The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation
(EPR) was used to determine the corrosion resistance and detect chromium depletion in all heattreated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The development of organic coatings for corrosion protection is an elaborate process with a multitude of often interminable investigations and tests of protection properties. Electrochemical methods support the processes of development to a great extent and help to understand mechanisms of action and failure. They are usually carried out on applied coating systems with a completed formulation. An examination possibility is presented in this publication that enables the characterization of waterbased coatings with different formulation variations in the liquid (aqueous) state with the aid of electrochemical noise technique. Thus, selection of binders, pigments, and other additives is supported essentially and made more efficient in a very early Phase of formulation development. The paper shows that a unique insight into the dynamic processes of a metal in contact with an aqueous coating dispersion is possible using the example of the development of zinc-free corrosion-inhibiting pigments for waterbased coatings. In addition, it is presented in which way the results correlate with the performance of applied coatings.