Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (13)
- Buchkapitel (1)
Sprache
- Englisch (14)
Schlagworte
- Bioactive glasses (2)
- NMR (2)
- Raman (2)
- Alternative test procedure (1)
- Annealing treatment (1)
- Bioactive coatings (1)
- Core-clusters (1)
- Energetic reference parameter (1)
- Extended storing (1)
- Fatigue crack growth (1)
Organisationseinheit der BAM
- 6 Materialchemie (2)
- 9 Komponentensicherheit (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.4 Sicherheit von Lagerbehältern (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.5 Röntgenbildgebung (1)
Paper des Monats
- ja (1)
KEY COMPARISON
Under the auspices of the Organic Analysis Working Group (OAWG) of the Comité Consultatif pour la Quantité de Matière (CCQM) a key comparison, CCQM K55.c, was coordinated by the Bureau International des Poids et Mesures (BIPM) in 2012. Twenty National Measurement Institutes or Designated Institutes and the BIPM participated. Participants were required to assign the mass fraction of valine present as the main component in the comparison sample for CCQM-K55.c. The comparison samples were prepared from analytical grade L-valine purchased from a commercial supplier and used as provided without further treatment or purification.
Valine was selected to be representative of the performance of a laboratory's measurement capability for the purity assignment of organic compounds of low structural complexity [molecular weight range 100300] and high polarity (pKOW > –2).
The KCRV for the valine content of the material was 992.0 mg/g with a combined standard uncertainty of 0.3 mg/g. The key comparison reference value (KCRV) was assigned by combination of KCRVs assigned from participant results for each orthogonal impurity class. The relative expanded uncertainties reported by laboratories having results consistent with the KCRV ranged from 1 mg/g to 6 mg/g when using mass balance based approaches alone, 2 mg/g to 7 mg/g using quantitative 1H NMR (qNMR) based approaches and from 1 mg/g to 2.5 mg/g when a result obtained by a mass balance method was combined with a separate qNMR result.
The material provided several analytical challenges. In addition to the need to identify and quantify various related amino acid impurities including leucine, isoleucine, alanine and a-amino butyrate, care was required to select appropriate conditions for performing Karl Fischer titration assay for water content to avoid bias due to in situ formation of water by self-condensation under the assay conditions. It also proved to be a challenging compound for purity assignment by qNMR techniques.
There was overall excellent agreement between participants in the identification and the quantification of the total and individual related structure impurities, water content, residual solvent and total non-volatile content of the sample. Appropriate technical justifications were developed to rationalise observed discrepancies in the limited cases where methodology differences led to inconsistent results.
The comparison demonstrated that to perform a qNMR purity assignment the selection of appropriate parameters and an understanding of their potential influence on the assigned value is critical for reliable implementation of the method, particularly when one or more of the peaks to be quantified consist of complex multiplet signals.
The capabilities of National Metrology Institutes (NMIsthose which are members of the Comité Consultatif pour la Quantité de Matière (CCQM)of the CIPM) and selected outside "expert" laboratories to quantitate (C4H9)3Sn+ (TBT) in a prepared marine sediment were assessed. This exercise was sanctioned by the 7th CCQM meeting, April 46, 2001, as an activity of the Inorganic Analysis Working Group and was jointly piloted by the Institute for National Measurement Standards of the National Research Council of Canada (NRC) and the Laboratory of the Government Chemist (LGC), UK. A total of 11 laboratories submitted results (7 NMIs, and 4 external labs). Two external laboratories utilized a standard calibration approach based on a natural abundance TBT standard, whereas all NMIs relied upon isotope dilution mass spectrometry for quantitation. For this purpose, a species specific 117Sn-enriched TBT standard was supplied by the LGC. No sample preparation methodology was prescribed by the piloting laboratories and, by consequence, a variety of approaches was adopted by the participants, including mechanical shaking, sonication, accelerated solvent extraction, microwave assisted extraction and heating in combination with Grignard derivatization, ethylation and direct sampling. Detection techniques included ICPMS (with GC and HPLC sample introduction), GCMS, GCAED and GCFPD. Recovery of TBT from a control standard (NRCC CRM PACS-2 marine sediment) averaged 93.5±2.4% (n=14). Results for the pilot material averaged 0.680±0.015 µmol kg1 (n=14; 80.7±1.8 µg kg1) with a median value of 0.676 µmol kg1. Overall, performance was substantially better than state-of-the-art expectations and the satisfactory agreement amongst participants permitted scheduling of a follow-up Key comparison for TBT (K-28), a Pilot intercomparison for DBT (P-43), and certification of the test sediment for TBT content and its release as a new Certified Reference Material (HIPA-1) with a TBT content of 0.679±0.089 µmol kg1 (expanded uncertainty, k=2, as Sn) (80.5±10.6 µg kg1). Electronic Supplementary Material Supplementary material is available in the online version of this article at http://dx.doi.org/10.1007/s00216-003-2016-9.
