Approximation of the crack driving force for cracks at notches under static and cyclic loading
(2017)
The work deals with the efficient calculation of the elastic-plastic crack driving force (J-integral for monotonic loading andΔJ-integral under cyclic loading) for short cracks at notches as essential parameter for the reliable static and fatigue assessment of notched structures. The J- or ΔJ-integral is calculated based on analytical solutions for stress intensity factors, estimated by means of well-known weight function solutions in the case of cracks under power-law stress distributions. A plasticity-correction function is applied to the stress intensity factors to obtain the final expression of the crack driving force. The comparison between analytical solutions and finite element calculations in case of cracks at the weld toe in welded joints shows good agreement.
Approximation of the crack driving force for cracks at notches under static and cyclic loading
(2017)
The work deals with the efficient calculation of the elastic-plastic crack driving force (J-integral for monotonic loading andΔJ-integral under cyclic loading) for short cracks at notches as essential parameter for the reliable static and fatigue assessment of notched structures. The J- or ΔJ-integral is calculated based on analytical solutions for stress intensity factors, estimated by means of well-known weight function solutions in the case of cracks under power-law stress distributions. A plasticity-correction function is applied to the stress intensity factors to obtain the final expression of the crack driving force. The comparison between analytical solutions and finite element calculations in case of cracks at the weld toe in welded joints shows good agreement.
The fracture mechanics-based IBESS approach is applied to the determination of FAT classes of butt welds with crack Initiation along the weld toe. The aim is an investigation of the effect of the geometrical parameters toe radius, flank angle, reinforcement and secondary notches such as roughness or undercuts. The influence of these parameters is discussed both individually and in combination; however, excluding statistical distributions of them and the material data. The results, when compared with conventional FAT classes for butt welds, are encouraging with respect to a potential contribution of IBESS to the discussion of more advanced quality criteria for welds. To that purpose, demands for further research are proposed.
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.
If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas.
The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined.
Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5.
Recently two of the authors of the present paper proposed a model for a fracture mechanics
based prediction of the S–N characteristics of metallic components with large microstructural
defects and supported this by a validation exercise on tensile plates made of an aluminium
alloy AL5380 H321. Here the authors extend the study using a number of further
data sets from the literature for which data were available at different R ratios. These data
include two aluminium alloys, Al 2024-T3 and Al 7075-T6, and a ductile cast iron, EN-GJS-
400-18-LT. Despite of necessary assumptions for the compensation of partially missing
input information the results were fairly reasonable with the exception of one data set.
The authors identify high applied stress levels in combination with potential multiple crack
initiation as the probable root of the problem and propose a scheme how the model can be
extended for taking into account crack initiation.
The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible.
A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel.