A new metallosilicate based on yttrium was synthesized and characterized by XRD, FT-IR, 29Si MAS-NMR, and 89Y MAS-NMR. The mixed framework of the material was confirmed by the detection of distinct chemical shift groups using 29Si MAS-NMR (at -82 to -87 ppm, -91 to -94 ppm, -96 to -102 ppm, and -105 to -108 ppm), as well as four distinct chemical shifts in the 89Y MAS-NMR spectrum (at -89, -142, -160, and -220 ppm). Adsorption and kinetic analyses indicated the potential of the new material for the removal of lead and cadmium from aqueous media. The adsorption results for lead indicated that dynamic equilibrium was reached after five hours, with total lead removal of around 94 %, while for cadmium it was reached in the first hour, with total Cadmium removal of around 74 %. The adsorptions of lead and cadmium were modeled using pseudo-first order (PFO) and pseudo-second order (PSO) kinetic models. Although both models provided high R2 values (0.9903 and 0.9980, respectively), the PSO model presented a much lower χ2 red value (4.41×10−4), compared to the PFO model (2.12×10−3), which indicated that the rate-limiting step was probably due to the chemisorption of lead from the solution onto the yttrium-based metallosilicate.
The small-pore framework sodium stannosilicate AV-10, chemical composition Na2SnSi3O9⋅2H2O and known crystallographic structure, was synthesized by hydrothermal crystallization. This stannosilicate is built up of a three-dimensional network of corner-shared SiO4 tetrahedra and SnO6 octahedra. The SnO6 sites are linked to six SiO4 tetrahedra (Sn(6Si)) while each of the two crystallographically different SiO4 units are connected to two SnO6 and SiO4 units (Si(2Si,2Sn)). This material was used as model compound for developing a solid-state MAS NMR strategy aimed on the challenges and possibilities for structural studies, particularly considering the short and medium range order to verify the connectivity of SiO4 and SnO6 of such compounds despite the low natural abundances of 4.68% for 29Si and 8.59% for 119Sn nuclei as a real challenge. 29Si{119Sn} and 119Sn{29Si} REDOR (Rotational-Echo Double-Resonance) NMR measurements after 1H cross-polarization (CP) were carried out. The REDOR curves show a significant change after the “normal” quadratic short time evolution from which both (i) the shortest internuclear 29Si – 119Sn distances (and vice versa) and (ii) the number of corner-sharing SiO4 tetrahedra around the SnO6 octahedra (and vice versa) can be obtained. Based on these data, optimized 29Si {119Sn} and 119Sn{29Si} REPT-HMQC (Recoupled Polarization Transfer-Heteronuclear Multiple-Quantum Correlation, again after 1H CP) experiments were implemented, which directly show those heterogroup connectivity as correlation peaks in a 2D spectrum. This information was also obtained using 2D29Si{119Sn}-J-Coupling NMR experiments. Furthermore, 2D29Si INADEQUATE NMR experiments are also feasible, showing the connectivity of SiO4 tetrahedra. The combination of REDOR, REPT-HMQC, J-Coupling and INADEQUATE experiments yielded a complete analysis of the short and medium range structure of this microporous stannosilicate, in agreement with the previously published structure obtained Ab Initio from powder X-Ray diffraction data (XRD).