Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase in the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are ana lyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verify the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains, that have been solidified and formed previously, from further growth and generates some small cel lular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement.
In diesem Beitrag werden Ergebnisse der Untersuchungen eines Verfahrens zum fehlerfreien Laserstrahl-Hybridschweißen von geschlossenen Rundnähten vorgestellt. Das Verfahren zielt auf die Vermeidung von Schweißimperfektionen im Überlappbereich einer laserstrahlhybridgeschweißten Rundnaht. Eine Strategie der Prozessführung beim Schließen der Rundnaht wurde entwickelt, mit der ein fehlerfreier Überlappbereich durch die Kontrolle der Erstarrungsbedingungen am Schweißnahtende erreicht wird. Die kontrollierte Wärmeführung wird durch eine Anpassung der Parameter von beiden beteiligten Schweißprozessen, dem Laserstrahl- sowie MSG-Schweißprozess realisiert. Experimentelle Untersuchungen wurden an 12 mm bis 15 mm dicken Rohrabschnitten durchgeführt. Der Einfluss von Prozessparametern wie der Laserleistungsrampe und Rampenzeit, der Veränderung des Abbildungsmaßstabes und der Defokussierung des Laserstrahls auf die Erstarrungsbedingungen am Ende der Rundnaht wurde untersucht, um eine optimale Strategie zum Herausführen der Prozessenergie zu finden. Im Rahmen der experimentellen Untersuchungen konnte gezeigt werden, dass eine Defokussierung des Laserstrahls im Bereich zwischen 60 mm und 100 mm über einen kurzen Auslaufbereich der Naht von ca. 15 mm zu einer deutlich besseren Nahtausbildung im Überlappbereich führte. Es konnte eine günstige kelchförmige Schweißnahtform ohne eine Tendenz zur Rissbildung erzielt werden. Die Laseroptik mit motorisch angesteuertem Linsensystem ermöglichte dabei eine Vergrößerung des Laserstrahldurchmessers ohne eine Veränderung der Position des MSG-Lichtbogens relativ zur Bauteiloberfläche.
Notch impact toughness of laser beam welded thick sheets of cryogenic nickel alloyed steel X8Ni9
(2020)
This research work deals with the investigations of the impact toughness of laser beam welded 14.5 mm thick sheets made of cryogenic steel X8Ni9 as a function of preheating. This 9% nickel alloyed steel is widely used in the liquefied natural gas (LNG) industry. An application of highly efficient welding processes such as high-power laser beam welding (LBW) in LNG sector requires an understanding of the interactions between the LBW process parameters and weld properties, in particular the impact toughness. The results show that the original fine-grained martensitic microstructure of the base metal (BM) is significantly changed by melting and crystallization during the LBW, what can lead to a decrease in the impact toughness of the weld metal (WM) below the required level. An optimal preheating temperature range leads to the favorable thermal welding cycle and is of remarkable importance for maintaining the notch impact toughness of laser beam welded joints of these thick steel sheets. A parameter window was identified in which V-notch impact toughness comparable to that of the BM at -196 °C was achieved.
The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high-speed camera, and two thermal imaging cameras is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs above 10 mm penetration depth. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root.
Schweißen mit dem Faserlaser
(2007)
Schweißen mit dem Faserlaser
(2007)
-With modern high-power lasers (and vacuum) penetration around 100 mm is possible
-Important for industrial applications: single-pass full penetration welds with tolerances
-Contactless EM-backing helps to overcome many main restrictions:
-Single-pass HLAW of up to 30 mm can be realized with 20 kW laser power
-Increase of the gap bridgeability and misalignement of edges
-Lower sensitivity to manufacturing tolerances and edge quality; samples can be prepared by a plasma-cut instead of time-consuming milling process
-Gives the possibility to increase the welding parameter window and cooling rate so that the required mechanical properties can be reached
-Improved filler wire mixing behaviour
The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high speed camera, and two thermal imaging cameras is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs above 10 mm penetration depth. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root
One of the challenges of the high-power hybrid laser welding of thick steels is the sensitivity of the process of the process to manufacturing tolerances. This usually leads to a time-consuming preparation of the welding edges, such as milling. The study deals with the influence of the edge quality of milled and plasma-cut steel made of S355J2 with a wall thickness of 20 mm on the laser hybrid welded seam quality. Furthermore, the gap bridgeability and the tolerances towards edge misalignment was investigated. An AC magnet was used as backing support to prevent sagging and positioned under the workpiece, to generate an upwards directed electromagnetic pressure. The profiles of the edges and the gap on the top and root side were measured using a digital camera. Single-pass laser hybrid welds of plasma-cut edges could be welded using a laser beam power of just 13.7 kW. A gap bridgeability up to 2 mm and misalignment of edges up to 2 mm could be achieved successful. Additionally, the independence of the cutting side and the welding side was shown, so that samples were welded to the opposite side to their cutting. For evaluation of internal defects or irregularities, X-ray images were carried out. Charpy impact strength tests were performed to determine the toughness of the welds.