The lead authors failed to name two collaborators as co-authors. The authors listed should include:
Miss Claudia L. Compean-Gonzalez (ORCID:
0000-0002-2367-8450) and Dr. Giacomo Ceccone (ORCID:
0000-0003-4637-0771).
These co-authors participated in VAMAS project A27, provided data that were analyzed and presented in this publication (and supporting information), and reviewed the manuscript before submission.
Clustering of magnetic nanoparticles can drastically change their collective magnetic properties, which in turn may influence their performance in technological or biomedical applications. Here, we investigate a commercial colloidal dispersion (FeraSpinTMR), which contains dense clusters of iron oxide cores (mean size around 9 nm according to neutron diffraction) with varying cluster size (about 18–56 nm according to small angle x-ray diffraction), and its individual size fractions (FeraSpinTMXS, S, M, L, XL, XXL). The magnetic properties of the colloids were characterized by isothermal magnetization, as well as frequency-dependent optomagnetic and AC susceptibility measurements. From these measurements we derive the underlying moment and Relaxation frequency distributions, respectively. Analysis of the distributions shows that the clustering of the initially superparamagnetic cores leads to remanent magnetic moments within the large clusters. At frequencies below 105 rad s−1, the relaxation of the clusters is dominated by Brownian (rotation) relaxation. At higher frequencies, where Brownian relaxation is inhibited due to viscous friction, the clusters still show an appreciable magnetic relaxation due to internal moment relaxation within the clusters. As a result of the internal moment relaxation, the colloids with the large clusters (FSL, XL, XXL) excel in magnetic hyperthermia experiments.
Under the auspices of the Organic Analysis Working Group (OAWG) of the Comité Consultatif pour la Quantité de Matière (CCQM) a key comparison, CCQM K55.b, was coordinated by the Bureau International des Poids et Mesures (BIPM) in 2010/2011. Nineteen national measurement institutes and the BIPM participated. Participants were required to assign the mass fraction of aldrin present as the main component in the comparison sample for CCQM-K55.b which consisted of technical grade aldrin obtained from the National Measurement Institute Australia that had been subject to serial recrystallization and drying prior to sub-division into the units supplied for the comparison.
Aldrin was selected to be representative of the performance of a laboratory's measurement capability for the purity assignment of organic compounds of medium structural complexity [molar mass range 300 Da to 500 Da] and low polarity (pKOW < -2) for which related structure impurities can be quantified by capillary gas phase chromatography (GC).
The key comparison reference value (KCRV) for the aldrin content of the material was 950.8 mg/g with a combined standard uncertainty of 0.85 mg/g. The KCRV was assigned by combination of KCRVs assigned by consensus from participant results for each orthogonal impurity class. The relative expanded uncertainties reported by laboratories having results consistent with the KCRV ranged from 0.3% to 0.6% using a mass balance approach and 0.5% to 1% using a qNMR method.
The major analytical challenge posed by the material proved to be the detection and quantification of a significant amount of oligomeric organic material within the sample and most participants relying on a mass balance approach displayed a positive bias relative to the KCRV (overestimation of aldrin content) in excess of 10 mg/g due to not having adequate procedures in place to detect and quantify the non-volatile content–specifically the non-volatile organics content–of the comparison sample.
There was in general excellent agreement between participants in the identification and the quantification of the total and individual related structure impurities, water content and the residual solvent content of the sample.
