A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.
Carbohydrate films on gold based on dimannoside thiols (DMT) were prepared, and a complementary surface chemical analysis was performed in detail by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), near-edge X-ray absorption fine structure (NEXAFS), FT-IR, and contact angle measurements in order to verify formation of ω-carbohydrate-functionalized alkylthiol films. XPS (C 1s, O 1s, and S 2p) reveals information on carbohydrate specific alkoxy (C–O) and acetal moieties (O–C–O) as well as thiolate species attached to gold. Angle-resolved synchrotron XPS was used for chemical speciation at ultimate surface sensitivity. Angle-resolved XPS analysis suggests the presence of an excess top layer composed of unbound sulfur components combined with alkyl moieties. Further support for DMT attachment on Au is given by ToF-SIMS and FT-IR analysis. Carbon and oxygen K-edge NEXAFS spectra were interpreted by applying the building block model supported by comparison to data of 1-undecanethiol, poly(vinyl alcohol), and polyoxymethylene. No linear dichroism effect was observed in the angle-resolved C K-edge NEXAFS.
Self-assembled monolayers of aromatic omega-aminothiols on gold: surface chemistry and reactivity
(2010)
Amino-terminated self-assembled monolayers on gold substrates were studied by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure (NEXAFS) measurements, and atomic force microscopy (AFM). Two different ω-amino-4,4'-terphenyl substituted alkanethiols of the general structure H2N-(C6H4)3-(CH2)n-SH (ATPn) were used: 2-(4''-amino-1,1':4',1''-terphenyl-4-yl)ethane-1-thiol (n = 2, ATP2) and 3-(4''-amino-1,1':4',1''-terphenyl-4-yl)propane-1-thiol (n = 3, ATP3). Moreover, the addressability of amino groups within the films was investigated by chemical derivatization of ATPn SAMs with 3,5-bis(trifluoromethyl)phenyl isothiocyanate (ITC) forming fluorinated thiourea ATPn-F films. Evaluation of high-resolution C 1s and N 1s XPS data revealed successful derivatization of at least 50% of surface amino species. Furthermore, it could be demonstrated by angle-resolved NEXAFS spectroscopy that chemical derivatization with ITC has no noticeable influence on the preferential upright orientation of the molecules in the SAMs.
We investigated the ageing of amine-terminated
self-assembled monolayers (amine-SAMs) on different silica
substrates due to exposure to different ambient gases,
pressures, and/or temperatures using time-of-flight secondary
ion mass spectrometry (ToF-SIMS) with principal component
analysis and complementary methods of surface
analysis as X-ray photoelectron spectroscopy (XPS) and
near edge X-ray absorption fine structure (NEXAFS). The
goal of this study is to examine the durability of primary
amine groups of amine-SAMs stored in a user laboratory
prior to being used as supports for biomolecule immobilization
and other applications. We prepared amine-SAMs on
the native oxides of silicon wafers and glass slides using 3-
aminopropyl triethoxysilane, by using optimized conditions
such as anhydrous organic solvent and reaction time scale of
hours to avoid multilayer growth. Selected commercial
amine-SAM slides have been investigated, too. When the
amine-SAMs are exposed to air, oxygen incorporation
occurs, followed by formation of amide groups. The formation
of oxygen species due to ageing was proved by ToFSIMS,
XPS, and NEXAFS findings such as CNO- secondary
ion emission at m/z 42, observation of the N 1s HNC=O
component peak at 400.2400.3 eV in XPS, and, last but not
least, by formation of a π*(HNC=O) resonance at 401 eV in
the N K-edge X-ray absorption spectrum. It is concluded
that the used multi-method approach comprising complementary
ToF-SIMS, XPS, and NEXAFS analyses is well
suited for a thorough study of chemical aspects of ageing
phenomena of amine-SAM surfaces.
Research on carbohydrate based interactions with proteins, nucleic acids or antibodies has gained increased interest in the last years especially in clinical diagnosis or drug development. The efficiency of diagnostic interfaces depends upon the number of probe molecules, e.g. carbohydrates. The control of surface parameters as density and distribution of immobilized carbohydrates is essential for a reliable interaction with protein analytes. A controlled production of biomolecular interfaces can be reached by a stepwise quality control during buildup of these biointerfaces.
