The studied aluminium alloy is EN AW-2618A (2618A). It is very widely used for exhaust gas turbo-charger compressor wheels. Due to long operating times, high cycle fatigue (HCF) and material aging under the influence of temperatures up to 230 °C is particularly relevant for the wheels. The wheels are typically milled from round wrought blanks. From such round blanks, different testpieces are extracted and a comprehensive series of HCF tests is conducted at room temperature. The tests investigate the materials fatigue performance in the T61 state for two load-ratios, namely R = -1 and R = 0.1. Additionally, two overaged material states are tested, accounting for the aging process the material undergoes during long operating times at high temperatures. The experimental results are evaluated and compared to each other.
Furthermore, the design process of notched specimens is presented. With the notched specimens, it is aimed to quantify the notch sensitivity of the material. Relating thereto, two potential model parameters for the fatigue lifetime model are introduced. Finally, the extended research data management in this project is highlighted and its advantages for sustainable use in material science and engineering applications are shown.
Die hohen Betriebstemperaturen während des Einsatzes von Radialverdichterrädern in Abgasturboladern führen zu einer Änderung der ursprünglich eingestellten Mikrostruktur in der warmfesten Aluminiumlegierung EN AW-2618A (Überalterung). Grund dafür sind thermische Belastungen, die nahe der Aushärtetemperatur liegen und diese kurzzeitig sogar überschreiten können. Die Alterungsmechanismen wurden zusammen mit den Themen niederzyklische (LCF) und thermomechanische Ermüdung (TMF) sowie Kriechen bis max. 190 °C in vorangegangenen Forschungsvorhaben untersucht. Kaum untersucht war bisher das Verhalten der Legierung unter hochzyklischer Beanspruchung (HCF) sowie der Einfluss von Kerben und Lastkollektiven. Da zukünftig mit weiter steigenden Betriebstemperaturen für Radialverdichter zu rechnen ist, wurde in diesem Forschungsvorhaben das HCF-Verhalten bei 230 °C untersucht und somit bei einer Prüftemperatur, die deutlich oberhalb der Aushärtetemperatur liegt. Das Ziel des Projektes war der Aufbau einer geeigneten experimentellen Datenbasis, das Verständnis der relevanten mikrostrukturellen Prozesse sowie die Weiterentwicklung und Anpassung geeigneter Modelle und Bewertungsmethoden.
Das experimentelle Untersuchungsprogramm umfasste neben einer Basischarakterisierung des HCF-Verhaltens am Ausgangszustand T61 gezielte mechanische Versuche zur Isolierung der Einflussfakto-ren Mittelspannung (𝑅 = −1, 𝑅 = 0,1), Werkstoffüberalterung (T61, 10 h/230 °C, 1000 h/230 °C), Prüftemperatur (20 °C, 230 °C), Prüffrequenz (0,2 Hz, 20 Hz) sowie Kerbwirkung und variable Amplituden. Darauf aufbauend wurden die in den vorangegangenen Projekten entwickelten Modelle und Bewertungsmethoden angepasst und weiterentwickelt, um die genannten thermischen und mechanischen Belastungen in der Lebensdauerbewertung abzubilden.
The article covers data on the Brinell hardness of the forged precipitation-hardened aluminum alloy EN AW-2618A in the initial T61 condition (i. e. slightly underaged) and after isothermal aging for up to 25,0 0 0 h at aging temperatures between 160 °C and 350 °C. In addition, the hardness was determined on specimens after creep testing at 190 °C and various stresses. The hardness decreases with increasing ag- ing time due to the microstructural evolution of the harden- ing precipitates. The drop occurs faster the higher the aging temperature. Aging under creep load additionally accelerates the hardness decrease.
A study was made on the effect of creep loading on the precipitate radii evolution of the aluminum alloy 2618A.
The overageing process of the alloy was investigated under load at a temperature of 190 °C with stresses between 79 and 181 MPa and compared to stress free isothermal ageing. The precipitates responsible for strength were characterized using dark-field transmission electron microscopy (DFTEM). This allows the experimental Determination of radii distributions of the rod-shaped Al2CuMg precipitates and the evaluation regarding their mean precipitate radius. It was found that the mean precipitate radius enables the comparison of the different microstructural conditions of crept and uncrept samples. The mean precipitate radii of the samples experiencing creep are significantly higher than those of undeformed samples. It was shown that the acquired radii distributions are viable to determine averaged particle radii for comparison of the aged samples. A ripening process including pipe diffusion along dislocations describes the data on coarsening very well for the creep samples.
Fatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface and is
associated with the primary phases.
In diesem Forschungsvorhaben wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus der ausscheidungs-härtbaren Aluminiumlegierung EN AW-2618A zu verbessern. Dies umfasst insbesondere die Berücksichtigung der Werkstoffalterung, mit der beim Einsatz dieser Bauteile unter entsprechender Betriebsbeanspruchung (Temperatur, Zeit, Spannung) gerechnet werden muss. Zunächst wurde eine solide experimentelle Datenbasis für den untersuchten Werkstoff geschaffen. Dies umfasste sowohl eine mechanische als auch eine mikrostrukturelle Charakterisierung des Ausgangszustands (T61) sowie von ausgelagerten Zuständen bis zu 25.000 h bei betriebsrelevanten Temperaturen (160 °C, 180 °C, 190 °C). Bei den Untersuchungen zur Mikrostruktur wurde der Fokus auf die Entwicklung der Radien der stäbchen-förmigen aushärtenden Phase gelegt, die während der Alterung vergröbern. Der Zusammenhang zwischen Auslagerungstemperatur, -zeit und ggfs. mechanischer Belastung wurde erstmals in diesem Umfang quantifiziert und entsprechende Gesetzmäßigkeiten zur Beschreibung der Vergröberung ermittelt. Vergleichend dazu wurde der Einfluss der Alterung auf die Härte, die Festigkeit, das Kriechverhalten und die Ermüdungslebensdauer (LCF, TMF) bestimmt, so dass eine Korrelation zur Mikrostruktur vorliegt.
Die Ergebnisse der Kriechversuche wurden zur Kalibrierung eines modifizierten Sinus-hyperbolicus-Kriechmodells verwendet. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. Lediglich ein LCF-Versuch mit einer Haltezeit von 900 s im Zug weicht deutlich vom Mittelwert ab und zeigt die Grenzen des zeitunabhängigen Schädigungsmodells auf. Versuche mit kürzeren Haltezeiten bis zu 60 s liegen im Streuband, ebenso die verschiedenen Alterungszustände. Eine Schädigungsakkumulation unter Berücksichtigung der fortschreitenden Alterung über der Lebensdauer wurde entwickelt und implementiert. Neben der Berücksichtigung der Alterung in der Verformungs- und Lebensdaueranalyse besteht auch die Möglichkeit, komplexe Belastungszyklen in einem Postprozessing zu bewerten, indem Rainflow-Klassierungen typischer komplexer Belastungszyklen vorgenommen werden.
Die Methodik und die Modelle wurden in die Finite-Elemente-Programme Abaqus und Ansys implementiert und stehen für die rechnerische Bewertung von Bauteilen zur Verfügung.
Die Mikrostruktur von ausscheidungsgehärteten Aluminiumlegierungen ist von herausragender Bedeutung für ihre Festigkeit, da nur Werkstoffe mit gezielt eingestellter Mikrostruktur für Radialverdichterräder ausreichende Festigkeiten erreichen. Diese optimierte Mikrostruktur ändert sich jedoch während des Betriebs, denn die Bauteile werden bei Temperaturen eingesetzt, die nahe der Aushärtetemperatur liegen oder sogar darüber hinausgehen und folglich ist mit Alterung der Mikrostruktur und damit einhergehender Degradation der Eigenschaften zu rechnen. Diese Effekte konnten bisher in der Lebensdauervorhersage nicht berücksichtigt werden, da ihre diesbezüglichen Auswirkungen lediglich qualitativ bekannt waren. In diesem Forschungsvorhaben wurde daher für die Legierung EN AW-2618A einerseits eine sorgfältige und umfassende Charakterisierung der Gefügeentwicklung für anwendungsrelevante Temperaturen und Zeiten bis zu 25.000 h vorgenommen und andererseits eine solide Datenbasis bezüglich der mechanischen Eigenschaften (Zugfestigkeit, Kriechwiderstand, LCF-, TMF-Verhalten) und ihren Änderungen geschaffen. Darauf aufbauend wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus EN AW-2618A zu verbessern. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer unter Rainflow-klassierten Betriebslastkollektiven wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein.