to 263 nm³, corresponding to molar masses of 140 × 10³ to 820 × 10³ g mol-1. We propose A4F-SAXS coupling as a new method for analysis of nanoparticles of complex composition in solution. It allows precise online determination of the particles shape and size distributions. This method can be applied to mixtures of nanoparticles of arbitrary shapes and sizes (1-100 nm). Moreover, the total time needed for fractionation and online SAXS data recording is usually only 20 min.
A facile approach for the synthesis of monodisperse gold nanoparticles with radii in the range of 7 to 20 nm is presented. Starting from monodisperse seeds with radii of 7 nm, produced in the first step, the addition of a defined amount of additional precursor material permits distinct size regulation and the realization of predicted nanoparticle sizes. These information were derived from ex- and in situ investigations by comprehensive small angle X-ray scattering (SAXS), X-ray absorption near edge structure (XANES) and UV-Vis data to obtain information on the physicochemical mechanisms. The obtained mechanisms can be transferred to other seeded growth processes. Compared to similar approaches, the presented synthesis route circumvents the use of different reducing or stabilizing agents. The size of resulting nanoparticles can be varied over a large size range presented for the first time without a measurable change in the shape, polydispersity or surface chemistry. Thus, the resulting nanoparticles are ideal candidates for size dependence investigations.