Schweißspannungen bei Bauteilschweißversuchen unter besonderer Berücksichtigung des Einspanngrades
(2011)
Mechanische Eigenschaften der laserhybridgeschweißten Schweißverbindungen von hochfesten niedriglegierten Stählen erfüllen die Anforderungen der geltenden Normen
Eindringtiefe des Zusatzwerkstoff bis ca. 12 mm
Halborbitales Schweißen an 36” Rohren mit einer Wandstärke von 16 mm bei einer Schweißgeschwindigkeit von bis zu 2,2 m/min und Laserleistung von 19 kW technisch möglich
Rissfreie Schweißverbindungen an Präzisionsrohren können durch eine geeignete Schweißparameterauswahl mittels Laser-Hybridverfahren hergestellt werden
•Main Welding Technologies in the Automotive: RSW and laserbeam welding
•Light Weight Design leads to increasing use of AHSS and UHSS which results in higher demands for the joining technology
•Joining Multi-Material Structures offers opportunities for “new” Thermal-Mechanical Joining Processes and Hybrid Processes
•In the coming years a trend towards sustainable manufacturing can be seen. Comparison between laserbeam and RSW will be a tight match!
High power laser welding technology has made a large progress in the last decade and established itself in different industrial applications;
Hybrid laser arc welding is one of the most prospective technologies for heavy components assembling;
Modern high speed video observation, in situ x-ray screening as well as simulation techniques contributed to better understanding of laser welding process;
New approaches e.g. application of electromagnetic fields for melt pool control and welding at reduced pressure ambient have significantly contributed to extending the process boundaries far beyond the known Limits.
Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120
(2015)
Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120
Hybrid laser arc welding of the root pass:
Significant reduction in the weld cross section – savings of filler material
Lower heat input into the base material - improvement of mechanical properties of the weld joint
The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld
14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit
Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials:
Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes
The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested
Surface cracks havenoinfluenceon thefatiguelife
Samples with cracks in the electrode indentation /HAZ where tested
Stiffness curves are not significantly influenced by surface cracks
3D FE-Simulation demonstrate no changes of stress due to surface imperfections
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test
The strain rate has a significant influence on the formation of the hot crack
It was possible to determine the critical strain and strain rate that led to shot crack formation
A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed.
Good agreement between the strain field measured using the DIC technique and the simulation results
Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties
Test procedure to characterize the cracking susceptibility of RSW-steels has been developed
During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior
With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel
Complex phase steels behavior during test procedure:
Crack length growth with increasing force could not be determined
The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case)
30
The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested
Surface cracks have no influence on the fatigue life
Samples with cracks in the electrode indentation /HAZ where tested
Stiffness curves are not significantly influenced by surface cracks
3D FE-Simulation demonstrate no changes of stress due to surface imperfections
•
Welding under external forces was found suitable for characterizing AHSS materials
New quick and easy-to-perform procedure for establishing a material ranking regarding cracking susceptibility
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
1. Steel Production and Processing in Europe
2. Design Trends in the Automotive Industry
3. Welding Technologies in the Automotive Industry
4. Problems while Processing AHSS/UHSS
5. Challenges in Joining Multi-Material Structures
6. Mechanical Joining Technologies
7. Thermal-Mechanical Joining Processes
8. Energy Efficiency of Welding Processes
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Single-pass Hybrid Laser Arc Welding of Thick Materials Using Electromagnetic Weld Pool Support
(2019)
Hybrid laser-arc welding process allows single-pass welding of thick materials, provides good quality formation of joints with minimal thermal deformations and a high productivity in comparison with arc-based welding processes. Nevertheless, thick-walled steels with a thickness of 20 mm or more are still multi-pass welded using arc welding processes, due to increased process instability by increasing laser power. One limitation factor is the inadmissible formation of gravity drop-outs at the root. To prevent this, an innovative concept of electromagnetic weld pool support is used in this study. With help of such system a stable welding process can be established for 25 mm thick steel plates and beyond. Sound welds could be obtained which are tolerant to gaps and misalignment of the welded parts. The adaptation of this system to laser and hybrid laser-arc welding process can dramatically increase the potential field of application of these technologies for real industrial implementation.
