The composition of concrete determines its resistance to various degradation mechanisms such as ingress of ions, carbonation or reinforcement corrosion. Knowledge of the composition of the hardened concrete is therefore helpful to assess the remaining service life of an existing structure or evaluate the damage observed during inspections. For example, for most existing concrete structures the type of cement originally used is not known and must therefore be determined afterwards. This paper presents a preliminary study on the application of laser-induced breakdown spectroscopy (LIBS) to identify the type of cement. For this purpose, ten different types of cement were investigated. For every type, three cement paste prisms were produced: (i) prisms dried, ground and pressed into tablets, (ii) prisms dried and (iii) prisms untreated. LIBS measurements were performed with a diode-pumped low energy laser (1064 nm, 3 mJ, 1.5 ns, 100 Hz) in combination with two compact spectrometers which cover the UV and NIR spectral range. A reduced subset of spectral features was used to build a classification model based on linear discriminant analysis. The results show that the classification of homogenized pressed cement powder samples provides a high accuracy, however, factors such as a different sample matrix and moisture content can affect the accuracy of the classification. The study demonstrates that LIBS is a promising tool to identify the type of cement.
The determination of chloride is still one of the main tasks for the evaluation of reinforced concrete structures.
The corrosion of the reinforcement induced by the penetrating chlorides is the dominant damage process affecting the lifetime of concrete structures. In the recent years different research groups demonstrated that LIBS can be a fast and reliable method to quantify chlorine in cement-bound materials. Because chlorine in concrete can only occur as solved ions in the pore solution or bound in salts or hydrated cement phases, the detected emission of chlorine can be correlated with the chloride concentration determined e.g. with potentiometric titration. This work inter alia describes the production of reference samples and possible side effects during the production process. Due to transport processes in the porous matrix of the cement a misinterpretation of the concentrations is possible. It is shown how to overcome these effects and higher precisions of the single measurements can be realised. Using the calibration method, blank sample method and noise method, three different ways of calculating the limit of detection (LOD) and limit of quantification (LOQ) are compared. Due to the preparation of the reference samples a precision of the whole calibration model of sx0 = 0.023 wt% is determined.
The validation of the model is based on different test sets, which are varying in their composition
(different Cl-salts, water-to-cement ratios and additives). The determined mean error of the validation is
0.595 ± 0.063 wt%, which is comparable to standardised methods like potentiometric titration, direct potentiometry
or photometry (0.40 ± 0.06 wt%) [1].
This paper will address the relevance of chloride measurements in practice for durability condition assessment and a description of the working principle of LIBS will be given. Examples of chloride profiles obtained by the common wet chemical analysis will be shown and compared with results from LIBS measurements as to demonstrate the accuracy of the LIBS-technique. The latter will be supported by clear graphs. In addition examples on the extra information resulting from measurements performed with LIBS for improvement of condition assessment and prediction will be shown.
The presented work discusses the accuracy of Laser Induced Breakdown Spectroscopy (LIBS) in determining the total chloride content in cement pastes. LIBS as an emission spectroscopy method is used to detect simultaneously several elements present in cement-based materials. By scanning surfaces the variability in the spatial distribution of elements can be visualised. However, for a quantification of the results, studies are necessary to characterise possible influences due to the wide variation of the chemical compositions in which cement can occur. It is shown how the calibration can be done, how the calibration samples were produced, and which statistical parameters are necessary to describe the precision of the regression. The performance of LIBS is estimated by detecting chloride in validation samples. Therefore, 55 samples and 7 ets with changing mix ompositions were produced. The presented study deals with possible influences of different mix compositions, ncluding different cations of chloride, varying w/c-ratios and the artial replacement of Portland cement with last furnace slag (50% BFS) and limestone (30% LS). Comparing the LIBS results with otentiometric titration, n accuracy of±0.05 wt%/total has been determined.
A big part of the infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. In addition, the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from deicing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through
formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulphates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2 , SO4 2-and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a drill core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.