Sol–gel technology was applied in tailoring
novel wood-made-inorganic composites with improved
thermal and fire properties. In practice, composites materials
were prepared by impregnating pine sapwood wood with
nano-scaled precursor solutions derived from titanium(IV)
isopropoxide followed by a thermal curing process. Thermal
and fire properties were evaluated by thermal analysis and
cone calorimetry, whereas flammability was specified by
oxygen index (LOI) and UL 94 test. Peak heat release rates
were moderately reduced indicating fire retardance potential
in terms of flame spread attributed to the appropriate protection
layer action of the titania-based depositions. LOI
(oxygen index) values of these composites were increased up
to 38 vol.% in comparison to 23 vol.% for untreated wood.
The flame retardancy performance depends on the fire scenario
and is strongly influenced by wood loading and crackfree
deposition of the titania layers inside the composite.
Fire retardancy effects in single and double layered sol-gel derived TiO2 and SiO2-wood composites
(2012)
Sol–gel derived TiO2 and SiO2-wood inorganic composites are prepared by direct vacuum infiltration of silicon and titanium alkoxide based precursors in pine sapwood in one or two cycles followed by a controlled thermal curing process. The resulting flame retardancy effect is investigated under two different fire scenarios using cone calorimetry and oxygen index (LOI). Heat release rates (HRR) especially the values for the second peak, are reduced moderately for all single layered composites. This effect is more pronounced for double layered composites where HRR was reduced up to 40 % showing flame retardancy potential in developing fires. Beside this, smoke release was lowered up to 72 % indicating that these systems had less fire hazards compared to untreated wood, whereas no meaningful improvement is realized in terms of fire load (total heat evolved) and initial HRR increase. However impressively, the LOI of the composites were increased up to 41 vol% in comparison to 23 vol% for untreated wood displaying a remarkable flame retardancy against reaction to a small flame. An approximate linear interdependence among the fire properties and the material loading as well as fire residue was observed. A residual protection layer mechanism is proposed improving the residue properties for the investigated composites.