Methods for characterization of epoxy-functionalized substrates used for microarray applications, prepared by silanization with 3-glycidoxypropyltrimethoxysilane, have been developed. Contact angle measurements, X-ray photoelectron spectroscopy, time of flight secondary ion mass spectrometry and fluorescence based methods have been applied to investigate these epoxy-functionalized microarray substrates. The surface density of epoxy-functionalized glass slides was investigated by fluorescence labeling of surface species utilizing Rhodamine 110 as fluorescence probe.
Nitrogen rich plasma polymer films (L-PPE:N) were prepared by low-pressure RF plasma using a 1:1 mixture of ethylene and ammonia and aged for 345 d in four different ambient conditions: (i) at room temperature (RT) in air; (ii) at RT in nitrogen; (iii) at -20?°C in air and; (iv) at –20 °C in nitrogen. The films were analyzed by X-ray photoelectron spectroscopy (XPS) and by time-of-flight secondary ion mass spectrometry (ToF-SIMS) at various intervals over the duration of the experiment. The ageing of primary amines, NH2, was followed by chemical derivatization with 4-trifluoromethyl benzaldehyde. Storage at –20 °C, mostly independently of ambient atmosphere, slowed down ageing to almost undetectable levels as evaluated by the analytical methods used for this study.
A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.
Functionalized organic layers prepared by plasma processes have complex surface chemistries. The problem of elucidating such chemistries is an extensively studied subject. One of the preponderant methods used to acquire information on specific functional groups is chemical derivatization XPS. In this communication, we focus on rather popular chemical derivatization XPS approaches, for instance, the quantification of amines with 4-trifluoromethyl benzaldehyde and of hydroxyl groups with trifluoroacetic anhydride. Although these procedures have been used for a long period by various laboratories, the use of varying protocols is obvious. Comparison of results is therefore difficult. We discuss steps toward a valid experimental procedure, in particular, the calculation of concentrations, the preparation of test samples, the pitfalls, and the shortcomings.
Carbohydrate films on gold based on dimannoside thiols (DMT) were prepared, and a complementary surface chemical analysis was performed in detail by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), near-edge X-ray absorption fine structure (NEXAFS), FT-IR, and contact angle measurements in order to verify formation of ω-carbohydrate-functionalized alkylthiol films. XPS (C 1s, O 1s, and S 2p) reveals information on carbohydrate specific alkoxy (C–O) and acetal moieties (O–C–O) as well as thiolate species attached to gold. Angle-resolved synchrotron XPS was used for chemical speciation at ultimate surface sensitivity. Angle-resolved XPS analysis suggests the presence of an excess top layer composed of unbound sulfur components combined with alkyl moieties. Further support for DMT attachment on Au is given by ToF-SIMS and FT-IR analysis. Carbon and oxygen K-edge NEXAFS spectra were interpreted by applying the building block model supported by comparison to data of 1-undecanethiol, poly(vinyl alcohol), and polyoxymethylene. No linear dichroism effect was observed in the angle-resolved C K-edge NEXAFS.
Self-assembled monolayers of aromatic omega-aminothiols on gold: surface chemistry and reactivity
(2010)
Amino-terminated self-assembled monolayers on gold substrates were studied by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure (NEXAFS) measurements, and atomic force microscopy (AFM). Two different ω-amino-4,4'-terphenyl substituted alkanethiols of the general structure H2N-(C6H4)3-(CH2)n-SH (ATPn) were used: 2-(4''-amino-1,1':4',1''-terphenyl-4-yl)ethane-1-thiol (n = 2, ATP2) and 3-(4''-amino-1,1':4',1''-terphenyl-4-yl)propane-1-thiol (n = 3, ATP3). Moreover, the addressability of amino groups within the films was investigated by chemical derivatization of ATPn SAMs with 3,5-bis(trifluoromethyl)phenyl isothiocyanate (ITC) forming fluorinated thiourea ATPn-F films. Evaluation of high-resolution C 1s and N 1s XPS data revealed successful derivatization of at least 50% of surface amino species. Furthermore, it could be demonstrated by angle-resolved NEXAFS spectroscopy that chemical derivatization with ITC has no noticeable influence on the preferential upright orientation of the molecules in the SAMs.
We investigated the ageing of amine-terminated
self-assembled monolayers (amine-SAMs) on different silica
substrates due to exposure to different ambient gases,
pressures, and/or temperatures using time-of-flight secondary
ion mass spectrometry (ToF-SIMS) with principal component
analysis and complementary methods of surface
analysis as X-ray photoelectron spectroscopy (XPS) and
near edge X-ray absorption fine structure (NEXAFS). The
goal of this study is to examine the durability of primary
amine groups of amine-SAMs stored in a user laboratory
prior to being used as supports for biomolecule immobilization
and other applications. We prepared amine-SAMs on
the native oxides of silicon wafers and glass slides using 3-
aminopropyl triethoxysilane, by using optimized conditions
such as anhydrous organic solvent and reaction time scale of
hours to avoid multilayer growth. Selected commercial
amine-SAM slides have been investigated, too. When the
amine-SAMs are exposed to air, oxygen incorporation
occurs, followed by formation of amide groups. The formation
of oxygen species due to ageing was proved by ToFSIMS,
XPS, and NEXAFS findings such as CNO- secondary
ion emission at m/z 42, observation of the N 1s HNC=O
component peak at 400.2400.3 eV in XPS, and, last but not
least, by formation of a π*(HNC=O) resonance at 401 eV in
the N K-edge X-ray absorption spectrum. It is concluded
that the used multi-method approach comprising complementary
ToF-SIMS, XPS, and NEXAFS analyses is well
suited for a thorough study of chemical aspects of ageing
phenomena of amine-SAM surfaces.
Research on carbohydrate based interactions with proteins, nucleic acids or antibodies has gained increased interest in the last years especially in clinical diagnosis or drug development. The efficiency of diagnostic interfaces depends upon the number of probe molecules, e.g. carbohydrates. The control of surface parameters as density and distribution of immobilized carbohydrates is essential for a reliable interaction with protein analytes. A controlled production of biomolecular interfaces can be reached by a stepwise quality control during buildup of these biointerfaces.
Here, ß-amino-cyclodextrin molecules were attached to amine-reactive silicon oxide surfaces via click chemistry to construct a model biosensor surface. The amount of surface bound carbohydrates was determined indirectly after chemical derivatization with 4-(trifluoromethyl)-benzylamine (TFMBA). Moreover, these surfaces were used to form host-guest complexes of ferrocene (guest) and β-cyclodextrin (host) moieties to mimic the target binding (sensing) of the model biosensor. Surface chemical analysis of all steps during biosensor construction was performed using X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine structure spectroscopy (NEXAFS). Our approach widens the possibilities to generate switchable surfaces based on ß-Cyclodextrin surfaces for biosensor applications.
The growing interest in artificial bioorganic Interfaces as a platform for applications in emerging Areas as personalized medicine, clinical diagnostics, biosensing, biofilms, prevention of biofouling, and other fields of bioengineering is the origin of a need for in Detail multitechnique characterizations of such layers and interfaces. The in-depth analysis of biointerfaces is of special interest as the properties of functional bioorganic coatings can be dramatically affected by in-depth variations of composition.
In worst cases, the functionality of a device produced using such coatings can be substantially reduced or even fully lost.