Melamine resins were used as 50-µm-thick fire retardant coatings for polypropylene (PP). Preceding deposition, low-pressure plasma polymer films of allyl alcohol were coated onto PP to improve the adhesion between PP and melamine resin coatings. The efficiency of such fire retardant coatings was confirmed by flame tests. The plasma-deposited polymer and the dip-coated melamine resin films were characterized by Fourier transform infrared-attenuated total reflectance spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesion of coatings was measured using a 90° peel test with a doubled-faced adhesive tape. To detect the locus of failure, the peeled layer surfaces were inspected using optical microscopy and XPS. Thermal properties of PP thick melamine resin-coated films were analyzed by thermogravimetric analysis.
The thermal degradation behavior of poly(vinyl chloride) (PVC) and poly(N-vinylpyrrolidone) (PVP) blends was investigated using potentiometric measurements of the released HCl gas during the degradation process, estimating the degree of discoloration of the degraded samples and measuring the thermal stability values (Ts) values. The influence of the PVP percentage in the blend and, moreover, the addition of commercial dibasic lead carbonate stabilizer to the blend on its thermal stability was studied. It was found that the dehydrochlorination rate of the blend was promoted by increasing the PVP concentration in the blend.