The present work deals with the development of a strategy for the prevention of end crater defects in high-power laser welding of thick-walled circumferential welds. A series of experiments were performed to understand the influence of the welding parameters on the formation of end crater defects such as pores, cracks, excessive root-side drop-through and shrinkage cavities in the overlap area. An abrupt switch-off of the laser power while closing the circumferential weld leads to a formation of a hole which passes through the whole welded material thickness. A laser power ramp causes solidification cracks which are initiated on the transition from full-penetration mode to partial penetration. Strategies with a reduction of the welding speed shows a creation of inadmissible root sagging. Defocusing the laser beam led to promising results in terms of avoiding end crater defects. Cracks and pores in the overlap area could be effectively avoided by using defocusing techniques. A strategy for avoiding of end crater imperfections was tested on flat specimens of steel grade S355J2 with a wall thickness of 10 mm and then transferred on the 9.5 mm thick pipe sections made of high-strength steel X100Q.
The presented study deals with the performing and mechanical testing of single pass hybrid laser-arc welds (HLAW) on 25 mm thick plates made of steel grade S355J2. One of the challenges have to be solved at full penetration HLAW of thick plates is the drop formation occurring due to the disbalances of the forces acting in the keyhole and on the melt pool surface. Such irregularities mostly limit the use of high-power laser beam welding or HLAW of thick-walled constructions. To overcome this problem, an innovative concept of melt pool support based on generating Lorentz forces in the weld pool is used in this work. This method allows to perform high quality welds without sagging even for welding of 25 mm thick plates in flat position at a welding speed of 0.9 m min-1. For the obtain of full penetrated welds a laser beam power of 19 kW was needed. A high V-impact energy of up to 160 J could be achieved at the test temperature of 0 °C. Even at the most critical part in the weld root an impact energy of 60 J in average could be reached. The tensile strength of the weld reaches that of the base material. An introduce of the HLAW process with electromagnetic support of the melt pool in the industrial practice is an efficient alternative to the time- and cost-intensive arc-based multi-layer welding techniques which are established nowadays for joining of thick-walled constructions.
Schwerpunkte:
Strategie zur Vermeidung von Schweißimperfektionen im Überlappbereich beilaserhybridgeschweißten Rundnähten für 9.5 mm dicke Rohre.
Anpassung der Laserleistung in Kombination mit der Defokussierung des
Laserstrahls sowie einer Endkraterfüllung am Ende der Schweißnaht führte zu einer besseren Nahtausbildung.
Herausrampung der Energie des Schweißprozesses, sodass ein Übergang von Durchschweißung zu einer Einschweißung mit gewünschter kelchförmiger Nahtgeometrie stattfand.
Einstellung eines Wärmestaus durch Defokussierung und Verschiebung des
Laserstrahls führt zu einem gut ausgebildeten Überlappbereich ohne Poren, Risse.
Schweißungen an Rohrabschnitten mit einer max. Wandstärke von 15 mm, bei gegebenenfalls weiteren Parameteranpassungen.
Digital vernetzte Sensorik für Erfassung von Prozessgrößen
- Datenbankstruktur zur Integration sämtlicher Messgrößen
- In-situ Korrelation zwischen Prozessparametern und
Schweißergebnis auf Basis künstlicher Intelligenz
- Sukzessiver Aufbau an Prozesswissen selbstlernendes
System
- Prozessregelung MSG-Engspaltschweißen
-Adaptiver Pendelwinkelkeine Vorgabe durch Anwender notwendig gleichmäßiger Flankeneinbrand
-Füllgradregelung Vorgabe einer Zielaufbauhöhe durch Anwender autarke Regelung der Prozessgrößenfür gleichmäßige Füllhöhe bei Variation der Spaltbreite
The laser hybrid welding process offers many advantages regarding deep penetration, increased welding velocity and with the help of the supplied filler wire an improved bridgeability to gap and misalignment tolerances. High power laser systems with a power of approx. 30 kW are already available on the market. Nevertheless, multi-layer technology with an arc process is still used for welding of plates from a thickness from 20 mm. A potential cause is the process instability with increasing laser power. It is inevitable that gravity drop-out due to the high hydrostatic pressure at increasing wall thickness especially at welding in flat position and with a low welding speed. The surface tension decreases with increasing root width resulting from low welding velocities. To prevent such inadmissible defects of the seam a use of weld pool support is required. Usual weld pool support systems such as ceramic or powder supports require a mechanical detachment which is time-consuming. The electromagnetic weld pool support system described in this work shows an alternative weld pool support which works contactless. It is based on generating Lorentz forces in the weld pool due to oscillating magnetic field and induced eddy currents. This innovative technology offers single pass welds up to 28 mm in flat position and reduced welding velocity with a laser power of just 19 kW. It also leads to improved mechanical-technological properties of the seams because of the slow cooling rate. With usage of an electromagnetic weld pool support the limitation of the hybrid laser arc welding process in the thick sheet metal will be extend.
