Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method.
Ageing at 600 °C (from 0.1 h up to 20 h) leads to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries of the lean duplex stainless steel (LDSS) X2CrNiN22-2. This leads to sensitisation due to chromium depletion and decreased pitting corrosion resistance proven by the results of various electrochemical methods (DL-EPR and determination of CPT, Epit). These results were compared with the KorroPad method, which uses an agar-based gel-electrolyte for the detection of stainless steel surfaces prone to pitting corrosion. However, the standard configuration of the KorroPad showed no differentiation for the various ageing conditions. Therefore, modified versions of the KorroPad with two, five and ten times higher NaCl and potassium ferrocyanide III (K3[Fe(CN)6]) concentrations were successfully used to visualise the behaviour detected by DL-EPR, Epit and CPT. Therefore, the KorroPad method can also detect a microstructure related reduction of pitting corrosion resistance, which can drastically reduce the experimental effort to generate sensitisation diagrams for stainless steels.
Einfluss des Schwefelgehalts auf die Korrosionsbeständigkeit des nichtrostenden Stahls 1.4404
(2016)
Die Korrosionsbeständigkeit nichtrostender Stähle wird maßgeblich von ihrer chemischen Zusammensetzung bestimmt. Der tendenzielle Einfluss ist für die Hauptlegierungselemente in der wissenschaftlichen Fachliteratur beschrieben. Bei Begleitelement Schwefel gibt es dagegen keine konkreten Untersuchungen die belegen, ab welchem Gehalt mit einer Verringerung der Korrosionsbeständigkeit zu rechnen ist. Im Lichtbogenschmelzofen wurden verschiedene Legierungen mit abgestuftem Schwefelgehalten hergestellt, um den Einfluss dieses Begleitelementes auf die Korrosionsbeständigkeit systematisch zu untersuchen. Die KorroPad-Prüfung und die Bestimmung kritischer Lochkorrosionspotentiale wurden zur Charakterisierung der Legierungen genutzt. Beide Methoden belegen eine zunehmende Verringerung der Lochkorrosionsbeständigkeit mit dem Schwefelgehalt.