The lead authors failed to name two collaborators as co-authors. The authors listed should include:
Miss Claudia L. Compean-Gonzalez (ORCID:
0000-0002-2367-8450) and Dr. Giacomo Ceccone (ORCID:
0000-0003-4637-0771).
These co-authors participated in VAMAS project A27, provided data that were analyzed and presented in this publication (and supporting information), and reviewed the manuscript before submission.
The work explores the synthesis and the properties of a novel composite membrane System based on modified polystyrene (PS) grafted onto a polyvinyl chloride (PVC) membrane.
PVC membranes were prepared by solution-casting followed by exposure to an atmospheric pressure dielectric barrier discharge (DBD) with O2 to obtain an activated Surface for grafting PS to it. Moreover, the thus prepared membranes were chemically modified furthermore by amination with polyethyleneimine or sulfonation with 4 M sulfuric acid.
The membrane surface characteristics such as wettability, structure and morphology were investigated using water contact angle measurements, attenuated total reflection Fourier transform infrared spectroscopy and scanning electron microscopy experiments. The thermogravimetric stability and electrolytic responses of the membranes were studied utilizing TGA, ion exchange capacity (IEC), and solvent uptake. A significant result of plasma and chemical modification was to produce a membrane material with low permeability. Thus, the methanol permeability of the sulfonated membranes measured for 12 h was measured to 2.34$108 cm2 s1 compared to 177.00$108 cm2 s1 of Nafion 117®which is considered as a benchmark. This result indicates that the prepared sulfonated samples are an innovative and effective material for decreasing the methanol crossover in fuel cells to a great extent. This makes the PVC-g-St membranes are promising and attractive as new materials for polyelectrolyte membrane for fuel cells.
We report the results of a Versailles Project on Advanced Materials and Standards interlaboratory study on the intensity scale calibration of x-ray photoelectron spectrometers using low-density polyethylene (LDPE) as an alternative material to gold, silver, and copper. An improved set of LDPE reference spectra, corrected for different instrument geometries using a quartz-monochromated Al Kα x-ray source, was developed using data provided by participants in this study. Using
these new reference spectra, a transmission function was calculated for each dataset that participants provided. When compared to a similar calibration procedure using the NPL reference spectra for gold, the LDPE intensity calibration method achieves an absolute offset of ∼3.0% and a systematic deviation of ±6.5% on average across all participants. For spectra recorded at high pass energies (≥90 eV), values of absolute offset and systematic deviation are ∼5.8% and ±5.7%, respectively, whereas for spectra collected at lower pass energies (<90 eV), values of absolute offset and systematic deviation are ∼4.9% and ±8.8%, respectively; low pass energy spectra perform worse than the global average, in terms of systematic deviations, due to diminished count rates and signal-to-noise ratio. Differences in absolute offset are attributed to the surface roughness of the LDPE induced by sample preparation. We further assess the usability of LDPE as a secondary reference material and comment on its performance in the presence of issues such as variable dark noise, x-ray warm up times, inaccuracy at low count rates, and underlying spectrometer problems. In response to participant feedback and the results of the study, we provide an updated LDPE intensity calibration protocol to address the issues highlighted in the interlaboratory study. We also comment on the lack of implementation of a consistent and traceable intensity calibration method across the community of x-ray photoelectron spectroscopy (XPS) users and, therefore, propose a route to achieving this with the assistance of instrument manufacturers, metrology laboratories, and experts leading to an international standard for XPS intensity scale calibration.
X-ray photoelectron spectroscopy (XPS) is widely used for characterising the chemistry of graphene-related two-dimensional materials (GR2M), however the careful preparation of the sample for analysis is important in obtaining representative quantifications. We report an investigation by three laboratories showing that the preparation method for oxygen-functionalised graphene nanoplatelet (GNP) powders has a significant effect on the homogeneous-equivalent elemental composition measured in XPS. We show that pressing GNP powders onto adhesive tapes, into recesses, or into solid pellets results in inconsistencies in the XPS quantification. The measured oxygen-to-carbon atomic ratio from GNP pellets depends upon the die pressure used to form them and the morphology of the GNPs themselves. We recommend that powder samples of GR2Ms are pelletised prior to XPS analysis to improve repeatability and reproducibility of measurements.