Open Access

Active thermography with lock-in excitation is a non-destructive testing method that is also feasible for testing of carbon fiber reinforced polymers (CFRP). For validating the method extensive investigations were done during a research project in order to advance a standardization process. The most important parameters of optical and ultrasonic excitation thermography were investigated. For example, the appropriate selection of spectral sensitivity of the used infrared camera systems is important for recording undisturbed thermal signals. Regarding excitation, influences of excitation power and ultrasonic frequency were studied. Furthermore, material parameters such as CFRP layup are known for strongly affecting the results of measurement.

Larger high pressure die castings (HPDC) and decreasing wall thicknesses are raising the issue of casting defects like pores in aluminum structures. Properties of components are often strongly influenced by inner porosity. As these products are being established more and more in lightweight construction (e.g. automotive and other transport areas), non-destructive testing methods, which can be applied fast and on-site, are required for quality assurance. In this contribution, the application of active thermography for the direct detection of larger pores is demonstrated. The analysis of limits and accuracy of the method are completed by numerical simulation and the method is validated using computed tomography.

Cracks are a major issue in the field of cultural heritage. In order to evaluate the significance of a crack, a long term monitoring of the damaged region is required. However, there is a lack of easy to operate tools for such monitoring measures. Therefore, new or existing methods for other applications have to be optimised for cultural heritage investigation. The paper describes the application of such crack observation methods on a historic concrete sculpture. Beside conventional methods, like mapping by hand and ultrasonic depth profiling, a novel tracking system is presented. Furthermore, the suitability of active thermography for the investigation of cracks was investigated. The results show promising prospects for these non-destructive techniques.

Using optical excitation sources for active thermography enables a contactless, remote, and non-destructive testing of materials and structures. Currently, two kinds of temporal excitation techniques have been established: pulse or flash excitation, usingmostly flash lamps; and periodic or lock-in excitation, using halogen lamps, LED, or laser arrays. From the experimental point of view, both techniques have their advantages and disadvantages. Concerning the comparison of the testing results of both techniques, only very few studies have been performed in the past. In this contribution, the phase values obtained at flat bottom holes in steel and CFRP and the spatial resolution measured at crossed notches in steel using flash and lock-in excitation are compared quantitatively.

The detection and characterization of surface breaking cracks in steel prior to damage is a technologically as well as economically important task especially for safety-relevant structures. Detection of small cracks already during the steel production process might significantly reduce the risk of failure and reduce production costs due to an obsolete post-processing. However, the hostile environmental conditions (high temperature specimens) together with very strict requirements in current steel production (production speeds, in-line testing and evaluation) are challenging and render many well-established NDE techniques hardly applicable. We present an approach to use laser thermographic testing as a fast, remote and contactless NDE method, that addresses these challenges and might ultimately allow for online crack detection. The basic idea of laser thermographic testing, introduced by Kubiak in 1968, is the monitoring of the heat flow as induced by local heating. Disturbances within the heat flow generated by the presence of surface cracks can then be analyzed by image processing algorithms, as we have shown in previous work. The aim of the presented work is to advance laser thermographic testing to be applicable to the specific conditions of steel production environments. This purpose was met by the development of a laboratory setup that allows us to simulate production conditions, as rolling speed, specimen temperature, laser heating power and study their influence on crack detection performance. This parametric study enabled us to develop and improve data processing and crack detection algorithms with the final goal of providing optimized in-line crack detection. The studies were accompanied by comprehensive FEM simulations to intensify the understanding of the contrast formation as well as the crucial parameters influencing the performance of the method.