Filtern
Erscheinungsjahr
- 2016 (4) (entfernen)
Dokumenttyp
- Vortrag (4) (entfernen)
Sprache
- Englisch (4)
Referierte Publikation
- nein (4)
Schlagworte
- Arc melting technique (1)
- Component Test (1)
- Constitution diagram (1)
- Degradation (1)
- Dissimilar weld joints (1)
- Heat treatment condition (1)
- High manganese steel (1)
- High strength steels (1)
- High-strength Steel (1)
- Hydrogen trapping (1)
- I-girder (1)
- Numerical simulation (1)
- Residual Stress (1)
- Sectioning method (1)
- Thermal desorption analysis (TDA) (1)
- Weld heat input (1)
- Weld residual stresses (1)
- Welding (1)
Eingeladener Vortrag
- nein (4)
Adaption of Heat Control Concepts for Welding Stress Optimization in High-strength Steel Components
(2016)
High-strength structural steels from 690 MPa are increasingly applied at present. Major reasons are lightweight design trends and potential cost reductions. The structural design of welds and their manufacturing become more challenging with increasing material strength. By reasons of a higher yield ratio of these steels, the development of high residual stresses has to be avoided, since they are detrimental to the components safety and performance. Local restraint stresses and welding loads due to external shrinkage restraints occur. Frequently, this leads to critical tensile residual stresses in the weld and HAZ. In this study, influences of welding process parameters and restraint conditions on the residual stress state in welded components of high-strength steels were investigated. Multilayer GMAW tests under free shrinkage and experiments under well-defined restraints in special in-house developed testing facilities were accomplished. The tests permitted analyses of the resulting local residual stresses measured by means of X-ray diffraction and global reaction stress build-up while welding and cooling. Significant effects were found for heat control, seam configuration and restraint condition. Besides high restraints, elevated preheating and interpass temperatures lead to increased welding stresses. An adaption of welding parameters considering heat control, weld run sequence and seam configuration proved to be beneficial.
Currently, residual stresses in welded HSLA (high strength low alloyed steels) are considerded by simplified “robust” procedures fixed in common standards (such as Eurocode 3). The models are mostly based on specimens from mild steel with lower strength. For HSLA, necessary material data is less available for realistic assessment of the appearing residual stresses in typical I-girders. Hence, the economic benefit of HSLA steels in scope of load bearing capacity cannot fully be exploit. Thus, the scope of this work is the measurement of weld residual stresses in component-like I-girders S355 and S690 by sectioning method and subsequent verification by global structural welding simulation.
Hydrogen can cause unexpected material failure under consideration of stresses (external/internal) during manufacturing, processing or service of the materials. This failure is mostly based on a certain degradation of the mechanical properties. Thus, the correlation of hydrogen trapping vs. a respective microstructure is necessary for high strength steels. Thus, the scope of this work is the improvement of existing hydrogen trap models by verification of activation energies for hydrogen traps as well as the influence of the determination method. In this scope, the thermal desorption method is appropriate to distinguish between different hydrogen traps. Nevertheless, the specimen temperature has to be accounted very carefully in case of calculating the necessary trap energy.
Experimental simulation of dissimilar weld metal in high manganese steels by arc metling technique
(2016)
High manganese steels have great potential for use in automotive lightweight constructions (like car body structures) due to their superior strength and formability. In this scope, welding is the most common joining technique for sheet metal with challenges especially of dissimilar weld joints. In this case, the formation of martensite has to be considered resulting in a certain propability of brittle fracture in a respective load condition. In addition, no reliable weld metal microstructure prediction is possible with currently available constitution diagrams like the Schaeffler or WRC1992-diagram. Thus, the arc melting technique offers the possibility to investigate the effects of dilution on microstructures and properties of weld metal of high manganese steels. The results suggested that a complex indentification of microstructures is possible by directed experiments using the arc metling technique