Volatile Organic Compounds (VOC) are ubiquitous in the indoor air, since they emit from materials used indoors. Investigations of these materials are mostly carried out in test chambers under controlled climatic conditions. Quality control of these test chamber measurements is important but there is a lack of commercially available homogenous reference materials as required for round robin tests or quality assurance of laboratories. The approach of the present study is the impregnation of a supporting material with VOC, which are reproducibly released in measurable chamber air concentrations under standardised test conditions. A polymer made of Thermoplastic Polyurethane (TPU) was chosen as carrier material. It was impregnated with the VOC trimethyl pentanediol isobutyrat (texanol).
Volatile Organic Compounds (VOC) are ubiquitous in the indoor air since they are emitted from materials used indoors. Investigations of these materials are mostly carried out in emission test chambers under controlled climatic conditions. Reference materials are an important tool for quality assurance/Quality control of emission test chamber measurements but so far they are not commercially available. In this study, a new approach was tested to develop an appropriate reference material with homogenous and reproducible emission of the VOC with well measurable air concentrations in emission test Chambers larger than 20 L at air change rates of 0.5 - 1 /h.
Thermoplastic Polyurethane (TPU) was selected as Matrix material which was impregnated with 2,2,4- trimethyl-1,3-pentanediol monoisobutyrate (texanol) as test VOC using compressed carbon dioxide. An optimization of the impregnation parameters such as temperature, pressure, time, VOC injection volume and TPU sample size was performed until the targeted area specific Emission rate (SERa) value was reached. Further aspects like process control, storage effects and correlation of the sample size to the emission rate were investigated. It was found that the SERa immediately after sample preparation were not reproducible between the batches but became unified 10 days after loading into the test chamber indicating the necessity of aging before use. SERa between 13,000 and 18,000 mg m-2 h-1 were obtained, and the impregnated materials could be well stored in aluminum-coated polyethylene foil for at least seven weeks without significant losses. Furthermore, the impregnation of styrene and the SVOC 2,6-diisopropylnaphthalene was tested.
Two new approaches towards an emission reference material for use in quality assurance measures for materials emissions testing were developed and intensively tested. The overall goal was to obtain solid materials with homogenous and reproducible (S)VOC release. Since the application in inter-laboratory comparisons is aimed at, it should furthermore be long-term stable to ensure safe shipment to the customer without sustaining compound losses. In the first approach, thermoplastic polyurethane (TPU) was impregnated with the VOC texanol under high-pressure with liquid CO2 as solvent. In the second, styrene (VOC) and the SVOC 2,6-diisopropylnaphthalene (DIPN) were spiked into vacuum grease (VG) and a mixture of paraf-fin/squalane (P/S). For the prediction of the emission rates a finite element model (FEM) was developed for the VG and P/S type materials. All requirements for reference materials were fulfilled, whereas the TPU samples need to be aged for about 10 days until repeatable and re-producible emission rates were obtained.