Die Anwendung von Leichtbauprinzipien im Stahlbau, wie z.B. die Verwendung von aufgelösten Tragstrukturen, sog. Jackets-Fundamenten, bietet ein großes Potential zur Reduzierung des Ressourcenverbrauchs, insbesondere im Hinblick auf die benötigte Stahlmenge.
In diesem Vortrag zeigen wir die Potenziale einer vollständigen Digitalisierung der schweißtechnischen Fertigungs- und Prüfkette auf, um eine vollautomatische Fertigung sowie Qualitätsprüfung von Rohrknoten als Schlüsselelement von Jackets-Fundamenten zu ermöglichen. Darüber hinaus wird der Zusammenhang zwischen der Geometrie der Nahtform und der resultierenden Ermüdungsfestigkeit durch numerische Methoden unter Einbeziehung bionischer Prinzipien bewertet. Es wird gezeigt, dass Hohlprofilknoten vollautomatisch unter Berücksichtigung von Geometrietoleranzen geschweißt werden können. Darüber hinaus konnte die Nahtform gemäß den numerischen Modellen hergestellt werden, was ein großes Potenzial für eine verlängerte Lebensdauer bietet. Anschließend werden die Verbesserungen bei der Ressourceneffizienz und die Reduzierung der Kohlendioxidemissionen durch eine Lebenszyklusanalyse bewertet.
Innovative Design- und Fertigungsstrategien zur Steigerung der Leichtbaupotenziale im Stahlbau
(2022)
Ziel des Verbundvorhabens „SmartWeld“ ist es, für die schweißtechnische Fertigung von Stahlbaustrukturen exemplarisch am Beispiel von Hohlprofilknoten, welche als designrelevante Elemente von Gründungsstrukturen für Offshore-Windenergieanlagen (OWEA) einsetzbar sind, die Möglichkeiten des Leichtbaus unter konsequenter Digitalisierung der Fertigungskette aufzuzeigen, um einerseits die Ressourceneffizienz zu forcieren und gleichzeitig wettbewerbsfähige Fertigungsstrategien aufzuzeigen.
Innerhalb von „SmartWeld“ werden daher die Möglichkeiten einer wirtschaftlichen Fertigung von Leichtbau-Gründungsstrukturen am Beispiel aufgelöster Tragstrukturen (Jackets) aufgezeigt. Eine lastgerechte Auslegung der Schweißverbindungen nach bionischen Prinzipien ermöglicht, weitere Einsparpotenziale an Ressourcen bei gleichzeitiger Erhöhung der Lebensdauer zu erschließen.
Die Ausnutzung konstruktiver Prinzipien des Leichtbaus zur Erzeugung innovativer und ressourcenschonender Produkte erfordert den Einsatz digitaler Werkzeuge in der Designphase, der virtuellen Absicherung, der Fertigung und Qualitätsüberwachung sowie nachgelagerten Bauteilprüfung zur Abbildung der Nutzungsphase. Im Rahmen der Arbeiten wird daher der gesamte Produktentstehungs- und Prüfprozess betrachtet. Dies beinhaltet das Design im Kontext des konstruktiven Leichtbaus, den schweißtechnischen Fertigungsprozess, die Bauteilprüfung sowie den Transfer der Ergebnisse in die Industrie durch serientaugliche Demonstratoren. Der Fokus der Arbeiten ist, die Fertigung auch im Umfeld eines für großskalige Stahlstrukturen üblichen hohen Individualisierungsgrades schweißtechnisch zu automatisieren und das Leichtbaupotenzial gezielt umzusetzen. Die Vorgaben aus der Designphase hinsichtlich einer lastgerechten Gestaltung bzw. Implementierung bionischer Ansätze können so gezielt durch einen adaptiven, automatisierten Schweißprozess eingestellt werden. Dies führt zu einer Erhöhung der Ermüdungs¬festigkeit und damit Produktlebensdauer, wodurch die Strukturen dünnwandiger ausgeführt und Ressourcen sowie CO2 eingespart werden können.