It has been shown that tetraethoxysilane-derived precursors are suitable solutions for impregnating pine sapwood to improve its dimensional stability. Tailored sol–gel syntheses result in precursors with nano-scaled silica species which are able to penetrate into the cell walls of wood. The physical fixation of those species inside the cell walls was verified by ESEM/EDX investigations. There is evidence that the silica species are chemically bonded to wood components. Nonreacted alkoxy groups can exist in the wood composites after impregnation. The amount of these organic residues depends on the composition of the precursors, especially their condensation degree and reactivity. Treatments for finishing the composites after the impregnation step to get clean products and stable properties are discussed in this context. An explanation of the complex relationship between solids content in the impregnation solutions and percentage weight gain and bulking of the composites is given. It can be demonstrated that high WPG values (>20 %) are pre-conditions for an effective protection of the resulting composites but they only guarantee efficient improvements if connected with the incorporation of the inorganic component inside the cell walls. Therefore, the sol–gel syntheses have to be carried out in such a manner that very small (<2 nm) as well as reactive species are sufficiently available. This demands syntheses using sub-stoichiometric water contents (H2O/TEOS <4, better <2).
Mit der Erfindung des Glas-Guß-Walzverfahrens eröffnete sich die Möglichkeit, größere Spiegelflächen als zuvor herzustellen. Diese sogenannten Quecksilberspiegel sind mit Zinnamalgam beschichtet. Wenn Restauratoren mit Zinnamalgamspiegeln arbeiten, müssen sie strenge Sicherheitsvorkehrungen einhalten. Häufig finden sich im Spiegelrahmen Quecksilberkugeln, die beim Öffnen herausfallen und damit gesundheitsschädliches Quecksilber freisetzen können. In einem Forschungsprojekt wurden die Quecksilberemissionen aus Zinnamalgamspiegeln gemessen und Möglichkeiten entwickelt, diese zu verringern.
With the implementation of glass casting in France in the second half of the 17th century, larger mirrors could be produced. So-called tin-mercury mirrors were made by coating glass with tin amalgam. Today, many historical mirrors are partly damaged, the image quality is compromised, and the material integrity of the mirror is threatened. The transformation from tin into an oxide starts at the surface of the amalgam and proceeds down to the glass surface. The mercury dissolves as a liquid or gaseous phase. The amalgam layer is destroyed, so that conservation is necessary. Conservators must follow strict safety precautions while handling amalgam mirrors because of possible mercury emissions and corrosion of the amalgam, during which elemental mercury accumulates near the mirror frame in droplets and is emitted into the air.
In a research project, the quantity of the mercury emissions from historical mirrors was examined and a technique to decrease these emissions was developed.
The antileaching efficacy of sol-gel-derived TiO2- and SiO2-based precursors has been evaluated through laboratory leaching trials with pine sapwood in two different ways. In a one-step process, wood was vacuum impregnated by the precursor solutions containing CuCl2. The copper (Cu) emission rates of the sol-gel-based impregnated woods were up to 70% lower than that of wood treated with pure CuCl2 solution at the same level of concentration. More improvement (80%) could be achieved in a two-step process, in which sol-gel precursors were introduced into an already CuCl2-treated wood. The refinement was attributed to several effects. In the one-step approach, Cu was embedded in the TiO2/SiO2 gels formed in the wood texture. During a two-step impregnation, gel layers that were formed in the wooden interior acted as an effective diffusion barrier. The sol-gel impregnations made wood more hydrophobic; therefore, the low amount of water that penetrated the cell wall was less efficient to leach out Cu.
Today glass is broadly used in modern architecture. For indoor applications it is possible to produce decorated glass by using enamel colours and glass painting techniques without any problems. However, this is more limited for applications out of doors. Humidity and environmental pollution attack the surface of the coating and can damage it. There are only a few colours on the market which are resistant towards acids and bases until now. Additionally, most of those colours are opaque. To extend the colour palette, chemically resistant low melting coloured glasses are being developed which are transparent and intensively toned even in thin coating thicknesses. To achieve such an ambitious aim, many parameters have to combine and act in a complex manner. New compositions of lead borosilicate, zinc borosilicate and lead-zinc borosilicate glasses were produced and milled as powder. The thermal properties as well as the environmental stability were analysed. The influence of PbO and ZnO on the thermal properties and the environmental stability were investigated. Evaluation of the fusing results shows that the production and mixture of transparent vitreous enamels for the exterior side of glasses is possible. The tests made it clear that the original materials for making the vitreous enamels must be excellently ground and prepared to achieve a satisfactory result. The method to produce durable vitreous enamels for exterior application also seems to allow the production of glass colours.
Untersuchung historischer Goldmosaike Herstellungstechnologie und charakteristische Schadensbilder
(2009)
The solgel process was applied to enhance properties of pine sapwood. For this purpose wood prisms were soaked in nanoscaled precursor solutions prepared from titanium(IV) n-butoxide and titanium(IV) iso-propoxide, respectively, using vacuum impregnation technique. The wet composites were cured by special program with final heat treatment at 103 °C. Weight percent gains (WPG) of the wood specimen in the range of 19-25% were obtained due to these procedures. SEM investigations show that precursor solutions penetrate into the whole wood body and the titania formed after heat treatment in the composites is deposited in the pores (lumen) and partly in the cell walls of the wooden matrix. The moisture sorption was investigated in long term tests for a period of some months by storage at 20-23 °C in humid air (relative humidity of 99%) and ambient atmosphere (relative humidity 40-60%), respectively. For untreated reference samples the moisture sorption results in increasing of mass and volume according to saturation values of 24 and 13%, respectively, after about 15 days. The incorporation of titania reduces the saturation values of the moisture sorption by up to 12% in mass and by up to 5% in volume at a relative humidity of 99%. Thus, an enhancement of the dimensional stability of about 60% is obtained at best. The results demonstrate that modification of wood with sol-gel derived precursors can enhance its dimensional stability, which prevents the formation of cracks. Because of that reduced moisture sorption biological attacks should be delimited. Additionally, thermal analyses show a retarded combustion of the wood matrix due to titania infiltration.