The comparison demonstrated the utility of 1H NMR as an independent method for quantitative analysis of high purity compounds. In discussion of the participant results it was noted that while several had access to qNMR estimates for the aldrin content that were inconsistent with their mass balance determination they decided to accept the mass balance result and assumed a hidden bias in their NMR data. By contrast, laboratories that placed greater confidence in their qNMR result were able to resolve the discrepancy through additional studies that provided evidence of the presence of non-volatile organic impurity at the requisite level to bring their mass balance and qNMR estimates into agreement.
The results of a structural study combining NMR and Raman spectroscopy of several melt-derived glasses in the system Na2OMgOCaOP2O5SiO2 are presented. The Raman spectra show clear changes in the SiOSi vibrational modes (related to the bridging oxygen atoms, BO) and also verify the presence of non-bridging oxygen atoms (NBO), also named terminal oxygens. The intensity of the SiONBO stretching mode depends on the cation concentration. It can be concluded from the NMR studies that the MgO-containing samples have orthophosphate units charge-compensated by Ca2+ and Mg2+. The silicate matrix also contains both types of two-valent cations and consists of Q2 and Q1 units. Similarly, the Na2O-containing samples contain isolated orthophosphate units in a silicate matrix (Q2 and Q3 units), both charge-compensated by mixed cations Ca2+ and Na+. These experimental data were compared with theoretical parameters given by the Stevels model, which is a suitable tool for understanding bioactive behavior of these glasses. Furthermore, results of the in vitro tests carried out in simulated body fluids are presented and compared with both Raman and NMR structural data.
The results of a combined structural characterisation (XRD, IR, NMR, SEM, TEM) of a
phosphate containing Mg-Ca silicate and a phosphate containing Na-Ca silicate glass samples are
presented. The structural results are also compared with in vitro tests carried out in simulated body
fluids for checking bioactivity.
Silicon substituted Hydroxyapatite coatings were prepared by Pulsed Laser Deposition
from targets made of mixtures of Hydroxyapatite with Si powder at different concentrations. The
properties of the Si-HA coatings with several degrees of Si substitution were analyzed by different
techniques such as FTIR, XRD, XPS and solid-state NMR. It was found that the Si incorporation
causes an amorphization of the structure together with a loss of carbonate groups. Furthermore, the
Si atoms are incorporated in the form of SiO4
4- groups, and H(PO4)2- appears as the predominant
phosphate group.
An automated and straightforward detection and data treatment strategy for the determination of the protein relative concentration in individual human cells by single cell–inductively coupled plasma–time-of-flight mass spectrometry (sc-ICP-ToF-MS) is proposed. Metal nanocluster (NC)-labeled specific antibodies for the target proteins were employed, and ruthenium red (RR) staining, which binds to the cells surface, was used to determine the number of cell events as well as to evaluate the relative volume of the cells. As a proof of concept, the expression of hepcidin, metallothionein-2, and ferroportin employing specific antibodies labeled with IrNCs, PtNCs, and AuNCs, respectively, was investigated by sc-ICP-ToF-MS in human ARPE-19 cells. Taking into account that ARPE-19 cells are spherical in suspension and RR binds to the surface of the cells, the Ru intensity was related to the cell volume (i.e., the cell volume is directly proportional to (Ru intensity)3/2), making it possible to determine not only the mass of the target proteins in each individual cell but also the relative concentration. The proposed approach is of particular interest in comparing cell cultures subjected to different supplementations. ARPE-19 cell cultures under two stress conditions were compared: a hyperglycemic model and an oxidative stress model. The comparison of the control with treated cells shows not only the mass of analyzed species but also the relative changes in the cell volume and concentration of target proteins, clearly allowing the identification of subpopulations under the respective treatment.
We investigated the possibility of minimizing tensile matrix residual stresses in age hardenable aluminum alloy metal matrix composites without detrimentally affect their mechanical properties (such as yield strength).
Specifically, we performed thermal treatments at different temperatures and times in an age-hardenable aluminum matrix composite 2014Al-15vol%Al2O3. Using X-ray synchrotron radiation diffraction and mechanical tests, we show that below a certain treatment temperature (250 °C) it is possible to identify an appropriate thermal treatment capable of relaxing residual stress in this composite while even increasing its yield strength, with respect to the as processed conditions.