Filtern
Erscheinungsjahr
- 2015 (36) (entfernen)
Dokumenttyp
Sprache
- Englisch (28)
- Deutsch (7)
- Mehrsprachig (1)
Schlagworte
- Laser beam welding (7)
- Solidification cracking (5)
- Hot cracking test (4)
- High power laser beam welding (3)
- Hot cracking (3)
- Keyhole (3)
- Local reduced pressure (3)
- Mobile vacuum (3)
- Duplex stainless steel (2)
- Electromagnetic weld pool support (2)
Eingeladener Vortrag
- nein (4)
Selective Laser Melting (SLM) and Laser Metal Deposition (LMD) are prominent methods in the field of additive manufacturing technology. While the powder-bed based SLM allows the manufacturing of complex structures, buildrate and part volumes are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, however shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates.
In this paper, a process chain consisting of additive technologies SLM and LMD is described. The experiments are conducted using the alloys Ti-6Al-4V and Inconel 718. A cylindrical test specimen is produced and the microstructure along the SLM-LMD zone is described. In addition, this process chain was tested in the manufacturing of a turbine blade. The feasibility of implementing this process chain for small batch production is discussed. The results are evaluated to show advantages and limitations of the SLM-LMD process chain. This paper is relevant for industrial or scientific users of additive manufacturing technologies, who are interested in the feasibility of a SLM-LMD process chain and its potential for increased deposition rates.
Build-up strategies for generating components of cylindrical shape with laser metal deposition
(2015)
Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process.
Der Beitrag stellt am Beispiel eines für adaptive MSG-Lichtbogen-Engspaltschweißungen im Dickblech-Bereich entwickelten Versuchsstandes ein Automatisierungskonzept für vernetzte kommerziell verfügbare Anlagenkomponenten über ein zentrales echtzeitfähiges Steuersystem auf Basis des EtherCAT-Protokolls vor. Der Fokus liegt hierbei auf der Eignung für Aufgaben im Bereich der Qualitätssicherung sowie Forschung und Entwicklung leistungsfähiger Algorithmen zur Prozessüberwachung und -regelung. Die sich daraus ergebende Vielzahl zu messender und steuernder Parameter stellen vor allem in Verbindung mit präzisen und hochfrequenten Messgeräten höchste Anforderungen an die Datenverarbeitung sowohl in Echtzeit als auch zur Auswertung nach dem Prozess. Die Einbindung etablierter Programmiertools wie MATLAB/Simulink in gängigen Automatisierungsstandards ermöglichen flexible und innovative Forschungsarbeit.
Durch die automatisierte Datenerfassung in einer übergelagerten Datenbank stehen die Messungen sämtlicher Schweißvorgänge jederzeit zur Entwicklung neuer Abläufe zur Prozessteuerung und -regelung oder zur Verbesserung der bestehenden Algorithmen zur Verfügung, was insbesondere den sukzessiven Aufbau komplexer Regressionsmodelle aus der Anwendung heraus ermöglicht.
Als Applikationsbeispiel wird die Entwicklung eines dynamischen Lichtbogensensors vorgestellt und diskutiert. Die Versuchsdurchführung mit dem Ziel der Ableitung nichtlinearer Regressionsmodelle erfolgt automatisiert mithilfe eines optischen Sensors. Der Vorteil dieses Verfahrens liegt dabei neben der schnellen Umsetzbarkeit in der direkten Korrelation der Messwerte zu realen physikalischen Systemgrößen und der schnellen Adaption auf unterschiedliche Schweißparameter und -prozesse.
Test procedure to characterize the cracking susceptibility of RSW-steels has been developed
During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior
With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel
Complex phase steels behavior during test procedure:
Crack length growth with increasing force could not be determined
The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case)
30
Der Fokus des vorliegenden Beitrages liegt in der Anwendung der numerischen Schweißsimulation zur Berechnung des schweißbedingten Verzugs an industriellen Bauteilen. Anhand einiger Applikationsbeispiele werden die Möglichkeiten und Einschränkungen am Markt verfügbarer Softwareprodukte aufgezeigt. Hierbei liegt die Gewichtung in einer qualitativ korrekten Abbildung der zu analysierenden Phänomene. Diese stellt die Basis für nachfolgende Parameterstudien dar, welche signifikante Einflussgrößen auf die Verzugsausbildung detektieren. Der Vorteil derartiger simulationsgestützter Analysemethoden gegenüber rein experimentellen Ansätzen wird diskutiert. Aufgrund der heutigen Verfügbarkeit spezialisierter anwenderfreundlicher Schweißsimulationssoftware und günstiger Rechenressourcen macht die Industrie in den letzten Jahren immer mehr von den zahlreichen Vorteilen einer virtuellen Prozessauslegung mit Hilfe der Schweißsimulation Gebrauch. Komplexe Praxisanwendungen können heutzutage innerhalb von 1-2 Wochen unter Berücksichtigung aller Arbeitsschritte bearbeitet werden. Die Anforderungen an den Anwender seitens der Numerik und Materialmodellierung hat sich drastisch verringert, wohingegen ein gewisses Maß an Wissen und Erfahrung vom simulierten Prozess weiterhin entscheidend für den Erfolg der Simulation ist. Am Beispiel des Einspritzventils konnte das Potential einer virtuellen Prozessauslegung anschaulich aufgezeigt werden.
Life Cycle Assessment (LCA) and Social Life Cycle Assessment (SLCA) are applied in evaluating possible social and environmental impacts of the state-of-art welding technologies, such as Manual Metal Arc Welding (MMAW), Manual Gas Metal Arc Welding (GMAW), Automatic GMAW and Automatic Laser-Arc Hybrid Welding (LAHW). The LCA results indicate that for 1 meter weld seam, MMAW consumes the largest amount of resources (like filler material and coating on electrodes) and energy, which contributes to comparatively higher environmental impacts in global warming potential, acidification, photochemical ozone creation potential and eutrophication than other chosen processes. With regard to social aspects, the health issues and fair salary are under survey to compare the relative potential risk on human health caused by fumes in different welding technologies, and to indicate the sufficiency of current salary of welders in Germany. The results reflect that the wage status of welders is still fair and sufficient. The manual processes bring much higher potential risk of welders health than the automatic processes, especially MMAW.
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test
The strain rate has a significant influence on the formation of the hot crack
It was possible to determine the critical strain and strain rate that led to shot crack formation
A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed.
Good agreement between the strain field measured using the DIC technique and the simulation results
Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Experimental study and numerical simulation of hot crack formation for novel laser weldability test.
(2015)
Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials.
An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an AC magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles-Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel surrounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modelled with a 3D turbulent steady-state model including heat transfer and fluid dynamics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagneticinduced pressure. The FE software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 mT and 90 mT. The corresponding oscillation frequencies were between 1 kHz and 10 kHz and the electromagnetic AC powers were between 1 kW and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 kW and 2.4 kW at oscillation frequencies between 1.2 kHz and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass fullpenetration laser beam welding of 15 mm and 20 mm thick AISI 2205.