Filtern
Erscheinungsjahr
- 2015 (25) (entfernen)
Dokumenttyp
Sprache
- Englisch (17)
- Deutsch (7)
- Mehrsprachig (1)
Referierte Publikation
- nein (25) (entfernen)
Schlagworte
- Laser beam welding (7)
- Solidification cracking (4)
- High power laser beam welding (3)
- Hot cracking (3)
- Hot cracking test (3)
- Keyhole (3)
- Local reduced pressure (3)
- Mobile vacuum (3)
- Duplex stainless steel (2)
- Electromagnetic weld pool support (2)
Eingeladener Vortrag
- nein (4)
Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding
The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied.
Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool.
Build-up strategies for generating components of cylindrical shape with laser metal deposition
(2015)
Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process.
Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120
(2015)
Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120
Hybrid laser arc welding of the root pass:
Significant reduction in the weld cross section – savings of filler material
Lower heat input into the base material - improvement of mechanical properties of the weld joint
The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld
14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit
Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials:
Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test
The strain rate has a significant influence on the formation of the hot crack
It was possible to determine the critical strain and strain rate that led to shot crack formation
A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed.
Good agreement between the strain field measured using the DIC technique and the simulation results
Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties
Test procedure to characterize the cracking susceptibility of RSW-steels has been developed
During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior
With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel
Complex phase steels behavior during test procedure:
Crack length growth with increasing force could not be determined
The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case)
30
Laser remote welding is a dynamic and flexible joining technology which enables various new approaches in welding sequence and weld position planning. However, the challenge is to find the optimal set-up within this large parameter space. In this article, numerical welding simulation is used to deal with this challenge. For a car door, different welding sequences and weld positions were numerically analyzed and compared with respect to its welding distortion behavior.
Welding is one of the most critical operations for the construction of reliable metal structures in everything from ships to reactor vessels. When welds fail, the entire structure often fails—so expectations on weld quality have never been higher. Any process that uses a localized heat source, such as welding, is likely to result in some distortion. The welding process of very thick metal components is not inherently stable and is barely controllable without external forces.