Filtern
Dokumenttyp
- Vortrag (6)
- Zeitschriftenartikel (4)
- Beitrag zu einem Tagungsband (4)
Sprache
- Englisch (14) (entfernen)
Schlagworte
- Alkali-activated materials (6)
- Steel corrosion (6)
- Leaching (4)
- Carbonation (3)
- Additive manufacturing (2)
- Alkali activation (2)
- Corrosion (2)
- Geopolymer (2)
- Geopolymers (2)
- Alkali-activated (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
The main objective of this work is to determine chloride migration coefficients for alkali activated fly ash-based mortars. The effect of various mixture composition is studied. The identified values will be used in simulations of chloride transport in the alkali-activated composites, mainly to determine a critical time span of exposition to chlorides causing corrosion of reinforcement. Rapid chloride migration experiments (RCM) are performed on cylindrical specimens, 100 mm diameter, 50 mm height. Low voltage electric field (10–30 V DC) is applied as a driving force for the accelerated chloride penetration. The chloride front in the sample is identified according to NT Build 492 standard after given time of penetration (depending on the electrical current ~ 3 hours) on a fracture surface using silver nitrate solution.
Further, accelerated diffusion experiments are performed in order to verify the migration coefficients obtained using RCM. The total chloride content is determined, and chloride profiles obtained on powder ground from separate layers of the specimen.
The development of alkali‐activated materials (AAMs) as an alternative to Portland cement (PC) has seen significant progress in the past decades. However, there still remains significant uncertainty regarding their long term performance when used in steel‐reinforced structures. The durability of AAMs in such applications depends strongly on the corrosion behaviour of the embedded steel reinforcement, and the experimental data in the literature are limited and in some cases inconsistent. This letter elucidates the role of the chemistry of AAMs on the mechanisms governing passivation and chloride‐induced corrosion of the steel reinforcement, to bring a better understanding of the durability of AAM structures exposed to chloride. The corrosion of the steel reinforcement in AAMs differs significantly from observations in PC; the onset of pitting (or the chloride ‘threshold’ value) depends strongly on the alkalinity, and the redox environment, of these binders. Classifications or standards used to assess the severity of steel corrosion in PC appear not to be directly applicable to AAMs due to important differences in pore solution chemistry and phase assemblage.
Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference).
Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials.
The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed.
Corrosion of steel rebars in concrete presents one of the main deterioration mechanisms limiting service life of the reinforced structures. The corrosion is accompanied by an expansion of the corrosion products causing high pressures, concrete cracking and finally spalling of a cover layer. Critical chloride concentration, loss of alkalinity and modeling of the steel corrosion are in researchers' spotlight for decades, however reinforcement corrosion in alkali activated materials is insufficiently described and understood yet.
In this work, the steel reinforcement corrosion in alkali-activated fly ash mortars is investigated in terms of electrochemical behaviour of the reinforced mortars exposed to aggressive environments such as leaching, carbonation and chloride ingress. A selected geopolymer mixture based on hard coal fly ash activated with sodium hydroxide and sodium silicate solutions is used for the steel reinforcement-corrosion experiments. The formation of passive layer on the steel rebars is observed after approx. two weeks of hardening at laboratory temperature. However, alternative heat-treatment at 80°C for several hours leads to immediate formation of the passive layer as well as to a faster strength gain (80 MPa after 24h at 80°C). Chloride-induced corrosion, leaching and carbonation resistance of the alkali activated fly ash-based concrete is studied, where leaching in deionized water or carbonation under natural conditions (~0.04 % CO2) for 300 days did not lead to corrosion of the embedded steel. On the other hand, accelerated carbonation under 100 % CO2 atmosphere lead to depassivation within two weeks.
For the additive manufacturing of large components typically powder-based methods are used. A powder is deposited layer by layer by means of a recoater, then, the component structure is printed into each individual layer. We introduce here the new method of local laser drying, which is a suspension-based method specially developed for the manufacturing of large voluminous ceramic parts. The structure information is directly written into the freshly deposited layer of suspension by laser drying. Initially, the technology was developed for ceramic suspensions, however, first experiments with geopolymers reveal a high potential for this class of materials. Metakaolin, fly ash and lithium aluminate-based one-part geopolymers were used in first experiments. The local annealing of the geopolymer slurry results in a drying and crosslinking reaction and, thus, in a local consolidation of the material. First parts made are introduced and their properties are discussed.
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes.
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet.
One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solu¬tion composition were monitored.
Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for pro¬tec¬tion of steel reinforcement in alkali-activated fly ash mortars and concretes.
Alkali-activated fly ash foams – mechanical, chemical and physical properties
Alkali-activation of fly ash together with an aluminum powder blowing agent led to the synthesis of inorganic fly ash-based foam. The aluminium powder reacts with the alkalies from the activation solution. Hydrogen is released during this reaction and creates a closed-pore structure. The amount of liquid activation solution and aluminium powder was optimized considering proper pore distribution and feasible bulk density of the resulting foam. The viscosity of the initial mix was found as a crucial factor for the foaming process as well as for the stability of the fresh foam.
The fly ash foam is characterized in terms of its compressive and flexural strength, thermal conductivity and capacity, resistance to chemically aggressive environments, fire resistance and 2D morphology. The fire resistance test shows, that almost all mass loss occurres below 500°C and the biggest volume change take place between 800°C and 1100°C. An excellent chemical durability stems mainly from the closed-pore network and absence of leachable Ca in the system. Experiments and micromechanical simulations prove that reasonable bulk densities lie in the range of 400 to 800 kg/m3.
Geopolymers present a group of novel building materials exhibiting improved chemical resistance, fire resistance and lower CO2 emissions over traditional OPC-based materials.
Corrosion of steel rebars in concrete presents one of the main deterioration mechanisms limiting service life of the reinforced structures. The corrosion is accompanied by an expansion of the corrosion products causing high pressures, concrete cracking and finally spalling of a cover layer. Critical chloride concentration, loss of alkalinity and modeling of the steel corrosion are in researchers' spotlight for decades, however steel corrosion in geopolymer materials is insufficiently described and understood yet.
An optimized geopolymer mixture based on German hard coal fly ash activated with sodium hydroxide and sodium silicate solutions was selected for steel reinforcement-corrosion experiments. The formation of passive layer on the steel rebars is observed after approx. two weeks of hardening at laboratory temperature. However, alternative heat-treatment at 80°C for several hours leads to immediate formation of the passive layer as well as to a faster strength gain (80 MPa after 24h at 80°C).
Chloride diffusion coefficient, Na+ leaching as well as carbonation rate is identified on unreinforced geopolymer mortar samples. The data are used for simulations and design of the steel rebars-corrosion experiments. The effect of chloride ingress, Na+ leaching and carbonation of the geopolymer mortar on the steel-reinforcement corrosion is studied.