Grain refinement is an important possibility to enhance the weldability of aluminium weld metal that is usually defined by its susceptibility to solidification cracking. In this study, grain refinement was achieved through the addition of commercial grain refiner containing titanium and boron to the GTA weld metal of aluminium alloy 6082. The weld metal mean grain size could be reduced significantly from about 70 µm to a saturated size of 21 µm with a change in grain shape from columnar to equiaxed. The grain refinement prevented the formation of centreline solidification cracking that was present only in welds with unrefined grain structure. A variation of torch speed led to a strong change of solidification parameters such as cooling rate that was measured in the weld metal and the corresponding solidification rate and thermal gradient. The ratio thermal gradient/growth rate (G/R) decreased from 50 K s/mm² (high torch speed) to 10 K s/mm² (low torch speed). However, the variation of torch speed did not change the tendency for solidification cracking. The microstructure of unrefined and completely refined weld metal was compared. The observed change in size and distribution of the interdendritic phases was related to the change in susceptibility to solidification cracking.
Laser GMA hybrid welds, producing partial penetration, were conducted on stiff tubes made of S460NH. Experiments, using a design-of-experiments plan were conducted to examine the influence of the welding parameters on the occurrence of solidification cracks. Results say that cracks diminish, when high levels of arc power are applied, while their number increases with rising laser beam power. The weld velocity had no measurable impact.
Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding
The safety of components or constructions is of great importance in the manufacturing and processing of metallic materials. Solidification cracking as well as the weldability of materials remain still for many years a highly contentious issues, particularly with regard to the causes of the hot crack formation. Many of studies have been conducted to determine the critical condition of occurrence of the solidification cracking. In this study different digital image correlation measuring techniques in conjunction with laser diodes as the illuminating source have been employed to measure the arising strain field during the laser welding process at the surface of the workpiece directed to the laser beam in the close vicinity of the weld pool. The Controlled Tensile Weldability test (CTW) was used to apply an external tensile load during the laser beam welding in order to generate the solidification cracks. The results showed that by means of those techniques it is possible to measure the strain field without any disturbances from the intense welding light or the smoke. Additionally, the strain and the strain rate as a critical factor determining solidification crack formation can be measured and analyzed.
Experimental study and numerical simulation of hot crack formation for novel laser weldability test.
(2015)
Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials.
Solidification cracking phenomena taking place under controlled tensile weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a threedimensional finite element model employing the contact element technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure, the resulting strain and displacement directed to the laser beam in the close vicinity of the weld pool was measured at the surface of the workpiece using a digital image correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good agreement with those observed in experiments.
Using the novel optical measurement technique together with the optical flow algorithm, a twodimensional deformation analysis during welding has been conducted. This technique provides for the first time a measurement of the strain field locally in the immediate vicinity of the assumed solidification front. The described procedure of the opticalmeasurement allows to determine the real martial-dependent values of critical strain and strain rate characterising transition to the hot cracking during laser welding processes. The local critical strain that obtained in the assumed solidification showed that the local critical strain decreases as the strain rate increases. Moreover, this phenomenon has also been shown with results from the CTW-test, since the global strain decreases with an increase in the external strain rate.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking as well as the weldability of materials is still since many years a highly contentious issue, particularly regarding the causes of the hot crack formation. Many of studies have been conducted to determine the critical conditions of occurrence of the solidification cracking. In this study a 2D in-situ observation technique in conjunction with laser diodes as the illuminating source has been employed to measure the arising strain field during the laser beam welding process. For the first time the employed technique enabled the in-situ measurement of the transient strain field at the surface of the workpiece directed to the laser beam in the critical range, where the solidification cracking normally occurs. Thus the critical threshold strain values at high temperatures characterizing transition from crack free to crack concomitant welding process could be deduced.