Here, ß-amino-cyclodextrin molecules were attached to amine-reactive silicon oxide surfaces via click chemistry to construct a model biosensor surface. The amount of surface bound carbohydrates was determined indirectly after chemical derivatization with 4-(trifluoromethyl)-benzylamine (TFMBA). Moreover, these surfaces were used to form host-guest complexes of ferrocene (guest) and β-cyclodextrin (host) moieties to mimic the target binding (sensing) of the model biosensor. Surface chemical analysis of all steps during biosensor construction was performed using X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine structure spectroscopy (NEXAFS). Our approach widens the possibilities to generate switchable surfaces based on ß-Cyclodextrin surfaces for biosensor applications.
We report a surface analytical study of poly(methyl methacrylate) (PMMA) microparticles (beads) with a grafted shell of poly(acrylic acid) (PAA) with thicknesses up to 4 nm using scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and near-edge X-ray adsorption fine structure (NEXAFS) spectroscopy. These polymer microparticles were analyzed before and after reaction of the surface carboxyl (CO2H) groups with 2,2,2-trifluoroethylamine (TFEA) to gain a better understanding of methods with use of covalently bound probe molecules for surface group analysis. The results obtained with chemical derivatization XPS using TFEA are discussed in terms of surface quantification of reactive CO2H groups on these PAA-coated microparticles. A labeling yield of about 50% was found for TFEA-derivatized particles with amounts of surface-grafted CO2H groups of 99 µmol/g or more, which is consistent with predicted reaction yields for homogeneously dispersed PAA hydrogels.
Functionalised surfaces are of interest in many fields, e.g. in biomedicine, materials science and molecular electronics. In this study a series of self-assembled aliphatic and aromatic monolayers on gold substrates with terminal amino groups was investigated. Four different thiol molecules were used: aliphatic 11-aminoundecane-1-thiol (AUDT), aromatic 4-aminobenzenethiol (ABT) and aromatic ω-amino thiols with an alkyl spacer as 4-aminophenylbutane-1-thiol (APBT) and 3-(4''-amino-1,1':4',1''-terphenyl-4-yl)propane-1-thiol (ATPT). Evaluation of N 1s XPS data revealed that on the aromatic self-assembled monolayers (SAMs) amino groups exist preferentially as primary amines, whereas on the aliphatic SAM protonated and/or hydrogen-bonded amines are the major species. This result is crosschecked by N K edge near edge X-ray absorption fine structure (NEXAFS) spectroscopy and can be rationalised by the different basicity of aliphatic and aromatic amines.
A sealable ultrathin window sample cell for the study of liquids by means of soft X-ray spectroscopy
(2017)
A new sample cell concept for the analysis of liquids or solid-liquid interfaces using soft X-ray spectroscopy is presented, which enables the complete sealing of the cell as well as the Transport into vacuum via, for example, a load-lock system. The cell uses pressure monitoring and active as well as passive pressure regulation systems, thereby facilitating the full control over the pressure during filling, sealing, evacuation, and measurement. The cell design and sample preparation as well as the crucial sealing procedure are explained in detail. As a first proof-of-principle experiment, successful nitrogen K-edge fluorescence yield near-edge X-ray absorption fine structure experiments of a biomolecular solution are presented. For this purpose, it is shown that the careful evaluation of all involved parameters, such as window type or photon flux, is desirable for optimizing the experimental result.
Biomedical applications, including functional biomaterials, carbohydrate-arrays, and glycan-based biosensors.
The chemistry of glycan immobilization plays an essential role in the bioavailability and function of surface bound carbohydrate moieties. For biomedical applications the stability over time (shelf life) of glycan arrays is a crucial factor. Herein we report on approaches for surface and interface characterization relevant to the needs of production of glycan microarrays which were tested using model carbohydrate surfaces. For detailed characterization of glycan model surfaces we used a combination of X-ray photoelectron spectroscopy (XPS), near edge X-ray absorption fine structure spectroscopy (NEXAFS) and ToF SIMS which are complementary techniques of surface chemical analysis. Links to fluorescence spectroscopy often used for characterization in the microarray community were established as well. In detail, amine-reactive silicon oxide and glass surfaces were used for anchoring oligosaccharides with an amino linker. The amount of surface bound carbohydrates was estimated by X-ray photoelectron spectroscopy (XPS). Glycan immobilization was investigated using lectins, which are glycan-binding molecules. A shelf life study of model glycan microarrays on epoxy-coated glass surfaces was done over a period of 160 days under different storage conditions utilizing fluorescence, ToF-SIMS and XPS analysis. It was shown that glycan activity of the models used can be maintained at least for half a year of storage at 4 °C.