Carrier gas hot extraction (CGHE) technique was used for measurement of hydrogen in press-hardened (and as delivered) condition of 22MnB5 steel primarily coated with a thin layer of Al–Si. The CGHE technique was applied using different temperature programs: isothermal heating, temperature step, and linear heating in solid state. The effusing hydrogen was measured using thermal conductivity device (TCD) and high resolution mass spectroscopy (MS). Single isothermal heating at 400 and 900 °C allowed determining absolute value of effusing hydrogen. The linear heating, also known as thermal desorption analysis (TDA), revealed temperature dependent hydrogen effusion peaks. The deconvolution of the TDA spectra by peak fitting allowed the calculation of hydrogen desorption energies for each peak. The results showed good agreement between hydrogen concentrations measured with MS and TCD. In addition, the as-received ferrite-perlite microstructure showed only hydrogen effusion above 400 °C. The subsequent press hardening process leads to hydrogen uptake in the microstructure. In general, the press-hardened 22MnB5 revealed a hydrogen concentration of 0.4 to 0.5 ppm. The biggest concentration was released at isothermal holding at 400 °C indicating reversibly trapped hydrogen. TDA results with different heating rates confirmed mostly diffusible and reversible trapped hydrogen due to calculated activation energies in the range from 4 to 20 kJ mol-1; it was ascertained that nearly 90 % of the hydrogen left the specimens below 400 °C. Melt extraction (ME) was performed to measure the total hydrogen amount (including the diffusible and trapped hydrogen) and showed that above 900 °C up to 1 ppm hydrogen is trapped.
Hydrogen can cause unexpected material failure under consideration of stresses (external/internal) during manufacturing, processing or service of the materials. This failure is mostly based on a certain degradation of the mechanical properties. Thus, the correlation of hydrogen trapping vs. a respective microstructure is necessary for high strength steels. Thus, the scope of this work is the improvement of existing hydrogen trap models by verification of activation energies for hydrogen traps as well as the influence of the determination method. In this scope, the thermal desorption method is appropriate to distinguish between different hydrogen traps. Nevertheless, the specimen temperature has to be accounted very carefully in case of calculating the necessary trap energy.