Open Access

The dataset provided in this repository comprises data obtained from a series of full-notch creep tests (FNCT) performed on selected high-density polyethylene (PE-HD) materials (for further details, see section 1 Materials in this document) in accordance with the corresponding standard ISO 16770. The FNCT is one of the mechanical testing procedures used to characterize polymer materials with respect to their environmental stress cracking (ESC) behavior. It is widely applied for PE-HD materials, that are predominantly used for pipe and container applications. It is based on the determination of the time to failure for a test specimen under constant mechanical load in a well-defined and temperature controlled liquid environment. The test device used here also allows for continuous monitoring of applied force, specimen elongation and temperature.

The full-notch creep test (FNCT) is a common test method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD), e.g. for container materials. The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of PE-HD specimens under constant mechanical load in a well-defined liquid test environment. Since the craze-crack damage mechanism underlying the ESC phenomenon is associated with brittle failure, the occurrence of a predominantly brittle fracture surface is a prerequisite to consider an FNCT measurement as representative for ESC, i.e. a time to failure dominated by craze-crack propagation. The craze-crack propagation continuously reduces the effective residual cross-sectional area of the specimen during the test, which results in a corresponding increase of the effective mechanical stress. Thus, a transition to ductile shear deformation is inevitable at later stages of the test, leading usually to a pronounced central ligament. Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. An enhanced imaging analysis of FNCT fracture surfaces enables a detailed assessment of craze-crack Propagation during ESC. In this study, laser scanning microscopy (LSM) was employed to evaluate whether FNCT fracture surfaces are representative with respect to craze-crack propagation and ESC. Based on LSM height data, a phenomenological criterion is proposed to assess the validity of distinct FNCT measurements. This criterion is supposed to facilitate a quick evaluation of FNCT results in practical routine testing. Its applicability is verified on a sample basis for seven different commercial PE-HD container materials.

The craze‐crack mechanism occurring in high‐density polyethylene (HDPE) causing slow crack growth and environmental stress cracking is investigated in detail with respect to the relation of crack length and the related craze zone. This is essential for the understanding of the resulting features of the formed fracture surface and their interpretation in the context of the transition from crack propagation to ductile shear deformation. It turns out that an already formed craze zone does not inevitably result in formation of a propagating crack, but could also undergo ductile failure. For the examination, the full notch creep test (FNCT) was employed with a subsequent advanced fracture surface analysis that was performed using various imaging techniques: light microscopy, laser scanning microscopy, scanning electron microscopy, and X‐ray micro computed tomography scan. FNCT specimens were progressively damaged for increasing durations under standard test conditions applying Arkopal, the standard surfactant solution, and biodiesel as test media were used to analyze the stepwise growth of cracks and crazes. From considerations based on well‐established fracture mechanics approaches, a theoretical correlation between the length of the actual crack and the length of the preceding craze zone was established that could be evidenced and affirmed by FNCT fracture surface analysis. Moreover, the yield strength of a HDPE material exposed to a certain medium as detected by a classic tensile test was found to be the crucial value of true stress to induce the transition from crack propagation due to the craze‐crack mechanism to shear deformation during FNCT measurements. Highlights - Progress of crack formation in high‐density polyethylene is analyzed by different imaging techniques - Determined growth rates depend on distinction between craze zone and crack - The ratio of the present crack to the anteceding craze zone is validated theoretically - The transition from crack propagation to ductile shear deformation is identified - An already formed craze zone may still fail by ductile mechanisms

Phase decomposition in multi-component high-entropy alloys (HEAs) can take complex routes, on the one hand, leading to various safety concerns during their service and, on the other hand, opening vast opportunities for intelligent alloy design. Insights into a controlled decomposition of initially homogeneous HEAs are therefore essential. In this study, we combine the recently developed multi-component elastic energy theory with CALPHAD databases to study potentially magnetic FeMnNiCoCu alloy system. In a first approximation, the elastic energy is added to the Gibbs free energy to reconstruct the thermodynamic phase diagrams and consequent phase decompositions. Our results show that depending on the alloy composition and the temperature, Cu-rich and FeCo-rich phases emerge, which lead to the formation of distinct magnetic phases of different extents. The spatial redistribution of elements is studied through Fourier analysis, auto-, and cross-correlation, revealing the contribution of the thermodynamic, kinetic and elastic driving forces throughout this process. These dissembled analysis methods contribute to a more comprehensive understanding of multi-component alloys and the role of elastic energy in their phase decomposition.

Elastic energy plays a critical role in determining phase stability in compositionally complex alloys. However, quantifying elastic contributions in multi-component systems and incorporating them into phase diagram construction remain challenging. In this study, we present a generalized elastic energy formalism tailored for multi-component alloys, which can be directly and efficiently integrated with CALPHAD thermodynamic databases and existing frameworks such as Thermo-Calc (Andersson et al., 2002), Pandat (Cao et al., 2009) or FactSage (Bale et al., 2016). This elasticity formalism can also be introduced as a post-processing layer in open-source software such as pyCALPHAD (Otis and Liu, 2017) and Kawin (Ury et al., 2023) , enabling elastic assessments in multi-component systems. We apply our framework for constructing the phase diagram of quinary Fe–Mn–Ni–Co–Cu alloy system, utilizing convex hull and Hessian matrix under elastic considerations. Our results reveal that incorporating elastic energy leads to an expansion of both the spinodal region and the miscibility gap. These are governed by the intricate interplay of chemical and elastic driving forces: We found that Mn and Ni contribute strongly to chemical stabilization, while Cu and Co tend to destabilize the alloy, especially at low Mn concentrations. The stabilizing effect of Fe is also pronounced in Mn-deficient regions. Acting as a destabilizing factor, the elastic energy is primarily driven by the presence of Mn, underscoring its multifaceted role in thermodynamic stability. In Mn-rich compositions, Cu markedly reduces the elastic energy contribution. Combined with CALPHAD infrastructures, the current framework offers a practical pathway to improve the predictive accuracy of phase stability and transformations in complex multi-component alloys.