Single particle imaging of upconversion nanoparticles (UCNPs) has typically been realized using hexagonal (β) phase lanthanide-doped sodium yttrium fluoride (NaYF4) materials, the upconversion luminescence (UCL) of which saturates at power densities (P) of several hundred W cm−2 under 980 nm nearinfrared (NIR) excitation. Cubic (α) phase UCNPs have been mostly neglected because of their commonly observed lower UCL efficiency at comparable P in ensemble level studies. Here, we describe a set of sub-15 nm ytterbium-enriched α-NaYbF4:Er3+@CaF2 core/shell UCNPs doped with varying Er3+ concentrations (5–25%), studied over a wide P range of ∼8–105 W cm−2, which emit intense UCL even at a low P of 10 W cm−2 and also saturate at relatively low P. The highest upconversion quantum yield (ΦUC) and the highest particle brightness were obtained for an Er3+ dopant concentration of 12%, reaching the highest ΦUC of 0.77% at a saturation power density (Psat) of 110 W cm−2. These 12%Er3+-doped core/shell UCNPs were also the brightest UCNPs among this series under microscopic conditions at high P of ∼102–105 W cm−2 as demonstrated by imaging studies at the single particle level. Our results underline the potential applicability of the described sub-15 nm cubic-phase core/shell UCNPs for ensemble- and single particle-
level bioimaging.
Obtaining high quality upconverting nanocrystals with only little crystal defects and hence, a high luminescence, affords a reliable synthesis route. Only this guarantees the reproducibility of the material and its spectroscopic properties required for future application. The fluorolytic sol-gel synthesis appears to be a convenient attempt, as this is a method with only few steps influencing the material properties, which can be well controlled.
Also creating bright upconverting nanocrystals requires a profound understanding of the interplay of photophysical processes like multiphoton absorption, radiative and non-radiative pathways, and energy transfer in the material.
Based on steady-state and time resolved luminescence measurements at different excitation power densities, the influence of the lanthanide doping ratio and synthesis parameters such as the annealing process on SrF2-nanocrystals obtained via the fluorolytic sol-gel synthesis was systematically studied.